The low temperature phase of Pd5Ce (L-Pd5Ce) has a one-dimensional long period superstructure (1D-LPS) derived from Ll2. The periodic antiphase boundaries (APBs) are parallel to (110) planes and have a shift vector of 1/2[110]. Hereafter, the indices are referred to the basic lattices of Ll2 As insertion of the APB causes a change in composition, such an APB is called “non-conservative”. Then, a domain size M depends upon the Ce concentration in the alloy. It was found that M increases also with temperature. The temperature dependency of M is attributed to a change of the degree of order within the antiphase domains. In this work, morphology of the non-conservative APBs is observed to clarify the formation process of the 1D-LPS.The alloy of Pd-16.7 at%Ce was prepared by arc melting in argon atmosphere. Disc specimens made from the alloy ingot were first held at 985 K for 260 ks and quenched in iced water to obtain the state of M=∞ or Ll2, followed by annealing for various lengths of time. The annealing temperature was 873 K where the equilibrium value for M is about 3 in unit of (110) lattice spacing of Ll2. Observation was carried out using microscopes JEM-2000FX, JEM-4000EX (HVEM Lab., Kyushu Univ.) and JEM-2000EX (Dept. of Mater. Sci. Tech., Kyushu Univ.).