ALLVAC 38-644

Alloy Digest ◽  
2004 ◽  
Vol 53 (7) ◽  
Keyword(s):  
High Strength ◽  
Heat Treating ◽  
Aged Condition ◽  
Beta Titanium Alloy ◽  
Solution Treated Condition ◽  
Solution Treated ◽  
Treated Condition ◽  
Beta Titanium ◽  
Metastable Beta ◽  
Strength And Ductility

Abstract Allvac 38-644 is a metastable beta titanium alloy known for its ductility in the solution treated condition and its high strength and ductility in the solution treated and aged condition. This datasheet provides information on composition, physical properties, hardness, elasticity, and tensile properties. It also includes information on forming, heat treating, machining, and joining. Filing Code: TI-134. Producer or source: Allvac Metals Company.

TIMETAL 15-3

Alloy Digest ◽  
1992 ◽  
Vol 41 (11) ◽  
Keyword(s):  
Titanium Alloy ◽  
High Strength ◽  
Heat Treating ◽  
Aged Condition ◽  
Beta Titanium Alloy ◽  
Solution Treated Condition ◽  
Solution Treated ◽  
Treated Condition ◽  
Beta Titanium ◽  
Metastable Beta

Abstract TIMETAL 15-3 is a metastable beta titanium alloy that offers substantial weight reductions over other engineering materials. In the solution treated condition, it has excellent cold formability; in the aged condition, it has high strength. TIMETAL 15-3 is usually acceptable for use at temperatures up to 550 F. This datasheet provides information on composition, physical properties, and tensile properties. It also includes information on forming and heat treating. Filing Code: Ti-101. Producer or source: Titanium Metals Corporation (Timet).

CARTECH Ti 15V-3Cr-3Sn-3Al

Alloy Digest ◽  
2021 ◽  
Vol 70 (7) ◽  
Keyword(s):  
High Strength ◽  
Heat Treating ◽  
Beta Titanium Alloy ◽  
Treated Condition ◽  
Beta Titanium ◽  
Heat Treated ◽  
Technology Corporation ◽  
Heat Treated Condition ◽  
Carpenter Technology Corporation ◽  
Metastable Beta

Abstract CarTech Ti 15V-3Cr-3Sn-3Al (UNS R58153) is a metastable beta titanium alloy that offers substantial weight reduction in comparison with other engineering materials. If used in the solution heat treated condition, the alloy has excellent cold formability. In the aged condition, the alloy has high strength. It is acceptable for use up to 230 °C (550 °F). This datasheet provides information on composition, physical properties, elasticity, and tensile properties. It also includes information on corrosion resistance as well as forming, heat treating, and joining. Filing Code: Ti-180. Producer or source: Carpenter Technology Corporation.

MST 431

Alloy Digest ◽  
1961 ◽  
Vol 10 (10) ◽  
Keyword(s):  
Aging Treatment ◽  
High Strength ◽  
Heat Treating ◽  
Temperature Performance ◽  
Solution Treated Condition ◽  
Solution Treated ◽  
Treated Condition ◽  
Alpha Beta ◽  
Reactive Metals ◽  
Principal Advantage

Abstract MST 431 is an alpha-beta type sheet alloy presently being supplied in the solution treated, solution treated and aged, and annealed conditions. Its principal advantage is good formability in the solution treated condition with subsequent high strength capability through an aging treatment. Properties indicate good strength and thermal stability for sheet applications up to 800 F for long times. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as creep. It also includes information on high temperature performance and corrosion resistance as well as forming, heat treating, machining, joining, and surface treatment. Filing Code: Ti-30. Producer or source: Reactive Metals Corporation.

ZAPP TiAl6V4

Alloy Digest ◽  
2020 ◽  
Vol 69 (12) ◽  
Keyword(s):  
Corrosion Resistance ◽  
Titanium Alloy ◽  
High Strength ◽  
Heat Treating ◽  
Aged Condition ◽  
Beta Titanium Alloy ◽  
Excellent Corrosion Resistance ◽  
Beta Titanium ◽  
Heat Treated ◽  
Low Weight

Abstract Zapp TiAl6V4 is an alpha-beta titanium alloy that is used in the annealed or solution heat treated and aged condition for applications requiring high strength, relatively low weight, and excellent corrosion resistance. It is typically used in the low to moderate temperature range (up to about 400 °C, or 750 °F). Ti-6Al-4V is the most widely used titanium alloy, accounting for more than 50% of the total titanium used. The aerospace industry accounts for more than 80% of this usage. This datasheet provides information on composition, physical properties, elasticity, and tensile properties. It also includes information on corrosion resistance as well as forming, heat treating, machining, and joining. Filing Code: Ti-173. Producer or source: Zapp AG.

