scholarly journals Microstructures and Hardness of the Experimental 57Fe15Cr25Ni Steel Around TIG Weld-Joints for Reactor Structure Materials

2018 ◽  
Vol 22 (2) ◽  
pp. 66
Author(s):  
Iing Farihin (Parikin) Yunasz (Parikin)
Keyword(s):  
Weld Joints ◽  
Reactor Structure

Effects of bottom plate in friction stir welding of AA6061-T6

2020 ◽  
Vol 118 (1) ◽  
pp. 108
Author(s):  
M.A. Vinayagamoorthi ◽  
M. Prince ◽  
S. Balasubramanian
Keyword(s):  
Mechanical Properties ◽  
Axial Load ◽  
Weld Zone ◽  
Welding Process ◽  
Bottom Plate ◽  
Welding Parameters ◽  
Nugget Zone ◽  
Friction Stir ◽  
Weld Joints ◽  
Fine Grain

The effects of 40 mm width bottom plates on the microstructural modifications and the mechanical properties of a 6 mm thick FSW AA6061-T6 joint have been investigated. The bottom plates are placed partially at the weld zone to absorb and dissipate heat during the welding process. An axial load of 5 to 7 kN, a rotational speed of 500 rpm, and a welding speed of 50 mm/min are employed as welding parameters. The size of the nugget zone (NZ) and heat-affected zone (HAZ) in the weld joints obtained from AISI 1040 steel bottom plate is more significant than that of weld joints obtained using copper bottom plate due to lower thermal conductivity of steel. Also, the weld joints obtained using copper bottom plate have fine grain microstructure due to the dynamic recrystallization. The friction stir welded joints obtained with copper bottom plate have exhibited higher ductility of 8.9% and higher tensile strength of 172 MPa as compared to the joints obtained using a steel bottom plate.

Specific aspects of the quality control for weldolet weld joints

2018 ◽  
Vol 8 (4) ◽  
pp. 420-425
Author(s):  
Nikolay G. Goncharov ◽  
◽  
Igor I. Mikhailov ◽  
Alexey A. Yushin ◽  
◽  
...  
Keyword(s):  
Quality Control ◽  
Weld Joints

Residual Stress Evaluation In Austenitic Stainless Steel Butt Weld Joints By Ultrasonic Technique

1992 ◽  
Vol 25 (3) ◽  
pp. 130 ◽  
Author(s):  
P. Palanichamy ◽  
A. Joseph ◽  
K. V. Kasiviswanathan ◽  
D. K. Bhattacharya ◽  
Baldev Raj
Keyword(s):  
Residual Stress ◽  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Ultrasonic Technique ◽  
Butt Weld ◽  
Stress Evaluation ◽  
Weld Joints

Experimental investigation on resistance spot welding of dissimilar weld joints

2020 ◽  
pp. 095440892096835
Author(s):  
Rohit Verma ◽  
Kanwer Singh Arora ◽  
Lochan Sharma ◽  
Rahul Chhibber
Keyword(s):  
Welding Process ◽  
High Strength ◽  
Dynamic Resistance ◽  
Interstitial Free ◽  
Resistance Spot ◽  
Dissimilar Weld ◽  
Steel Sheets ◽  
Weld Joints ◽  
Resistance Spot Weld ◽  
Weld Current

In the present study, galvanized High Strength Interstitial Free (HIF) steel sheets, and Dual Phase (DP780) steel sheets were used for the investigations. Resistance spot weld joints were fabricated between dissimilar steel sheets. The variation in dynamic resistance (DR) with the change in welding process parameters such as weld current, weld time and electrode force were used for establishing the range of adequate weld nugget formation parameters. Effect of these parameters over tensile strength, nugget diameter and the observed failure mode was studied using one factor at a time (OFAT) approach. Microstructure and hardness of parent metal, fusion & HAZ region has also been studied.