Particulate Composite Damage: Numerical Estimation of Micro-Crack Propagation Direction

2013 ◽  
Vol 592-593 ◽  
pp. 445-448 ◽  
Author(s):  
Zdeněk Majer ◽  
Petr Marcián ◽  
Luboš Náhlík ◽  
Pavel Hutař ◽  
Zdeněk Knésl
Keyword(s):  
Crack Propagation ◽  
High Performance ◽  
Construction Materials ◽  
Particulate Composite ◽  
Polymer Particle ◽  
Propagation Direction ◽  
Material Behavior ◽  
Rigid Particles ◽  
Crack Propagation Direction ◽  
The Matrix

In recent years, particle reinforced composites are widely used due their mechanical properties as construction materials, high-performance engineering materials or protective organic coatings. The paper was mainly focused on the estimating of the interactions of the micro-crack and the particles in the particulate polymer composites. A non-linear material behavior of the matrix was obtained from the experiment and it was used to investigation by means of the finite element method - using ANSYS software. A two-dimensional numerical model was developed and a micro-crack propagation direction was calculated based on the assumption of the linear elastic fracture mechanics. The results indicated that the presence of the interphase between particle and matrix can improve the fracture toughness of the polymer particle composites through debonding process. The paper can contribute to a better understanding of the behavior and failure of the composites with the polymer matrix reinforced by the rigid particles.

Micro-Crack Propagation in Particulate Composite with Different Types of Matrix

2012 ◽  
Vol 245 ◽  
pp. 138-143 ◽  
Author(s):  
Zdeněk Majer ◽  
Luboš Náhlík
Keyword(s):  
Polymer Matrix ◽  
High Performance ◽  
Construction Materials ◽  
Particulate Composite ◽  
Polymer Particle ◽  
Material Behavior ◽  
Particulate Composites ◽  
Mineral Filler ◽  
Non Linear ◽  
The Matrix

Particulate composites with polymer matrix and solid fillers are one of important types of materials. Generally, these materials are usually used as construction materials, high-performance engineering materials or protective organic coatings. The main aim of a present paper is an estimation of the micro-crack behavior in the particulate composite with non-linear polymer matrix. The polymer matrix filled by magnesia-based mineral filler is investigated by means of the finite element method. A non-linear material behavior of the matrix was obtained from experiment as well as properties of mineral filler. Numerical model on the base of representative plane element (RPE) was developed. The results show that the presence of interphase between particle and matrix can improve fracture toughness of polymer particle composite through debonding process. The conclusions of this paper can contribute to a better understanding of the behavior of micro-crack in particulate composites with respect to interphase.

Automatic 3-D Crack Propagation Calculations in Industrial Components: A Pure Hexahedral versus a Combined Hexahedral-Tetrahedral Approach

2007 ◽  
Vol 348-349 ◽  
pp. 45-48
Author(s):  
Guido Dhondt
Keyword(s):  
Crack Propagation ◽  
Computing Time ◽  
Propagation Direction ◽  
Hexahedral Elements ◽  
Crack Propagation Direction ◽  
Low Weight ◽  
Out Of Plane ◽  
Hexahedral Meshes ◽  
Crack Faces

In recent years, increased loading and low weight requirements have led to the need for automatic crack tracing software. At MTU a purely hexahedral code has been developed in the nineties for Mode-I applications. It has been used extensively for all kinds of components and has proven to be very flexible and reliable. Nevertheless, in transition regions between complex components curved cracks have been observed, necessitating the development of mixed-mode software. Due to the curvature of the crack faces, purely hexahedral meshes are not feasible, and therefore a mixture of hexahedral elements at the crack tip, combined with tetrahedral in the remaining structure has been selected. The intention of the present paper is to compare both methods and to point out the strength and weaknesses of each regarding accuracy, complexity, flexibility and computing time. Furthermore, difficulties arising from the out-of-plane growth of the crack such as the determination of the crack propagation direction are discussed.

