Study on the Thermal Fatigue Resistance of Ductile Iron

2012 ◽  
Vol 512-515 ◽  
pp. 2093-2096
Author(s):  
Zhang Yin Xu ◽  
Yin Ju Jiang
Keyword(s):  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Ductile Iron ◽  
Service Condition ◽  
Nodular Cast Iron ◽  
Temperature Cycle ◽  
Matrix Structure ◽  
Thermal Fatigue Resistance ◽  
Aluminum Ingot ◽  
Bainitic Structure

Simulated service condition of aluminum ingot casting molds, samples of ductile iron was tested in a temperature Cycle from750°C and water-cooled to 25°C till a crack appeared in the sample. its thermal fatigue resistance of samples based various microstructure included as—casting, annealing or alloying ferritic matrix structure, or alloying pearlitic structure and the upper or low the bainitic structure had been researched. The study shows that the thermal fatigue resistance of the annealing ferritic nodular cast iron was superior to the others.

Thermal Fatigue of the Selected Tool Steel Applied for Metal Moulds Elements in Die Casting of Metals

2013 ◽  
Vol 58 (3) ◽  
pp. 757-761 ◽  
Author(s):  
J. Zych
Keyword(s):  
Fatigue Resistance ◽  
Tool Steel ◽  
Thermal Fatigue ◽  
Test Bench ◽  
Die Casting ◽  
Fatigue Tests ◽  
Vanadium Content ◽  
Temperature Cycle ◽  
Thermal Fatigue Resistance ◽  
Steel Grades

Abstract The work presents the results of research on thermal fatigue resistance of four steel grades used in the production of metal moulds for pressure diecasting. Thermal fatigue tests were performed on an original test bench using the L.F Coffin method - resistance heated samples. The steels additionally contained alloy additives in the following proportions: Cr = 5.0 ÷5.3%, Mo = 1.30 ÷3.0%, and V = 0.50 ÷1.0%. The thermal fatigue was analyzed using the temperature cycle: Tmin = 200°C; Tmax = 700 ÷750°C. The samples endured between few to few dozens of thousands of temperature cycles in the above temperature range. Steel with maximum vanadium content exhibited the highest level of resistance.

scholarly journals Bionic Repair of Thermal Fatigue Cracks in Ductile Iron by Laser Melting with Different Laser Parameters

Metals ◽  
2020 ◽  
Vol 10 (1) ◽  
pp. 101 ◽  
Author(s):  
Siyuan Ma ◽  
Ti Zhou ◽  
Hong Zhou ◽  
Geng Chang ◽  
Benfeng Zhi ◽  
...  
Keyword(s):  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Ductile Iron ◽  
Laser Energy ◽  
Fatigue Cracks ◽  
Fatigue Cracking ◽  
Unit Distance ◽  
Thermal Fatigue Resistance ◽  
Brake Discs ◽  
Thermal Fatigue Cracks

Nodular iron brake discs typically fail due to serious thermal fatigue cracking, and the presence of graphite complicates the repair of crack defects in ductile iron. This study presents a novel method for remanufacturing ductile iron brake discs based on coupled bionics to repair thermal fatigue cracks discontinuously using bio-inspired crack blocking units fabricated by laser remelting at various laser energy inputs. Then, the ultimate tensile force and thermal fatigue crack resistance of the obtained units were tested. The microhardness, microstructure, and phases of the units were characterized using a digital microhardness meter, optical microscopy, scanning electron microscopy, and X-ray diffraction. It was found that the units without defects positively impacted both the thermal fatigue resistance and tensile strength. The unit fabricated at a laser energy of 165.6 − 15 + 19 J/ mm 2 had sufficient depth to fully close the crack, and exhibited superior anti-cracking and tensile properties. When the unit distance is 3 mm, the sample has excellent thermal fatigue resistance. In addition, the anti-crack mechanism of the units was analysed.

THERMO-SPAN ALLOY

Alloy Digest ◽  
1994 ◽  
Vol 43 (2) ◽  
Keyword(s):  
Physical Properties ◽  
Tensile Properties ◽  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Rupture Strength ◽  
Stress Rupture ◽  
Heat Treating ◽  
Thermal Fatigue Resistance ◽  
Stress Rupture Strength

Abstract THERMO-SPAN ALLOY is a precipitation-hardenable superalloy with a low coefficient of expansion combined with tensile and stress-rupture strength. Thermal fatigue resistance is inherent. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as creep. It also includes information on forming and heat treating. Filing Code: FE-105. Producer or source: Carpenter.

