Влияние редкоземельных металлов на стеклообразующую способность и кристаллизацию аморфных сплавов CoFeSiBNb

In present work amorphous alloys Co48Fe25Si4B19Nb4-R (R = Nd, Sm, Tb, Yb) were obtained by planar flow casting in the form of ribbons with 3-5 mm wide and 35-45 μm thickness. It was found that crystallization process goes into two stages and depends on the used rare-earth addition and its content in the alloy by differential thermal analysis method. Glass-forming ability criteria were calculated. It is shown that paramagnetic Curie temperature of alloys in liquid state can be used as their a-priori criterion of glass-forming ability.

Investigations of Thermal Stability and Spectroscopic Features of Sm3+ Doped Strontium Aluminate Glasses

In the present work, a series of Sm3+ doped transparent strontium aluminate glasses with the composition Al2O3-(3-x)SrO: xSm3+ (x = 0, 0.01, 0.03, 0.06, 0.1, 0.2) were fabricated by a containerless process using an aerodynamic levitation furnace. The structural characteristics, density, Vicker’s hardness, and thermal and spectroscopic behaviors of these glasses were investigated. All the glasses exhibit excellent thermal stabilities (Tg ≥ 792 °C) and the glass-forming ability is enhanced with the increasing content of Sm3+. The emission spectra recorded under an excitation of 404 nm show four emission transitions as a result of 4G5/2 translated to the lower states of 6H5/2, 6H7/2, 6H9/2, and 6H11/2, and a bright orange-reddish luminescence can be observed in Al2O3-(3-x)SrO: xSm3+ glasses. The high thermal stability, good glass-forming ability and excellent hardness provide new options for the development of visible orange-reddish lasers and smart photoluminescent glass coating materials.