Based on magnesium carbonate and antimony oxide (V), MgO•Sb2O5 was obtained. In the formulation of fire-resistant cable PVC-plasticate, antimony (III) oxide was replaced by MgO•Sb2O5 and the fire resistance and physical and mechanical properties of the resulting compound were investigated. It is shown that the replacement of antimony (III) oxide in the composition of PVC cable compound MgO•Sb2O5 leads to the production of a compound that is not inferior in its characteristics to the original plastic compound. In particular, the fire resistance of cable PVC-plasticate, standard industrial formulation and with the obtained MgO•Sb2O5, is practically the same (OI=32%). It has been established that the physical and mechanical characteristics of the cable compound, when replacing antimony oxide (III) with MgO•Sb2O5 in the formulation, remain at the level of the original compound, while MgO×Sb2O5 will have a less negative impact on the environment.