Experimental Study and Finite Element Simulation of Heat Build-Up in Rubber Compounds with Application to Fracture

2003 ◽  
Vol 76 (2) ◽  
pp. 386-405 ◽  
Author(s):  
Vladamir Kerchman ◽  
Cheng Shaw
Keyword(s):  
Finite Element ◽  
Crack Propagation ◽  
Numerical Models ◽  
Propagation Direction ◽  
Transient Temperature ◽  
Ir Thermography ◽  
Crack Propagation Direction ◽  
Measure Surface Temperature ◽  
Rubber Compounds ◽  
Heat Build Up

Abstract IR thermography was used to measure surface temperature profiles of cylindrical rubber specimens during cyclic compression. A linearized constitutive approach and finite element analysis were used to evaluate heat generation and associated transient temperature fields. Modeled temperatures compared well with the IR measurements. This led to extended simulation efforts on lab fracture samples. IR thermography was used to measure temperature of filled NR and filled SBR specimens during tensile fatigue cut growth tests. Temperature gradients are expected to relate to kinetics of rubber fracture and identify regions within the sample that are undergoing accelerated damage. The following cut growth issues were addressed: 1) crack propagation direction in a non-uniform stress field; 2) crack propagation direction as a function of the angle of initial cuts; 3) initiation of crack branching; and 4) catastrophic failure. The nonlinear coupled mechanical and thermal FEA was used to evaluate the energy dissipation in the non-homogeneous cyclic deformation of cracked samples. Modeled and measured surface temperatures are in good agreement. Accounting for heat build-up ahead of an advancing crack can improve numerical models that quantify fatigue cut growth behavior in rubber compounds.

Crack Propagation Analysis Procedure Using FEM Applied to the Three-Dimensional Stress Field

2005 ◽  
Author(s):  
Yukihiko Okuda ◽  
Yuuji Saito ◽  
Masayuki Asano ◽  
Masakazu Jimbo ◽  
Hiroshi Hirayama ◽  
...  
Keyword(s):  
Stress Field ◽  
Crack Propagation ◽  
Three Dimensional ◽  
Tensile Load ◽  
Analysis Procedure ◽  
Propagation Direction ◽  
Crack Shape ◽  
Weld Joints ◽  
Crack Propagation Direction ◽  
Propagation Analysis

Recently, several cracks have been found on the weld joints of Boiling Water Reactor (BWR) core shrouds during inspection. In order to ensure the continuous operation of nuclear power plants, it is necessary to assess the structural integrity of core shrouds with cracks on the weld joints. In general, a crack propagates in a complicated manner according to three-dimensional stress field and it is difficult to predict crack propagation direction and crack shape change. Usually, half ellipsoid crack shape is assumed and the propagation of the crack is calculated in the constant direction for assessment. In this study, crack propagation analysis procedure using the Finite Element Method (FEM) is developed for general shaped crack, and the procedure is verified by experiments. In this procedure, it is assumed that the crack propagates according to the maximum J-integral under three-dimensional stress fields and the re-mesh technique is used in the FEM analysis in order to calculate crack shape variation during propagation. The fatigue crack propagation tests under cyclic tensile load were performed to verify the analysis procedure. The specimens are made of a plate from 316SS and designed to generate non-uniform stress distribution on the crack front in order to observe continuous crack propagation direction change.

Study of Mode I-II Mixed Crack Propagation in Electrofusion Joint of Polyethylene Pipe

2018 ◽  
Author(s):  
Yue Zhang ◽  
Jianfeng Shi ◽  
Jinyang Zheng
Keyword(s):  
Finite Element ◽  
Crack Propagation ◽  
Strain Distribution ◽  
Axial Stress ◽  
Propagation Direction ◽  
Image Correlation ◽  
J Integral ◽  
Full Field ◽  
Crack Propagation Direction ◽  
Finite Element Numerical Simulation

Electrofusion joint plays an important role in connecting polyethylene (PE) pipe. In our previous study, penetrating crack failure through the fitting with an angle of about 70° was observed, and axial stress was found to be an important factor in the crack propagation. In this paper, experiments were carried out to study the crack propagation phenomena of the electrofusion joint of PE pipe. Digital Image Correlation (DIC) method was used to measure the displacement on specimen’s surface, as well as full-field strain distribution, based on which the J-integral of the crack tip was calculated. Besides, a finite element numerical simulation was conducted, and its accuracy was verified by experimental J-integral value. Through combination of experimental observations and finite element method, the phenomenon that the angle between crack propagation direction and tube axial is about 70° is detailed analysed. By comparison and analysis of the testing results, critical J-integral value during crack propagation is determined. Furthermore, critical J-integral value of crack propagation in electrofusion joint is predicted.

Sign in / Sign up

Export Citation Format

Share Document