One-step crystallization kinetic parameters of the glass-ceramics prepared from stainless steel slag and pickling sludge

2016 ◽  
Vol 23 (3) ◽  
pp. 220-224 ◽  
Author(s):  
Shen-gen Zhang ◽  
Jian Yang ◽  
Bo Liu ◽  
De-an Pan ◽  
Chun-li Wu ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Kinetic Parameters ◽  
Crystallization Kinetic ◽  
Steel Slag ◽  
Glass Ceramics ◽  
Stainless Steel Slag ◽  
Pickling Sludge ◽  
One Step ◽  
Step Crystallization

Crystallization mechanism of glass-ceramics prepared from stainless steel slag

Rare Metals ◽  
2018 ◽  
Vol 37 (5) ◽  
pp. 413-420 ◽  
Author(s):  
Wen-Di Fan ◽  
Qiang-Wei Yang ◽  
Bin Guo ◽  
Bo Liu ◽  
Shen-Gen Zhang
Keyword(s):  
Stainless Steel ◽  
Steel Slag ◽  
Glass Ceramics ◽  
Crystallization Mechanism ◽  
Stainless Steel Slag

Microstructural transformation of stainless steel slag-based CAMS glass ceramics prepared by SPS

2021 ◽  
Vol 47 (1) ◽  
pp. 1284-1293
Author(s):  
Saiyu Liu ◽  
Yuxin Chen ◽  
Shunli Ouyang ◽  
Hangren Li ◽  
Xin Li ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Steel Slag ◽  
Glass Ceramics ◽  
Stainless Steel Slag ◽  
Microstructural Transformation

scholarly journals Experimental Study on Precipitation Behavior of Spinels in Stainless Steel-Making Slag under Heating Treatment

Processes ◽  
2019 ◽  
Vol 7 (8) ◽  
pp. 487 ◽  
Author(s):  
Jianli Li ◽  
Qiqiang Mou ◽  
Qiang Zeng ◽  
Yue Yu
Keyword(s):  
Particle Size ◽  
Stainless Steel ◽  
Steel Slag ◽  
Calcium Content ◽  
Heating Time ◽  
X Ray Diffraction ◽  
Stainless Steel Slag ◽  
Steel Making ◽  
Heating Treatment ◽  
The Stability

The stability of chromium in stainless steel slag has a positive correlation with spinel particle size and a negative correlation with the calcium content of the spinel. The effect of heating time on the precipitation of spinel crystals in the CaO-SiO2-MgO-Al2O3-Cr2O3-FeO system was investigated in the laboratory. Scanning electron microscopy with energy-dispersive and X-ray diffraction were adopted to observe the microstructure, test the chemical composition, and determine the mineral phases of synthetic slags, and FactSage7.1 was applied to calculate the crystallization process of the molten slag. The results showed that the particle size of the spinel crystals increased from 9.42 to 10.73 μm, the calcium content in the spinel crystals decreased from 1.38 at% to 0.78 at%, and the content of chromium in the spinel crystal increased from 16.55 at% to 22.78 at% with an increase in the heating time from 0 min to 120 min at 1450 °C. Furthermore, the species of spinel minerals remained constant. Therefore, an extension in the heating time is beneficial for improving the stability of chromium in stainless steel slag.

Sign in / Sign up

Export Citation Format

Share Document