Microstructure characteristics and surface oxidation behaviour of SLM WC/IN718 composite

2021 ◽  
pp. 1-10
Author(s):  
Yanlin Wang ◽  
Longchao Zhuo ◽  
Min Liu ◽  
Zhanjun An ◽  
Chao Li ◽  
...  
Keyword(s):  
Surface Oxidation ◽  
Oxidation Behaviour ◽  
Microstructure Characteristics

Surface Oxidation Behaviour of Cubic BN Powders

2014 ◽  
Vol 602-603 ◽  
pp. 544-547
Author(s):  
Xin Yan Yue ◽  
Yue Zhang ◽  
Jian Jun Wang ◽  
Wei Wang ◽  
Hong Qiang Ru
Keyword(s):  
Heat Treatment ◽  
Surface Oxidation ◽  
Mass Gain ◽  
Oxidation Behaviour ◽  
Experimental Results ◽  
Oxidation Temperature ◽  
Oxidation Reactions ◽  
Oxidation Treatment ◽  
Treatment Processes

In order to improve the sinterability of the cBN, surface oxidation treatment was conducted to form a B2O3 film on the surface of the cBN powders. The cBN powders (d50 = 7.5 μm) were used as original powders. The heat treatment processes were 500, 800, 900, 950, 980 and 1000 °C holding for 30 minutes, respectively. The oxidation reactions which probably happened were calculated based on the thermodynamics. The experimental results showed that the oxidation starting temperature of cBN powders was higher than 800 °C. The higher the oxidation temperature, the greater the mass gain of the cBN powders.

Growth of hematite by surface oxidation of olivine

1988 ◽  
Vol 46 ◽  
pp. 800-801
Author(s):  
S. McKernan ◽  
C. B. Carter
Keyword(s):  
Electron Microscope ◽  
Surface Oxidation ◽  
Thin Foil ◽  
Nucleation And Growth ◽  
Ion Milling ◽  
Annealed Material ◽  
Thin Foils ◽  
Natural Olivine ◽  
Approximate Composition ◽  
Second Phases

The oxidation of natural olivine has previously been performed on bulk samples and the reactions followed by preparation of TEM specimens from the annealed material. These results show that below ∼1000°C hematite and amorphous silica are formed, particularly around dislocations. At higher temperatures magnetite and some enstatite-like phase are formed. In both cases the olivine is left almost totally Fe depleted. By performing the oxidation on characterized thin TEM specimens it is possible to obtain more information on the nucleation and growth of the second phases formed. The conditions in a thin foil, however, are very different from those in the bulk especially with regard to surface effects. The nucleation of precipitates in particular may be expected to occur differently in these thin foils than in the bulk.TEM specimens of natural olivine (approximate composition Mg+Fe+Si2o4) which had been annealed at 1000°C for 1 hr were prepared by mechanical polishing and dimpling, followed by Ar ion milling to perforation. The specimens were characterized in the electron microscope and then heated in air in alumina boats to 900°C for between 30 and 180 minutes.

In-Situ Study of NiO Growth on Textured Nickel Tape Using Environmental Scanning Electron Microscope (ESEM) and Hot Stage

2001 ◽  
Vol 7 (S2) ◽  
pp. 1276-1277
Author(s):  
Y. Akin ◽  
R.E. Goddard ◽  
W. Sigmund ◽  
Y.S. Hascicek
Keyword(s):  
Buffer Layer ◽  
Lattice Mismatch ◽  
Sol Gel ◽  
Surface Oxidation ◽  
Dip Coating ◽  
Buffer Layers ◽  
Superconducting Film ◽  
Environmental Scanning ◽  
Cold Rolling And Annealing

Deposition of highly textured ReBa2Cu3O7−δ (RBCO) films on metallic substrates requires a buffer layer to prevent chemical reactions, reduce lattice mismatch between metallic substrate and superconducting film layer, and to prevent diffusion of metal atoms into the superconductor film. Nickel tapes are bi-axially textured by cold rolling and annealing at appropriate temperature (RABiTS) for epitaxial growth of YBa2Cu3O7−δ (YBCO) films. As buffer layers, several oxide thin films and then YBCO were coated on bi-axially textured nickel tapes by dip coating sol-gel process. Biaxially oriented NiO on the cube-textured nickel tape by a process named Surface-Oxidation- Epitaxy (SEO) has been introduced as an alternative buffer layer. in this work we have studied in situ growth of nickel oxide by ESEM and hot stage.Representative cold rolled nickel tape (99.999%) was annealed in an electric furnace under 4% hydrogen-96% argon gas mixture at 1050°C to get bi-axially textured nickel tape.

Oxidation behaviour and strength degradation of a Yb 2 O 3 -SiO 2 -doped hot-pressed silicon nitride between 1200 and 1500°C

2002 ◽  
Vol 82 (16) ◽  
pp. 3027-3043 ◽  
Author(s):  
Shuqi Guo ◽  
Naoto Hirosaki ◽  
Toshiyuki Nishimura ◽  
Yoshinobu Yammoto ◽  
Mamoru Mitomo
Keyword(s):  
Silicon Nitride ◽  
Strength Degradation ◽  
Oxidation Behaviour

KINETICS OF SURFACE OXIDATION AND RELATED CHANGES IN THE MAGNETISM OF AMORPHOUS TbFeCo FILMS

1988 ◽  
Vol 49 (C8) ◽  
pp. C8-1711-C8-1712 ◽  
Author(s):  
S. Klahn ◽  
H. Heitmann ◽  
M. Rosenkranz ◽  
H. J. Tolle
Keyword(s):  
Surface Oxidation ◽  
Kinetics Of