The Effect of Bleaching Agents on the Color Stability of Ceromer and Porcelain Restorative Materials In Vitro

2012 ◽  
Vol 38 (1) ◽  
pp. E1-E8 ◽  
Author(s):  
HB Kara ◽  
F Aykent ◽  
B Ozturk
Keyword(s):  
Color Change ◽  
Glass Ceramics ◽  
In Vitro Study ◽  
Color Stability ◽  
Color Changes ◽  
Bleaching Procedure ◽  
Significant Difference ◽  
Restorative Materials ◽  
The Difference

SUMMARY Purpose The aim of this in vitro study was to determine the color changes of five different restorative materials after exposing these materials to two different home bleaching agents. Methods This study applied bleaching agents to an ultralow-fusing porcelain, a low-fusing porcelain, two types of heat-pressed glass ceramics, and a ceromer. A total of 24 disc-shaped specimens were fabricated (with a diameter of 10 mm and a thickness of 2 mm) from each material (n=12). The initial color measurements were taken with a spectrophotometer. The first set of specimens were bleached with 10% hydrogen peroxide (HP) for one hour daily for 10 days. The other set of specimens were bleached with 10% carbamide peroxide (CP) bleaching gel for eight hours daily for 14 days. Data were analyzed with the one-way analysis of variance and Kruskal-Wallis statistical test. The difference in the prebleaching and postbleaching color of each material was considered to be statistically significant at p < 0.05. Results The study found a statistically significant difference among the color changes of the test groups after exposing them to both bleaching agents (p<0.05). Appreciable color change was observed in the Estenia (ΔE=3.99) specimens that were bleached with the HP, and noticeable color changes were observed in the Estenia (ΔE=1.89) and IPS Empress 2 (ΔE=1.66) groups when they were treated with the CP. Conclusions Restorations (especially polymer-containing restorative materials) should be protected before any bleaching procedure due to the high risk of color change.

Effect of Children's Drinks on Color Stability of Different Dental Composites: An in vitro Study

2017 ◽  
Vol 41 (2) ◽  
pp. 120-125 ◽  
Author(s):  
Ahmed Nour El-din Ahmed Habib ◽  
Soad Abdelmoniem Abdelmoniem ◽  
Sara Ahmed Mahmoud
Keyword(s):  
Color Change ◽  
In Vitro Study ◽  
Color Stability ◽  
Dental Composites ◽  
Chocolate Milk ◽  
Water Control ◽  
Color Changes ◽  
Significant Difference ◽  
Mango Juice

Aim: To assess the effect of four different children's drinks on color stability of resin dental composites. Study design: A total of one hundred and twenty specimens were prepared from Grandio SO, Filtek Z350 XT and Filtek Z250 XT (forty specimens each). Specimens were thermocycled, then each group was further subdivided into four subgroups (n=10) according to the immersion media which were chocolate milk, mango juice, orange fizzy drink, and water (control). The initial color parameters of each specimen were recorded before immersion (baseline) and color change values were recorded three and seven days after immersion in each solution using a digital spectrophotometer. Atomic force microscope was used to measure the surface roughness in randomly selected samples after one week immersion in children's drinks. Results: All the children's drinks produced color changes in the examined resin dental composites, yet there was no statistical significant difference between the effects of tested drinks on the color changes (mean ΔE) of the three different dental composites (P>0.05). Conclusions: All tested children's drinks caused clinically unacceptable color changes of the tested resin dental composites. Immersion in chocolate milk and orange fizzy led to the highest color changes in the tested resin dental composites.

scholarly journals The effect of optical brightening toothpaste on the color stability of esthetic restorative materials

2021 ◽  
Vol 11 (Suppl. 1) ◽  
pp. 81-85
Author(s):  
Firdevs Kahvecioğlu ◽  
Elçim Çoban ◽  
Hayriye Esra Ülker
Keyword(s):  
Color Change ◽  
Calculated Data ◽  
Color Stability ◽  
Color Changes ◽  
Significant Difference ◽  
Restorative Materials ◽  
Cherry Juice ◽  
Native Speakers Of English ◽  
Materials Used ◽  
Post Hoc

