Scanning electron microscopy (SEM) of polymers at routine operating voltages of 15 to 25 keV can lead to beam damage and sample image distortion due to charging. Imaging polymer samples with low accelerating voltages (0.1 to 2.0 keV), at or near the “crossover point”, can reduce beam damage, eliminate charging, and improve contrast of surface detail. However, at low voltage, beam brightness is reduced and image resolution is degraded due to chromatic aberration. A new generation of instruments has improved brightness at low voltages, but a typical SEM with a tungsten hairpin filament will have a resolution limit of about 100nm at 1keV. Recently, a new field emission gun (FEG) SEM, the Hitachi S900, was introduced with a reported resolution of 0.8nm at 30keV and 5nm at 1keV. In this research we are reporting the results of imaging coated and uncoated polymer samples at accelerating voltages between 1keV and 30keV in a tungsten hairpin SEM and in the Hitachi S900 FEG SEM.