Protein Adsorption of Highly (001) Oriented Hydroxyapatite Coating Using Rf-Plasma Spraying

The protein adsorption behavior was investigated for highly (001) oriented hydroxypatatite coatings (HACs). Highly (001) oriented (HO-) HACs and HAC with low orientation (LO-HAC) were prepared on titanium (Ti) substrates through a radio-frequency thermal plasma spraying method. Sintered HA pellets (S-HA) was also prepared as a control. The solution of 22 'g/100 'l PBS of the fluorescein-isothiocyanate (FITC) labeled bovine serum albumin (FITC-BSA), immunoglobulin G (FITC-IgG) and cytochrom c (FITC-CCC) was separately dropped on the surface of HACs and was incubated for 30 min. After the incubation, such HACs were washed with the PBS additionally supplemented with 125mM NaCl and observed using a fluorescence microscope. Fluorescence microscopic examination indicates that FITC labeled proteins somewhat adsorbed on the HACs, while proteins adsorbed little on S-HA surface. In particular, it can be seen that FITC-CCC adsorbed more prominently on the HO-HAC.

Highly Oriented Hydroxyapatite Coating Using rf Plasma Spraying

Highly oriented hydroxyapatite (HA) coatings were prepared on titanium (Ti) substrates through a radio-frequency thermal plasma spraying method. XRD patterns showed that the HA coating layer had an structure with (00l) preferred crystal orientation. TEM observation showed that 200-800 nm-width prismatic crystals were formed in HA splats and the longitudinal axis of such prismatic crystals oriented vertical to the coating's surface. TEM images also indicate that the interface between prismatic crystals became compacted. SAD pattern show that the longitudinal axis of prismatic crystals corresponds to the <001> axis of HA.