Analysis on Welding Performance of the WH80 Steel Used in the Hydraulic Support

2011 ◽  
Vol 225-226 ◽  
pp. 111-114
Author(s):  
Lian Min Cao ◽  
Guo Xiu Su ◽  
Qing Liang Zeng ◽  
Xing Yuan Xiao
Keyword(s):  
Heat Affected Zone ◽  
High Strength Steel ◽  
Arc Welding ◽  
High Strength ◽  
Hardness Test ◽  
Bend Test ◽  
Hydraulic Support ◽  
Good Material

This paper mainly has carried on the analysis to the welding performance of high strength steel WH80, through the stretch and the bend test of manual welding rod, arc welding, the slanting y bevel weld crack test and the highest hardness test in welding heat-affected zone. It indicates that the WH80 steel has the good welding performance and is good material for hydraulic support.

Welding of Fe-Al Intermetallic Compound and Steel by SPS Technology

2012 ◽  
Vol 581-582 ◽  
pp. 582-585
Author(s):  
Guo Dong Zhang ◽  
Ya Dong Xiao ◽  
Nian Liu ◽  
Min Hong
Keyword(s):  
Intermetallic Compound ◽  
Base Metal ◽  
Heat Affected Zone ◽  
High Strength Steel ◽  
Chemical Potential ◽  
High Strength ◽  
Micro Hardness ◽  
Axial Pressure ◽  
Welding Joint ◽  
Short Period

The welding between Fe-Al intermetallic compound and high-strength steel was done via SPS technology. Microstructure, elements concentration and micro-hardness of welding joint were examined. The results indicated that there was no obvious welding heat-affected zone in both Fe-Al intermetallic compound and high-strength steel. The HAZ microstructures of high-strength steel were mainly martensite. In Fe-Al intermetallic compound, the grain size of heat-affected zone was larger than that of base metal and the density of heat-affected zone was lower than that of base metal. Besides, the grains of base metal had deformation phenomena. The welding joint had steady performance and the connection was reliable. Under the influence of chemical potential differences, unidirectional impulses discharge current and axial pressure, elements diffused perfectly in a short period of time.

Study on the hybrid laser-arc welding of 3 mm thick high-strength steel with high speed

2018 ◽  
Vol 6 (2) ◽  
pp. 026546 ◽  
Author(s):  
Zhang Peilei ◽  
Gu Siyuan ◽  
Liu Zhengjun ◽  
Yu Zhishui
Keyword(s):  
High Strength Steel ◽  
Arc Welding ◽  
High Speed ◽  
High Strength ◽  
Hybrid Laser Arc Welding

Hybrid laser/arc welding of thick high-strength steel in different configurations

2017 ◽  
Vol 6 (2) ◽  
pp. 176-188 ◽  
Author(s):  
M. Mazar Atabaki ◽  
N. Yazdian ◽  
R. Kovacevic
Keyword(s):  
High Strength Steel ◽  
Arc Welding ◽  
High Strength ◽  
Hybrid Laser Arc Welding

Multi-Pass Route Planning for Thick Plate of Low Alloy High Strength Steel by Double-Sided Double Arc Welding

2012 ◽  
Vol 590 ◽  
pp. 28-34 ◽  
Author(s):  
Cheng Dong Yang ◽  
H.Y. Huang ◽  
H.J. Zhang ◽  
Y.X. Chen ◽  
San Ben Chen
Keyword(s):  
High Strength Steel ◽  
Arc Welding ◽  
Thick Plate ◽  
High Efficiency ◽  
Route Planning ◽  
High Strength ◽  
Welding Parameters ◽  
Welding Torch ◽  
Welding System

Double-sided double arc welding (DSDAW), a high efficiency method for welding thick plate of low alloy high strength steel which does not require back chipping is used in this paper, research on multi-pass route planning for thick plate of low alloy high strength plate by double-sided double arc welding. Firstly, establish a double-sided double arc welding system that can realize thick plate of low alloy high strength steel double-sided double arc welding by double robots. Then, Propose the multi-pass route planning for thick plate of low alloy high strength steel by double-sided double arc welding by means of misplaced welding. According to the welding parameters and the geometry size of groove, plan the layers, the number of beads and the concrete position of the welding torch for each bead. Finally, the welding experiment has been done to verify the effectiveness of multi-pass route planning. The results of welding experiment are approximately agreement with the multi-pass route planning results. The backing weld can get better appearance in the front and guarantee fusion penetration in the back simultaneously. On the basis of the multi-pass welding route planning, good fusion and leveling interface can be obtained after filler passes.

Hydrogen-induced cold cracking in heat-affected zone of low-carbon high-strength steel

2014 ◽  
Vol 94 (12) ◽  
pp. 764-771 ◽  
Author(s):  
Liangyun Lan ◽  
Xiangwei Kong ◽  
Zhiyong Hu ◽  
Chunlin Qiu
Keyword(s):  
Heat Affected Zone ◽  
High Strength Steel ◽  
High Strength ◽  
Cold Cracking ◽  
Low Carbon
Sign in / Sign up

Export Citation Format

Share Document