A technology of continuous casting of steel has a large effect on its contamination. In particular, proper organization of metal flows in tundish and mold is very important. After completion a series of casting through a tundish and drop of metal level in it, it possible, that the slag flows from the surface layers of the tundish to capture the metal. An analysis of results of ultrasonic control of finished strip showed, that the basic number of the revealed defects was obtained during strip rolling out of the last slabs of the last heat in a series for a tundish. Metallographic studies determined, that the defects were located in the slab axis zone and filled by macro-inclusions of complex composition. To determine the actual distribution of metal flows, a water simulation of them was accomplished for the existing design of the EVRAZ NTMK tundish. It was determined, that at the drop of metal level in a tundish, a capture of slag from the metal reservoir and its transfer into the main bath of the tundish takes place due to whirligig flows. Following the weight metal consumption, the zone of slag inclusions distribution enlarges. Besides, denudation of the metal mirror in the metal reservoir takes place, resulted in metal secondary oxidation. Based on the results of the simulation, it was proposed to modify the design of the “turbostop”, which is installed in the metal reservoir of the tundish. Besides, it was proposed to remove the dividers installation in the tundish. It was noted, that the proposed steps enable to ensure a minimal level of rejections.