ATEM has been used to characterize three different silicon nitride materials after tensile creep in air at 1200 to 1400° C. In Part I, the microstructures and microstructural changes that occur during testing were described, and consistent with that description the designations and sintering aids for these materials were: W/YAS, a SiC whisker reinforced Si3N4 processed with yttria (6w/o) and alumina (1.5w/o); YAS, Si3N4 processed with yttria (6 w/o) and alumina (1.5w/o); and YS, Si3N4 processed with yttria (4.0 w/o). This paper, Part II, addresses the interfacial cavitation processes that occur in these materials and which are ultimately responsible for creep rupture.