Aim: The aim of this study is to evaluate the effects of whitening toothpaste applications on the color stability of different tooth-colored restorative materials (Fuji IX, GC Fuji II LC, Equia Forte, and Kerr Point 4)  Methodology: Standardized fourty disc-shaped specimens were prepared from esthetic restorative materials and polished. The baseline color values of each specimen were then measured using a spectrophotometer, according to the Commission Internationale de l'Eclairage L*, a*, and b* (CIELAB) color scale. Ten specimens from each group were then immersed in two different beverages (cherry juice and coke) for seven days. After immersion, the color value of each specimen was re-measured. Each sample was brushed with whitening toothpaste for 30 seconds using an electric toothbrush. The samples were kept in distilled water at room temperature and brushing continued twice a day for seven days. The color change value, Delta E (ΔE), was calculated. Data were analyzed by two-way ANOVA and post hoc Tukey's test. Results: When the results were evaluated, after the colored samples had been brushed with whitening toothpaste, a difference was found between the Delta E values according to the materials used (p<0.001), but no difference was found in relation to the beverages (p>0.001). When the values of the color changes were evaluated after the first brushing with whitening toothpaste and before the specimens were colored with drinks, a difference was observed in the Fuji II cola, Fuji II cherry, and Equia Forte cola groups (p<0.05). When the values of the color changes were evaluated for specimens in which brushing had been done twice a day for seven days with whitening toothpaste and before they were colored with drinks, a significant difference was observed in the Fuji II cherry and Equia Forte cola groups (p<0.05). Conclusion: Using Signal White Now whitening toothpaste for 2 min 2 times a day for seven days caused significant changes in the color of the restorative materials. The color change is dependent upon the type of restorative material that is used.   How to cite this article: Kahvecioğlu F, Çoban E, Ülker HE. The effect of optical brightening toothpaste on the color stability of esthetic restorative materials. Int Dent Res 2021;11(Suppl.1):80-4. https://doi.org/10.5577/intdentres.2021.vol11.suppl1.13   Linguistic Revision: The English in this manuscript has been checked by at least two professional editors, both native speakers of English.

scholarly journals Impact of Bleaching before or after Veneer Preparation on Color Masking Ability of Laminate Veneers: An In Vitro Study

2021 ◽  
Vol 2021 ◽  
pp. 1-9
Author(s):  
Gollshang Ahmad Mhammed Dalloo ◽  
Bestoon Mohammed Faraj ◽  
Abdulsalam Rasheed Al-Zahawi
Keyword(s):  
Hydrogen Peroxide ◽  
Color Change ◽  
In Vitro Study ◽  
Tooth Discoloration ◽  
Significant Difference ◽  
Color System ◽  
The Difference ◽  
Laminate Veneers ◽  
Cielab Color

Purpose. This study evaluates the effect of bleaching before or after veneer preparation and the depth of preparation on color masking ability of laminate veneers. Methods. Sixty extracted premolars were artificially stained to vita shade A4, verified by digital spectrophotometer (Vita Easy Shade V), and then divided into three groups: NB = nonbleached , BBP = bleaching before preparation, and BAP = bleaching after preparation. Based on the preparation depths, each group was further divided into two subgroups: S 1 = 0.5   mm and S 2 = 1.0   mm . BBP and BAP were subjected to one session of in-office bleaching using 35% hydrogen peroxide. IPS e-max CAD veneers of 0.5 and 1.0 mm thickness (corresponding to the preparation depths) of the same shade and translucency (HT A1) were cemented immediately to the bleached surfaces. Immediately after cementation, the color change Δ E between the baseline (after staining) and the resulted shades was measured using the Vita Easy Shade V digital spectrophotometer and CIELab color system. Results. Bleached groups exhibited a significant Δ E value compared to the nonbleached group ( p < 0.05 ). BAP showed the highest Δ E value. No significant difference was found between BBP and BAP. S2 revealed a significant Δ E value than S1 ( p < 0.05 ). No significant difference was found between S1of BAP and S2 of NB, BBP, and BAP ( p > 0.05 ). Regarding the color coordinates, the difference between the tested groups was highly significant in lightness ( Δ L ∗ ) ( p < 0.001 ), while no significant differences were found in green/red value ( Δ a ∗ ) and yellow/blue value ( Δ b ∗ ) ( p > 0.05 ). Conclusions. In cases of severe tooth discoloration, one session of in-office bleaching before or after veneer preparation and the preparation depth do not influence the color masking ability of laminate veneers.

scholarly journals Does Modification of Amalgomer with Propolis Alter Its Physicomechanical Properties? An In Vitro Study

2020 ◽  
Vol 2020 ◽  
pp. 1-10
Author(s):  
Reham M. Abdallah ◽  
Amr M. Abdelghany ◽  
Neven S. Aref
Keyword(s):  
Compressive Strength ◽  
Color Change ◽  
In Vitro Study ◽  
Ethanolic Extract ◽  
Color Stability ◽  
Physicomechanical Properties ◽  
X Ray ◽  
Group I ◽  
Significant Difference

