Antibacterial properties of poly ( N , N -dimethylaminoethyl methacrylate) obtained at different initiator concentrations in solution polymerization

The samples of poly( N , N -dimethylaminoethyl methacrylate) were synthesized by radical polymerization. The amount of monomer and solvent was constant as opposed to an amount of initiator which was changing. No clear relationship between polymerization conditions and the molecular weight of the polymer was found, probably due to the branched configuration of produced polymer. Bactericidal interactions in all samples against Gram-positive and Gram-negative bacteria have been demonstrated. However, the observed effect has various intensities, depending on the type of bacteria and the type of sample.

Preparation and Characterization of Semi-IPN Cryogels Based on Polyacrylamide and Poly(N,N-dimethylaminoethyl methacrylate); Functionalization of Carrier with Monochlorotriazinyl-β-cyclodextrin and Release Kinetics of Curcumin

Curcumin (CCM) is a natural hydrophobic polyphenol known for its numerous applications in the food industry as a colorant or jelly stabilizer, and in the pharmaceutical industry due to its anti-inflammatory, antibacterial, antioxidant, anti-cancer, and anti-Alzheimer properties. However, the large application of CCM is limited by its poor solubility in water and low stability. To enhance the bioavailability of CCM, and to protect it against the external degradation agents, a novel strategy, which consists in the preparation of semi-interpenetrating polymer networks, (s-IPNs) based on poly(N,N-dimethylaminoethyl methacrylate) entrapped in poly(acrylamide) networks, by a cryogelation technique, was developed in this work. All s-IPN cryogels were characterized by SEM, EDX, FTIR, and swelling at equilibrium as a function of pH. Functionalization of semi-IPN cryogel with monochlorotriazinyl-β-cyclodextrin (MCT-β-CD) led to IPN cryogel. The release profile of CCM from the composite cryogels was investigated at 37 °C, in pH 3. It was found that the cumulative release increased with the increase of the carrier hydrophobicity, as a result of increasing the cross-linking degree, the content and the molar mass of PDMAEMA. Fitting Higuchi, Korsmeyer–Peppas, and first order kinetic models on the CCM release profiles indicated the diffusion as the main driving force of drug release from the composite cryogels.

The Influence of Polymer Composition on the Hydrolytic and Enzymatic Degradation of Polyesters and Their Block Copolymers with PDMAEMA

Well-defined, semi-degradable polyester/polymethacrylate block copolymers, based on ε-caprolactone (CL), d,l-lactide (DLLA), glycolide (GA) and N,N′-dimethylaminoethyl methacrylate (DMAEMA), were synthesized by ring-opening polymerization (ROP) and atom transfer radical polymerization. Comprehensive degradation studies of poly(ε-caprolactone)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PCL-b-PDMAEMA) on hydrolytic degradation and enzymatic degradation were performed, and those results were compared with the corresponding aliphatic polyester (PCL). The solution pH did not affect the hydrolytic degradation rate of PCL (a 3% Mn loss after six weeks). The presence of a PDMAEMA component in the copolymer chain increased the hydrolysis rates and depended on the solution pH, as PCL-b-PDMAEMA degraded faster in an acidic environment (36% Mn loss determined) than in a slightly alkaline environment (27% Mn loss). Enzymatic degradation of PCL-b-PDMAEMA, poly(d,l-lactide)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PLA-b-PDMAEMA) and poly(lactide-co-glycolide-co-ε-caprolactone)-block-poly(N,N′-dimethylaminoethyl methacrylate) (PLGC-b-PDMAEMA) and the corresponding aliphatic polyesters (PCL, PLA and PLGC) was performed by Novozyme 435. In enzymatic degradation, PLGC degraded almost completely after eleven days. For polyester-b-PDMAEMA copolymers, enzymatic degradation primarily involved the ester bonds in PDMAEMA side chains, and the rate of polyester degradation decreased with the increase in the chain length of PDMAEMA. Amphiphilic copolymers might be used for biomaterials with long-term or midterm applications such as nanoscale drug delivery systems with tunable degradation kinetics.