Improving engineering properties of mature fine tailings using Tubifex

The present study investigated the effects of Tubifex (Oligochaeta: Tubificidae) treatment on the dewatering process of mature fine tailings (MFT). Experiments testing the survival rate showed that Tubifex can survive at 20 °C and 4 °C. MFT with initial solids content (Sc) of 30% of total mass were treated in 11 settling columns by three Tubifex densities, 1400, 2000 and 4200 individuals·m−2. Test results showed that the mean survival rate at 20 °C and 4 °C on the 28th day stayed around 85%. Tubifex enhanced MFT dewatering by providing compacted tailings with 11.6% and 66.7% higher Sc and undrained shear strength compared with nontreated tailings. Tubifex accelerated pore water pressure dissipation. Tubifex did not affect the chemical composition of tailings except for a decrease in sulfate content. The Sc of tailings treated by Tubifex increased by 67.4% within nine months, which was 129% greater than the Sc increase of the nontreated tailings after 11 months.

Evaluation of a Novel Polymeric Flocculant for Enhanced Water Recovery of Mature Fine Tailings

The novel cationic flocculant, poly(lactic acid) choline iodide ester methacrylate (poly(PLA4ChMA)), has been shown to provide improved flocculation of 5.0 wt.% mature fine tailings (MFT) diluted in deionized water compared to commercial anionic polymers, with continued dewatering of the sediment occurring as the polymer undergoes partial hydrolytic degradation. However, the elevated dosages (10,000 ppm) required would make the polymer costly to implement on an industrial scale. With this motivation, the impact of MFT loading and the use of process water is explored while comparing the settling performance of poly(PLA4ChMA) to available commercial alternatives such as anionic FLOPAM A3338. Improved consolidation of 5.0 wt.% MFT diluted with process water could be achieved at reduced dosages (500 ppm) with poly(PLA4ChMA). However, the final compaction levels after polymer degradation were similar to those achieved with the nondegradable commercial flocculants. Flocculation-filtration experiments with undiluted MFT are also conducted to compare the performance of the polymers. Significantly faster rates of water release were observed with the cationic flocculants compared to FLOPAM A3338, but no improvement in the overall tailings compaction was found either before or after poly(PLA4ChMA) degradation. Thus, the improved dewatering observed with poly(PLA4ChMA) in dilute MFT suspensions does not extend to conditions that would be encountered in the field.