The Development of High-Alumina Heat Resisting Alloy Used for Scaleboard

2011 ◽  
Vol 287-290 ◽  
pp. 949-952
Author(s):  
Yong Zhe Fan ◽  
Yu Chen Song ◽  
Rui Na Ma
Keyword(s):  
Oxidation Resistance ◽  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Abrasion Resistance ◽  
High Alumina ◽  
Thermal Fatigue Resistance ◽  
Dry Quenching

According to the requirement of the pot scaleboard of Coke Dry Quenching, high content of aluminium heat resisting alloy was developed.Through changing the content of carbon,boron and titanium,the best compounding of the heat resisting alloy was Fe-8Al-1B-5Cr-0.3C-0.5Ti.The microstructure of this kind of alloy was observed and analyzed with optical microscope.It also had good performance of oxidation resistance,abrasion resistance and thermal fatigue resistance,it was suitable for using as pot scaleboard of CDQ.

The Microstructure and Properties of Coating from Mo2FeB2 Cermet on Surface of H13 Steel by Reactive Flame Spraying

2010 ◽  
Vol 97-101 ◽  
pp. 1321-1327 ◽  
Author(s):  
Xiao Ping Zhou ◽  
Xin Bin Hu ◽  
Yi Sheng Xu
Keyword(s):  
Wear Resistance ◽  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Ceramic Coating ◽  
Flame Spraying ◽  
H13 Steel ◽  
Thermal Fatigue Resistance ◽  
Microstructure And Properties ◽  
Cermet Coating ◽  
Ternary Boride

The microstructure and properties of ternary boride ceramic coating prepared by reactive flame spraying on surface of H13 steel are studied as well as the microstructures, microhardness, wear resistance and thermal fatigue resistance of the coating. The results show that the Mo2FeB2 cermet coating by reactive flame spraying has good wear resistance and thermal fatigue resistance and its microhardness can even reach 1200 HV.

A New Method to Study the Thermal Fatigue Resistance of Molybdenum by High Power Laser Irradiation

2012 ◽  
Vol 184-185 ◽  
pp. 1384-1388 ◽  
Author(s):  
Shuai Lu ◽  
Hong Wei Li ◽  
Dun Bo Yu ◽  
Ming Pang ◽  
Bo Wang
Keyword(s):  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
High Power ◽  
Laser Heating ◽  
Fatigue Cracks ◽  
Crack Density ◽  
Scale Production ◽  
High Power Laser ◽  
Power Laser ◽  
Thermal Fatigue Resistance

In single roll rapid quenching molding, especially for the preparation of amorphous ribbons and rare earth permanent magnetic materials, the chilling roll is an extremely important component of the preparation equipment. However, frequent repair of the roll is not conducive to continuous large-scale production because of its poor thermal fatigue resistance. Molybdenum is gradually being used as chilling roll material in some applications, and in the present paper a new approach to study the thermal fatigue resistance of molybdenum is based on laser pulse irradiation on the molybdenum surface. A new designed device effectively prevents the molybdenum to be oxidized during the laser heating test. The experiments of thermal fatigue damage on molybdenum were conducted by the high power laser. The results shows that the fatigue cracks had been propagated in the irradiated region after the specimen was loaded by 200 times pulsed laser heating. There is a greater crack density in the laser heating brim region than in the center of the irradiated region. According to the transgranular mode of crack propagation in the laser heating brim region and intergranular mode in the center of the irradiated region, the maximum stress took place at the intersection region due to the great temperature gradient in the laser heating brim region. Continued basis-oriented experiments are planned, regarding the mechanism of thermal fatigue crack initiation and propagation for chilling roll materials.

Failure prediction of the thermal fatigue resistance of a glass

1976 ◽  
Vol 11 (3) ◽  
pp. 458-464 ◽  
Author(s):  
D. P. H. Hasselman ◽  
R. Badaliance ◽  
K. R. McKinney ◽  
C. H. Kim
Keyword(s):  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Failure Prediction ◽  
Thermal Fatigue Resistance

Freeze and Thaw and Thermal Fatigue Resistance of LMM Incorporating CNT

2017 ◽  
Author(s):  
Ahmed Abdel-Mohti ◽  
Nathan Craft ◽  
Michael J. Rider ◽  
Jed Marquart ◽  
David Sawyers ◽  
...  
Keyword(s):  
Fatigue Resistance ◽  
Thermal Fatigue ◽  
Thermal Fatigue Resistance ◽  
Freeze And Thaw
Sign in / Sign up

Export Citation Format

Share Document