Polyurethane elastomers for facial prostheses

1978 ◽  
Vol 39 (2) ◽  
pp. 179-187 ◽  
Author(s):  
Juan B. Gonzalez
Keyword(s):  
Polyurethane Elastomers ◽  
Facial Prostheses

scholarly journals Development of Highly Efficient, Glassy Carbon Foam Supported, Palladium Catalysts for Hydrogenation of Nitrobenzene

Nanomaterials ◽  
2021 ◽  
Vol 11 (5) ◽  
pp. 1172
Author(s):  
Ádám Prekob ◽  
Mahitha Udayakumar ◽  
Gábor Karacs ◽  
Ferenc Kristály ◽  
Gábor Muránszky ◽  
...  
Keyword(s):  
Zeta Potential ◽  
Glassy Carbon ◽  
Palladium Nanoparticles ◽  
Palladium Catalysts ◽  
Sucrose Solution ◽  
Supported Catalyst ◽  
Carbon Foam ◽  
Hydroxyl Groups ◽  
Polyurethane Elastomers ◽  
Oh Groups

Glassy carbon foam (GCF) catalyst supports were synthesized from waste polyurethane elastomers by impregnating them in sucrose solution followed by pyrolysis and activation (AC) using N2 and CO2 gas. The palladium nanoparticles were formed from Pd(NO3)2. The formed palladium nanoparticles are highly dispersive because the mean diameters are 8.0 ± 4.3 (Pd/GCF), 7.6 ± 4.2 (Pd/GCF-AC1) and 4.4 ± 1.6 nm (Pd/GCF-AC2). Oxidative post-treatment by CO2 of the supports resulted in the formation of hydroxyl groups on the GCF surfaces, leading to a decrease in zeta potential. The decreased zeta potential increased the wettability of the GCF supports. This, and the interactions between –OH groups and Pd ions, decreased the particle size of palladium. The catalysts were tested in the hydrogenation of nitrobenzene. The non-treated, glassy-carbon-supported catalyst (Pd/GCF) resulted in a 99.2% aniline yield at 293 K and 50 bar hydrogen pressure, but the reaction was slightly slower than other catalysts. The catalysts on the post-treated (activated) supports showed higher catalytic activity and the rate of hydrogenation was higher. The maximum attained aniline selectivities were 99.0% (Pd/GCF-AC1) at 293 K and 98.0% (Pd/GCF-AC2) at 323 K.

Effect and Detection of Loose Chain Ends in Crosslinked Polyurethane Elastomers

1971 ◽  
Vol 44 (1) ◽  
pp. 152-165 ◽  
Author(s):  
A. E. Oberth
Keyword(s):  
Crosslink Density ◽  
Volume Fraction ◽  
Present Theory ◽  
Swelling Ratio ◽  
Polyurethane Elastomers ◽  
Equilibrium Volume ◽  
Equilibrium Swelling ◽  
Volume Swelling

Abstract The effect of loose chain ends on tensile properties and equilibrium swelling of crosslinked polyurethane rubbers is studied. As in plasticized elastomers, tensile strength and elastic modulus are reduced approximately by a factor (1−νE,P)2, where νE,P is the volume fraction of loose chain ends, plasticizer, or both. This effect is much larger than predicted by present theory. Also the equilibrium volume swelling ratio, V0/V, of rubbers having terminal chains or an equal volume of plasticizer is the same, provided they do not differ in crosslink density. However, the volume fraction of “network rubber” in the equilibrium swollen specimen, ν2, differs owing to the non-extractability of terminal chains. On this basis a method is proposed which allows experimental determination of the volume fraction of loose ends. Elastomers abounding in loose chain ends show markedly less long term stress relaxation. This effect is not clearly understood but is useful to detect the presence of non load-bearing network.

scholarly journals Impact of Macrodiols on the Morphological Behavior of H12MDI/HDO-Based Polyurethane Elastomer

Polymers ◽  
2021 ◽  
Vol 13 (13) ◽  
pp. 2060
Author(s):  
Shazia Naheed ◽  
Mohammad Zuber ◽  
Mahwish Salman ◽  
Nasir Rasool ◽  
Zumaira Siddique ◽  
...  
Keyword(s):  
Molecular Weight ◽  
Contact Angle ◽  
Chain Length ◽  
Microphase Separation ◽  
Soft Segment ◽  
Group Identification ◽  
Degree Of Crystallinity ◽  
Polyurethane Elastomers ◽  
Hard Segments ◽  
Morphological Behavior

In this study, we evaluated the morphological behavior of polyurethane elastomers (PUEs) by modifying the soft segment chain length. This was achieved by increasing the soft segment molecular weight (Mn = 400–4000 gmol−1). In this regard, polycaprolactone diol (PCL) was selected as the soft segment, and 4,4′-cyclohexamethylene diisocyanate (H12MDI) and 1,6-hexanediol (HDO) were chosen as the hard segments. The films were prepared by curing polymer on Teflon surfaces. Fourier transform infrared spectroscopy (FTIR) was utilized for functional group identification in the prepared elastomers. FTIR peaks indicated the disappearance of −NCO and −OH groups and the formation of urethane (NHCOO) groups. The morphological behavior of the synthesized polymer samples was also elucidated using scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques. The AFM and SEM results indicated that the extent of microphase separation was enhanced by an increase in the molecular weight of PCL. The phase separation and degree of crystallinity of the soft and hard segments were described using X-ray diffraction (XRD). It was observed that the degree of crystallinity of the synthesized polymers increased with an increase in the soft segment’s chain length. To evaluate hydrophilicity/hydrophobicity, the contact angle was measured. A gradual increase in the contact angle with distilled water and diiodomethane (38.6°–54.9°) test liquids was observed. Moreover, the decrease in surface energy (46.95–24.45 mN/m) was also found to be inconsistent by increasing the molecular weight of polyols.

scholarly journals Degradation and stabilization of polyurethane elastomers

2019 ◽  
Vol 90 ◽  
pp. 211-268 ◽  
Author(s):  
Fengwei Xie ◽  
Tianlong Zhang ◽  
Peter Bryant ◽  
Valsala Kurusingal ◽  
John M. Colwell ◽  
...  
Keyword(s):  
Polyurethane Elastomers

scholarly journals Highly exfoliated montmorillonite clay reinforced thermoplastic polyurethane elastomer:in situpreparation and efficient strengthening

RSC Advances ◽  
2019 ◽  
Vol 9 (15) ◽  
pp. 8184-8196 ◽  
Author(s):  
Jingshui Xu ◽  
Lihua Cheng ◽  
Zhong Zhang ◽  
Ling Zhang ◽  
Cen Xiong ◽  
...  
Keyword(s):  
Thermoplastic Polyurethane ◽  
Montmorillonite Clay ◽  
Solution Polymerization ◽  
Polyurethane Elastomers ◽  
Thermoplastic Polyurethane Elastomers ◽  
Mmt Clay ◽  
Polymerization Method

Highly exfoliated montmorillonite (MMT) clay reinforced thermoplastic polyurethane elastomers (TPUs) were prepared by anin situsolution polymerization method.