Objective. To assess if incorporating ethanolic extract of propolis into ceramic-reinforced glass ionomer (Amalgomer CR) might have an influence on its physicomechanical properties. Materials and Methods. Three groups were assessed; group I: Amalgomer CR (control) and two experimental groups (II and III) of propolis added to the liquid of Amalgomer CR with 25 and 50 v/v %, respectively. Evaluation parameters were color stability, compressive strength, microhardness, and surface roughness. Representative specimens of each group were analyzed by Fourier-transform infrared spectroscopy, energy-dispersive X-ray, X-ray diffraction, and scanning electron microscopy. Analysis of variance (ANOVA) was used to compare the results, followed by a Tukey post hoc test (p<0.05). Results. Nonsignificant color change for both groups of modified Amalgomer CR. Meanwhile, the two experimental groups exhibited a significant increase in both compressive strength and microhardness. Simultaneously, there was a significant difference in roughness values among groups with the lowest roughness values exhibited by the 50 v/v % propolis concentration. Conclusions. Modification of Amalgomer CR with 50 v/v % propolis may increase its mechanical properties without compromising its esthetic. Clinical Significance. Modification of Amalgomer CR by 50 v/v % propolis is supposed to be a hopeful restorative material with favorable characteristics.

scholarly journals Discoloration of different esthetic restorative materials: A spectrophotometric evaluation

2017 ◽  
Vol 11 (02) ◽  
pp. 149-156 ◽  
Author(s):  
Matteo Ceci ◽  
Matteo Viola ◽  
Davide Rattalino ◽  
Riccardo Beltrami ◽  
Marco Colombo ◽  
...  
Keyword(s):  
Red Wine ◽  
Color Change ◽  
In Vitro Study ◽  
Color Stability ◽  
Surface Roughening ◽  
Multiple Comparison Test ◽  
Restorative Materials ◽  
Group A

ABSTRACT Objective: A crucial property of esthetic restorative materials is their long-term color stability. The aim of this in vitro study was to evaluate the color stability of esthetic restorative materials (one microfilled flowable composite, one nanofilled composite, one nanoybrid composite, one microfilled composite, and one nanoybrid ormocer-based composite) after surface roughening with cola and exposure to different staining solutions (coffee and red wine).Materials and Methods: All materials were polymerized into silicone rubber rings (2 mm × 6 mm × 8 mm) to obtain 150 specimens identical in size. Seventy-five specimens of Group A were first exposed to cola for 24 h, and then samples were immersed in coffee or red wine over a 28-day test period. A colorimetric evaluation, according to the CIE L*a*b* system, was performed at 7, 14, 21, 28 days. Shapiro–Wilk test and Kruskal–Wallis analysis of variance were applied to assess significant differences among restorative materials. Means were compared with Scheffe's multiple comparison test at the 0.05 level of significance.Results: Specimens of Group A showed higher variations when compared with Group B's specimens (P < 0.05). After 28 days, the immersion protocols caused a clinically perceivable color change for all materials tested (P < 0.05). CeramX Universal and Admira Fusion showed the lowest ΔE variations (P < 0.05). Conclusions: Staining beverages caused significant discolorations for all the materials tested. The first exposure to cola enhanced the subsequent staining with coffee or red wine. Nanohybrid composites reported the lowest color variations.

scholarly journals Color Stability of Composites After Short-term Oral Simulation: An in vitro Study

2016 ◽  
Vol 10 (1) ◽  
pp. 431-437 ◽  
Author(s):  
Didem Öner Özdaş ◽  
Mağrur Kazak ◽  
Aylin Çilingir ◽  
Meryem Gülce Subaşı ◽  
Murat Tiryaki ◽  
...  
Keyword(s):  
Repeated Measures ◽  
Color Change ◽  
In Vitro Study ◽  
Color Stability ◽  
Black Tea ◽  
Composite Resins ◽  
Pomegranate Juice ◽  
Restorative Materials ◽  
Color Alteration

