Effects of High Co Contents in Fe-Cr-Mo-C-B-Y Alloy on the Glass Forming and the Mechanical Properties

2013 ◽  
Vol 652-654 ◽  
pp. 1054-1058 ◽  
Author(s):  
Qing Jun Chen ◽  
Jiang Lie Liu ◽  
Xian Liang Zhou ◽  
Jun Shen ◽  
Xiao Zhen Hua
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Thermal Diffusivity ◽  
Metallic Glasses ◽  
Amorphous Region ◽  
Glass Forming Ability ◽  
Copper Mold ◽  
Casting Method ◽  
Glass Forming ◽  
Wedge Shape

A series of wedge shape Fe24+XCo24-XCr15Mo14C15B6Y2 (x=0,2,4,6,8) samples were prepared by copper mold suction casting method. The effects of high Co contents on glass forming ability (GFA) and mechanical properties of Fe24+XCo24-X Cr15Mo14C15B6Y2 bulk metallic glasses (BMG) were investigated, respectively. The glass forming ability of bulk amorphous Fe24+XCo24-XCr15Mo14C15B6Y2 (x=0,2,4,6,8) and Fe41Co7Cr15Mo14C15B6Y2 alloys have been researched. Simultaneously, the thermal conductivity parameters of those alloys were tested. The maximum thickness of amorphous region of wedge-shaped samples are dm =7.80 mm for Fe28Co20Cr15Mo14C15B6Y2, dm =7.10 mm for Fe41Co7Cr15Mo14C15B6Y2 and the thermal conductivity are λ=7.11 w.m-1.k-1 and 7.19 w.m-1.k-1, the thermal diffusivity are α=1.875 mm2/s and 1.905 mm2/s for Fe28Co20Cr15Mo14C15B6Y2 and Fe41Co7Cr15Mo14C15B6Y2 BMGs, respectively. The glass forming ability of Fe28Co20Cr15Mo14C15B6Y2 alloy is bigger than that of well known Fe41Co7Cr15Mo14C15B6Y2 alloy. With the change of Co content, the Vickers hardness of Fe24+XCo24-XCr15Mo14C15B6Y2 (x=0,2,4,6,8) change from 1292 to 1322Hv.

scholarly journals Effect of Sn addition on the glass-forming ability and mechanical properties of Ni-Nb-Zr bulk metallic glasses

2011 ◽  
Vol 56 (36) ◽  
pp. 3926-3931 ◽  
Author(s):  
DengKe Li ◽  
HaiFeng Zhang ◽  
AiMin Wang ◽  
ZhengWang Zhu ◽  
ZhuangQi Hu
Keyword(s):  
Mechanical Properties ◽  
Metallic Glasses ◽  
Bulk Metallic Glasses ◽  
Glass Forming Ability ◽  
Glass Forming

Effect of B2O3 Fluxing on Glass-Forming Ability and Soft Magnetic Properties of Fe(-Co)-B-Si-Nb Bulk Metallic Glasses

2014 ◽  
Vol 783-786 ◽  
pp. 1895-1900 ◽  
Author(s):  
Teruo Bitoh
Keyword(s):  
Magnetic Properties ◽  
Metallic Glasses ◽  
Bulk Metallic Glasses ◽  
Glass Forming Ability ◽  
The Other ◽  
Maximum Diameter ◽  
Soft Magnetic Properties ◽  
Copper Mold ◽  
Soft Magnetic ◽  
Glass Forming

The effect of B2O3 fluxing on the glass-forming ability (GFA), the structure and the soft magnetic properties of Fe (-Co)-B-Si-Nb bulk metallic glasses (BMGs) has been investigated. The large Fe-Co-B-Si-Nb BMG specimens with diameters up to 7.7 mm, which is approximately 1.5 times as large as that of the maximum diameter of the copper mold cast one (= 5 mm), were prepared by the fluxing and water quenching. Thus the GFA of the Fe-Co-B-Si-Nb BMG are improved by the fluxing. It was confirmed that the soft magnetic properties of the Fe-Co-B-Si-Nb BMG are also improved by the fluxing. On the other hand, it was found for the Co-free Fe-B-Si-Nb BMG that the B2O3 fluxing promotes the precipitation of the α-Fe (-Si) and Fe2B phases in the central region of the specimens; i.e., the GFA of the Fe-B-Si-Nb BMG is decreased by the fluxing. The Fe-B-Si-Nb BMG specimens show a flat hysteresis loop, indicating a good linear relationship between the magnetic induction and the applied magnetic field. These results of the Fe-B-Si-Nb BMG show that it is possible to develop a new soft magnetic material that exhibits constant permeability, which is necessary for producing inductors and choke coils.

Thermal stability, magnetic and mechanical properties of Fe–Dy–B–Nb bulk metallic glasses with high glass-forming ability

2014 ◽  
Vol 46 ◽  
pp. 85-90 ◽  
Author(s):  
Jiawei Li ◽  
Weiming Yang ◽  
Diana Estévez ◽  
Guoxin Chen ◽  
Wenguang Zhao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Metallic Glasses ◽  
Bulk Metallic Glasses ◽  
Glass Forming Ability ◽  
Glass Forming

Effect of Minor Si and Ag Additions on Glass-Forming Ability of Ti-Cu-Co-Zr-Sn-Be Bulk Metallic Glass

2011 ◽  
Vol 688 ◽  
pp. 400-406
Author(s):  
Xin Fang Zhang ◽  
Hong Xiang Li ◽  
Zhi Qiang Jiang ◽  
Seong Hoon Yi
Keyword(s):  
Metallic Glass ◽  
Metallic Glasses ◽  
Base Alloy ◽  
Maximum Size ◽  
Amorphous Structure ◽  
Glass Forming Ability ◽  
Copper Mold ◽  
Glass Forming ◽  
Splat Quenching ◽  
Ag Additions

Effect of Minor Si and Ag additions on glass-forming ability (GFA) of the base Ti44Cu38.9Co4Zr6Sn2Be5.1(at. %) alloy are studied. (Ti44Cu38.9Co4Zr6Sn2Be5.1)100-xRx(R = Si, Ag, x=0, 1, 2, 3 at. %) metallic glasses are formed by splat-quenching and copper mold suction casting. It is found that the minor Si and Ag additions enhance the glass-forming ability of Ti44Cu38.9Co4Zr6Sn2Be5.1greatly. The maximum size of fully amorphous structure is increased from 4 mm for base alloy to be larger than 6 mm for alloys containing 1-2 at. % Si/Ag, while Si/Ag more than 2 at. % additions decrease the GFA.

Sign in / Sign up

Export Citation Format

Share Document