ALUMINUM A356.0

Alloy Digest ◽  
1985 ◽  
Vol 34 (6) ◽  
Keyword(s):  
High Strength ◽  
Heat Treating ◽  
Good Combination ◽  
Age Hardening ◽  
Casting Alloy ◽  
Aged Condition ◽  
Solution Treated ◽  
Mold Casting ◽  
Hardening Heat Treatment ◽  
Strength And Ductility

Abstract ALUMINUM A356.0 is a sand and permanent-mold casting alloy. It responds to an age-hardening heat treatment. This alloy has a relatively good combination of strength and ductility in the solution-treated and aged condition. Aluminum A356.0 is recommended for aircraft and missile components where high strength and resistance to corrosion are required. This datasheet provides information on composition, physical properties, hardness, elasticity, tensile properties, and compressive and shear strength as well as fatigue. It also includes information on corrosion resistance as well as casting, heat treating, machining, and joining. Filing Code: Al-258. Producer or source: Various aluminum companies.

Ti-8Mo-8V-2Fe-3Al

Alloy Digest ◽  
1973 ◽  
Vol 22 (5) ◽  
Keyword(s):  
Fracture Toughness ◽  
Corrosion Resistance ◽  
Titanium Alloy ◽  
High Temperature ◽  
High Strength ◽  
Heat Treating ◽  
Beta Titanium Alloy ◽  
Temperature Performance ◽  
Beta Titanium ◽  
Metastable Beta

Abstract Ti-8Mo-8V-2Fe-3A1 is a metastable beta titanium alloy that can be age hardened to high-strength levels. Aging in the range of 800-1200 F partially transforms beta to alpha to produce the high strength. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as fracture toughness. It also includes information on low and high temperature performance, and corrosion resistance as well as forming, heat treating, machining, and joining. Filing Code: Ti-68. Producer or source: Titanium Metals Corporation of America.

Decomposition of the metastable beta titanium alloy Ti-15-3

1983 ◽  
Vol 41 ◽  
pp. 264-265
Author(s):  
Y. L. Chen ◽  
S. Fujlshiro
Keyword(s):  
Low Cost ◽  
High Strength ◽  
Alpha Phase ◽  
Thick Sheet ◽  
Omega Phase ◽  
Beta Titanium Alloy ◽  
Beta Titanium ◽  
Beta Matrix ◽  
Metastable Beta ◽  
Very High

Metastable beta titanium alloys have been known to have numerous advantages such as cold formability, high strength, good fracture resistance, deep hardenability, and cost effectiveness. Very high strength is obtainable by precipitation of the hexagonal alpha phase in a bcc beta matrix in these alloys. Precipitation hardening in the metastable beta alloys may also result from the formation of transition phases such as omega phase. Ti-15-3 (Ti-15V- 3Cr-3Al-3Sn) has been developed recently by TIMET and USAF for low cost sheet metal applications. The purpose of the present study was to examine the aging characteristics in this alloy.The composition of the as-received material is: 14.7 V, 3.14 Cr, 3.05 Al, 2.26 Sn, and 0.145 Fe. The beta transus temperature as determined by optical metallographic method was about 770°C. Specimen coupons were prepared from a mill-annealed 1.2 mm thick sheet, and solution treated at 827°C for 2 hr in argon, then water quenched. Aging was also done in argon at temperatures ranging from 316 to 616°C for various times.

SP 700

Alloy Digest ◽  
1995 ◽  
Vol 44 (6) ◽  
Keyword(s):  
High Strength ◽  
Heat Treating ◽  
Bend Strength ◽  
Beta Titanium Alloy ◽  
Superplastic Behavior ◽  
Temperature Performance ◽  
Beta Titanium ◽  
Wide Range ◽  
Alpha Beta ◽  
Cold Workability

Abstract SP 700 is a high strength, beta-rich alpha-beta titanium alloy. It was developed with the following attributes: (1) excellent hot- and cold-workability; (2) enhanced hardenability with a wide range of mechanical properties that can be obtained by heat treatment; and (3) superior superplastic behavior at low temperature (around 1050 K). This datasheet provides information on composition, physical properties, microstructure, elasticity, tensile properties, and bend strength. It also includes information on high temperature performance as well as heat treating. Filing Code: TI-107. Producer or source: NKK Corporation.

UNS R54620

Alloy Digest ◽  
1987 ◽  
Vol 36 (7) ◽  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Time Use ◽  
Temperature Stability ◽  
High Strength ◽  
Heat Treating ◽  
High Temperature Stability ◽  
Beta Titanium Alloy ◽  
Beta Titanium ◽  
Long Time

Abstract UNS No. R54620 is an alpha-beta titanium alloy. It has an excellent combination of tensile strength, creep strength, toughness and high-temperature stability that makes it suitable for service to 1050 F. It is recommended for use where high strength is required. It has outstanding advantages for long-time use at temperatures to 800 F. This datasheet provides information on composition, physical properties, elasticity, tensile properties, and bend strength as well as creep. It also includes information on high temperature performance and corrosion resistance as well as forming, heat treating, machining, joining, and surface treatment. Filing Code: Ti-86. Producer or source: Titanium alloy mills.

Sign in / Sign up

Export Citation Format

Share Document