Background:Although most of the studies investigated color stability of different restorative materials, evaluation of color stability of composites after immersion in multiple beverages in the same day by anin vitrooral simulation study is unclear.Objective:To assess color change of different restorative materials at the end of days 1, 14, and 30 of immersion in multiple liquid types to mimic the oral environmentin vitro.Method:Ten disc-shaped specimens were made from each of four different resin composites (Filtek Z250, Voco x-tra base, Beautifil Flow Plus, Beautifil II). Baseline color value of each sample was measured using a spectrophotometer. Each composite was respectively immersed in coffee, an orange/pomegranate juice mixture, black tea, and a mouth rinse on the same day to mimic daily liquid consumption of individuals. Color measurements were taken after 1, 14, and 30 days by spectrophotometer and color change values were calculated. Statistical analyses were executed by one-way ANOVA/Tukey HSD and repeated-measures ANOVA.Results:All materials showed significant color change after 1, 14, and 30 days (P< 0.01) of immersion in liquids, with the lowest color alteration observed at the 1stday and the highest observed after the 30thday. Among the materials tested, at each time point (1, 14, and 30 days), the lowest color alteration was detected in Filtek Z250 and the highest color alteration was detected in Beautifil II.Conclusion:Color alteration of composite resins is affected by composite type and storage time. With the exception of 1 day of storage, color changes of all materials were substantial and clinically unacceptable.

scholarly journals A Pilot Study on the Degree of Tooth Staining Caused by Pollen Water and Chlorhexidine: In Vitro Study

2021 ◽  
Vol 15 (1) ◽  
pp. 674-679
Author(s):  
Khalid S. Almulhim ◽  
Muhanad S. Alhareky ◽  
Ahmed Mohammed AlDakhil ◽  
Odai Alsultan ◽  
Kasumi K. Barouch
Keyword(s):  
Color Change ◽  
In Vitro Study ◽  
Three Solutions ◽  
Human Teeth ◽  
Oral Rinse ◽  
Significant Difference ◽  
Normal Water ◽  
The Difference ◽  
Sudden Decrease

Background: Chlorhexidine oral rinse has been used as an adjuvant in the treatment of periodontal disease. However, there are drawbacks of using chlorhexidine i.e. tooth staining and other side effects, including allergy reaction. In light of the proven therapeutic properties of pollen water as well as its relatively cheap cost in the market, pollen water has a potential to be an effective alternative to chlorhexidine oral rinse. The aim of this study is to compare the degree of tooth staining influenced by water-based pollen mouthwash to the standard Chlorhexidine mouthwash using spectrophotometer. Materials and Methods: 24 specimens from extracted intact human teeth were soaked into the three different solutions, Chlorhexidine, Pollen water (date palm pollen water suspension), and normal water. Color measurements were carried out by a spectrophotometer devise and recorded at 5 different time intervals. Color change (∆E), Chroma (C*) and Hue (H*) were analyzed and compared among the three solutions. Results: Overall mean ∆E was similar in all groups, significant difference between all time points was found only in pollen water. The change in C* was higher in pollen water as compared to other solutions. There was a subtle increase in H* in the Chlorhexidine samples after week 3. The H* values in pollen water were stable, but a sudden decrease was observed in week 6. The difference in H* among the three solutions was significant after 3 weeks. Conclusion: Within the limitation of our study, it can be concluded that Pollen water stained teeth to a lesser extent than did chlorhexidine. It might be beneficial to use Pollen water as mouthwash however, further investigation is needed regarding the efficacy of plaque control.

scholarly journals In Vitro Effect of Denture Cleansers on the Color Stability of Polyetheretherketone and Other Denture Base Polymers

2021 ◽  
pp. 284-293
Author(s):  
Samet Tekin
Keyword(s):  
Color Change ◽  
Color Stability ◽  
Chemical Compositions ◽  
Denture Base ◽  
Color Changes ◽  
All Solutions ◽  
Significant Difference ◽  
Denture Cleansers

The aim of this in vitro study was to compare the long-term effect of overnight use of denture cleansers with different chemical compositions on the color stability of denture base polymers (DBPs). The four DBPs evaluated were PEEK (PK group), thermoinjection-molded polyamide (PA group), auto-polymerized polymethylmethacrylate (PMMA) (AP group), and heat-polymerized resin PMMA (HP group). The cleaning agents used were Corega tablet (CT), Protefix tablet (PT), and 0.5% sodium hypochlorite (NaOCl) solution (SH). Distilled water (DW) served as a control. Forty-eight disc-shaped specimens (10mm × 2mm) were prepared from each DBP and randomly immersed in the different storage media (n=12 in each group). Color measurements of the specimens before and after immersion in the denture cleansers were made using a spectrophotometer (VITA Easyshade V). The color changes were measured and recorded in L* a* b*. After 120 d, the CIEDE2000 formula was used to calculate color changes (∆E00). For analysis of the data, a multivariate analysis of variance was used (p<0.05).  The results of the statistical analysis revealed significant color change differences in the DBPs immersed in the various denture cleansers (p<0.05). Groups PA and PK showed the highest values for all solutions. AP-SH showed the highest ∆E00 value in group AP, no significant difference was found between other solutions. In group HP, there was no statistically significant difference between the average ∆E00 values of all solutions.  Long-term daily use of the denture cleansers affected the color stability of all the DBPs, although the level of color change was acceptable. Laboratory and clinical studies on the color stability of PEEK are needed to confirm the results of this study.

