The construction industry continues to develop and the requirements for cement performance are getting higher and higher. At the same time, in the steel industry, the discharge of steel slag is also increasing. The effective reuse of steel slag has become a prominent problem in the steel industry. . Therefore, it is envisaged to use steel slag as a raw material for the cement production process to produce cement and to produce high-performance cement. The main raw materials of this experiment are steel slag, limestone, sandstone and shale. Through the cement preparation process, the cement is made, and then the cement is made into concrete to test its performance. This experiment mainly studies the sintering temperature and holding time variable. In the experimental test, the analysis and comparison were carried out in five aspects of the degree of macroscopic cracking, particle size, density, microstructure and composition. In the comparison experiment of sintering temperature, with the increase of temperature, the flexural and compressive properties of cement gradually increased. In this test, 1200 °C is the most suitable temperature for the performance of the cement. Through the experimental comparison of different holding time, it is known that with the prolonging of the holding time, the microstructure and actual performance of the cement are continuously enhanced. Comprehensive consideration: the ratio of steel slag in cement ratio is 10%, sintering temperature is 1200 °C, and heat preservation is 2h. The steel slag cement prepared under this condition has the strongest performance.
Effect of nano and micro conductive materials on conductive properties of carbon fiber reinforced concrete