AbstractA set of GaN/InGaN multiple quantum wells (QWs) with well thickness 30 Å and barrier thickness 60 Å were grown by MOCVD on sapphire substrates. The n-type Si doping of the InGaN QWs was varied, in order to produce a different electron concentration in the QWs for the different samples. Optical spectra were obtained by time resolved photoluminescence spectroscopy. The data show weak excitonic spectra from the QWs as well as a broad deeper emission with a much stronger intensity. The spectral shape becomes narrower and the energy position shifts to higher energies with increasing doping. The two different emissions are not easily separated in CW or time integrated spectra, but are clearly observed in a time resolved spectral measurement due to their different recombination rates. The deeper emission has a long and non-exponential decay, with an average decay time in the order of several hundred nanoseconds. The higher energy exciton emission has a much faster decay of about 1 ns. The lower energy band is tentatively explained as due to separately localized electron-hole (e-h) pairs in the QW.
Time-Resolved Photoluminescence Measurement of Frenkel-type Excitonic Lifetimes in InGaN/GaN Multi-quantum Well Structures