Single-phase CuInSe 2 films were grown by high vapor selenization of CuIn alloy precursors within a partially closed graphite box. The CuIn precursors were prepared using Cu x In y alloy targets with different composition rates under low vacuum level by a homemade sputtering system. The Cu and In composition rates of the used targets are 11:9, 10:10, and 9:11, respectively. The metallic precursor films were selenized using a two-step temperature profile, i.e. at 250°C and 400–500°C, respectively. The influence of the temperature at the second selenization step on the quality of the CIS absorbing layers was investigated. The CIS films were characterized by X-ray diffractometry, scanning electron microscopy, energy dispersive X-ray analysis, and Raman spectroscopy. The deposited CIS absorbers selenized at a high temperature of 500°C for 30 min exhibited a single-phase chalcopyrite structure with a preferential orientation in the (112) direction. These layers display uniform, large, and densely packed crystals with a grain size of about 3–5 μm. Cadmium sulfide buffer layer was manufactured by chemical bath deposition method. Bilayers ZnO / ZnO : Al were prepared by RF magnetron sputtering deposition. CIS solar cells with an efficiency of about 6.5% were produced without antireflective films. The method to fabricate CIS solar cells by a combination of the low vacuum sputtering deposition and the graphite box selenization process has provided a simple control process and shown a promising potential for developing high efficient and low-cost CuInSe 2 solar cells.
Low-cost and High-efficient Extraction of Lipids from Chlorella by using Industrial Ionic Liquids