scholarly journals Effect of brushing on colour stability of nanohybrid composite after immersion in brewed beverages – an in vitro study

2021 ◽  
Author(s):  
Jayeeta Verma ◽  
Leena Padhye ◽  
Sidharth Verma
Keyword(s):  
Color Change ◽  
In Vitro Study ◽  
Color Stability ◽  
Distilled Water ◽  
Staining Solution ◽  
Significant Difference ◽  
Nanohybrid Composite ◽  
Powered Toothbrush ◽  
Disk Sample

Background and aims. In today’s world, everyone is mindful of one’s appearance and appreciates aesthetics. Of the various restorative materials available, composites are considered as the most aesthetic with good color stability. This study aims at finding the effect of brushing  on the color stability of nanohybrid composite after being immersed in various beverages. Methods. Thirty disk specimens were prepared for each staining solution (N=30), with a total of 90 specimens. The disk specimens for each staining solution were then sub divided into 2 groups (N=15): brushing and non-brushing. After preparation, the specimens were soaked in distilled water for 24 hours in separate containers. Baseline color of the samples was evaluated using spectrophotometer. The samples were then immersed in tea, coffee or water. The groups of samples to be brushed were held in the mold and 20 strokes of brushing using an electronically powered toothbrush were done on each side of the disk sample. The color was re-evaluated after a period of 14 days. Results. When comparing among the three beverages, tea showed the highest ΔE*ab indicating greatest discoloration when compared to coffee and water. This can be graded as tea > coffee > water. However, statistically there was no significant difference between tea and coffee. When compared within tea, coffee, or water specimens the non - brushed specimens showed greater discoloration compared to the brushed specimens both clinically and statistically. Conclusion. When immersing the specimens in the solutions, tea showed more color change compared to coffee, making the specimens clinically unacceptable. However, brushing the specimens reduced the discoloration when compared to non–brushing, making the coffee specimens clinically acceptable.

scholarly journals Effects of Mouth Rinses on Color Stability of Resin Composites

2008 ◽  
Vol 02 (04) ◽  
pp. 247-253 ◽  
Author(s):  
Cigdem Celik ◽  
Bulem Yuzugullu ◽  
Selim Erkut ◽  
Kıvanc Yamanel
Keyword(s):  
Color Change ◽  
Calculated Data ◽  
Color Stability ◽  
Color Difference ◽  
Distilled Water ◽  
Significance Level ◽  
Color Changes ◽  
Mouth Rinses ◽  
Significant Difference ◽  
Restorative Materials

ABSTRACTObjectives: The aim of this study was to evaluate the effects of 3 commercially available mouth rinses on the color stability of 4 different resin-based composite restorative materials.Methods: Forty disc-shaped specimens (10x2 mm) were prepared from each of the following materials: A nanofill composite Filtek Supreme XT (3M/Espe, St. Paul, MN, USA); a packable lowshrinkage composite, AeliteLS Packable (BISCO, Inc, Shaumburg, IL, USA); nanoceramic compositeresin Ceram-X (Dentsply, Konstanz, Germany); a microhybrid composite, and Aelite All-Purpose Body (BISCO). The specimens were then incubated in distilled water at 37°C for 24 hours. The baseline color values (L*, a*, b*) of each specimen were measured with a colorimeter according to the CIELAB color scale. After baseline color measurements, 10 randomly selected specimens from each group were immersed in 1 of the 3 mouth rinses and distilled water as control. The specimens were stored in 20 mL of each mouth rinse (Oral B Alcohol-free, Listerine Tooth Defense Anti-cavity Fluoride Rinse and Klorhex) for 12 hours. After immersion, the color values of all specimens were remeasured, and the color change value ΔE*ab was calculated. Data were analyzed using a 2-way analysis of variance at a significance level of .05.Results: All specimens displayed color changes after immersion, and there was a statistically significant difference among restorative materials and mouth rinses (P<.05); however, the change was not visually perceptible (ΔE*ab<3.3). The interaction between the effect of mouth rinses and type of restorative materials was not statistically significant (P>.05).Conclusions: It may be concluded that although visually nonperceptible, all resin restorative materials tested showed a color difference after immersion in different mouth rinses. (Eur J Dent 2008;2:247-253)

Sign in / Sign up

Export Citation Format

Share Document