Sulfonated Polysulfone/TiO2(B) Nanowires Composite Membranes as Polymer Electrolytes in Fuel Cells

New proton conducting membranes based on sulfonated polysulfone (sPSU) reinforced with TiO2(B) nanowires (1, 2, 5 and 10 wt.%) were synthesized and characterized. TiO2(B) nanowires were synthesized by means of a hydrothermal method by mixing TiO2 precursor in aqueous solution of NaOH as solvent. The presence of the TiO2(B) nanowires into the polymer were confirmed by means of Field Emission Scanning Electron Microscopy, Fourier transform infrared and X-ray diffraction. The thermal study showed an increase of almost 20 °C in the maximum temperature of sPSU backbone decomposition due to the presence of 10 wt.% TiO2(B) nanowires. Water uptake also is improved with the presence of hydrophilic TiO2(B) nanowires. Proton conductivity of sPSU with 10 wt.% TiO2(B) nanowires was 21 mS cm−1 (at 85 °C and 100% RH). Under these experimental conditions the power density was 350 mW cm−2 similar to the value obtained for Nafion 117. Considering all these obtained results, the composite membrane doped with 10 wt.% TiO2(B) nanowires is a promising candidate as proton exchange electrolyte in fuel cells (PEMFCs), especially those operating at high temperatures.

Application of ZIF-67 as a crosslinker to prepare sulfonated polysulfone mixed-matrix membranes for enhanced water permeability and separation properties

High-performance sulfonated polysulfone (SPSf) mixed-matrix membranes (MMMs) were fabricated via a nonsolvent-induced phase separation (NIPS) method using ZIF-67 (Zeolitic imidazolate frameworks-67) as a crosslinker. Acid-base crosslinking occurred between the sulfonic acid groups of SPSf and the tertiary amine groups of the embedded ZIF-67, which improved the dispersion of ZIF-67 and simultaneously improved the membrane structure and permselectivity. The dispersion of ZIF-67 in the MMMs and the acid-base crosslinking reaction were verified by energy-dispersive X-ray spectroscopy (EDX), X-ray diffractometry (XRD), Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The pore structure analysis of MMMs indicated that filling ZIF-67 into SPSf enhanced the average surface pore sizes, surface porosities and more micropore in cross-sections. The crossflow filtrations showed the MMMs have higher pure water fluxes (57 to 111 L m−2 h−1) than the SPSf membrane (55 L m−2 h−1) but also higher BSA(bovine serum albumin) rejection rate of 93.9–95.8%, a model protein foulant. The MMMs showed a higher water contact angle than the SPSf membrane due to the addition of hydrophobic ZIF-67 and acid-base crosslinking, and also maintained high thermal stability evidenced by the TGA(Thermogravimetric analysis) results. At the optimal ZIF-67 concentration of 0.3 wt%, the water flux of the SPSf-Z67-0.3 membrane was 82 L m−2 h−1 with a high BSA rejection rate of 95.3% at 0.1 MPa and better antifouling performance (FRR = 70%).

New Insights into Properties of Methanol Transport in Sulfonated Polysulfone Composite Membranes for Direct Methanol Fuel Cells

Methanol crossover through a polymer electrolyte membrane has numerous negative effects on direct methanol fuel cells (DMFCs) because it decreases the cell voltage due to a mixed potential (occurrence of both oxygen reduction and methanol oxidation reactions) at the cathode, lowers the overall fuel utilization and contributes to long-term membrane degradation. In this work, an investigation of methanol transport properties of composite membranes based on sulfonated polysulfone (sPSf) and modified silica filler is carried out using the PFG-NMR technique, mainly focusing on high methanol concentration (i.e., 5 M). The influence of methanol crossover on the performance of DMFCs equipped with low-cost sPSf-based membranes operating with 5 M methanol solution at the anode is studied, with particular emphasis on the composite membrane approach. Using a surface-modified-silica filler into composite membranes based on sPSf allows reducing methanol cross-over of 50% compared with the pristine membrane, making it a good candidate to be used as polymer electrolyte for high energy DMFCs.