Liquid Metal Embrittlement of Resistance Spot Welded 1180TRIP Steel - Effects of Crack Geometry on Weld Mechanical Performance

2017 ◽  
Author(s):  
D. Choi ◽  
S. Uhm ◽  
C. Enloe ◽  
H. Lee ◽  
G. Kim ◽  
...  
Keyword(s):  
Liquid Metal ◽  
Mechanical Performance ◽  
Liquid Metal Embrittlement ◽  
Resistance Spot ◽  
Crack Geometry ◽  
Spot Welded

scholarly journals Microstructure and Mechanical Performance of Resistance Spot Welded Martensitic Advanced High Strength Steel

Processes ◽  
2021 ◽  
Vol 9 (6) ◽  
pp. 1021
Author(s):  
Yunzhao Li ◽  
Huaping Tang ◽  
Ruilin Lai
Keyword(s):  
Mechanical Properties ◽  
Failure Modes ◽  
Mechanical Performance ◽  
Strong Dependence ◽  
High Strength ◽  
Weld Nugget ◽  
Resistance Spot ◽  
Pull Out ◽  
Cross Tension ◽  
Spot Welded

Resistance spot welded 1.2 mm (t)-thick 1400 MPa martensitic steel (MS1400) samples are fabricated and their microstructure, mechanical properties are investigated thoroughly. The mechanical performance and failure modes exhibit a strong dependence on weld-nugget size. The pull-out failure mode for MS1400 steel resistance spot welds does not follow the conventional weld-nugget size recommendation criteria of 4t0.5. Significant softening was observed due to dual phase microstructure of ferrite and martensite in the inter-critical heat affected zone (HAZ) and tempered martensite (TM) structure in sub-critical HAZ. However, the upper-critical HAZ exhibits obvious higher hardness than the nugget zone (NZ). In addition, the mechanical properties show that the cross-tension strength (CTS) is about one quarter of the tension-shear strength (TSS) of MS1400 weld joints, whilst the absorbed energy of cross-tension and tension-shear are almost identical.