Abutment and Orthodontics for Endurance of Dental Crowns

The split-increment horizontal placement (SHP) is the popular technique being used, along with other therapeutic modus operandi. As more than adequate, SHP methods are being enhanced in barricade cavities for reducing the shrinkage stress that were generated during light polymerization. Such stress, if released unrestrained, may redress within the composite, tooth or at the adhesive contact .

A Comparative Study of the Mechanical Properties of Selected Dental Composites with a Dual-Curing System with Light-Curing Composites

Dual-curing composites have a wide spectrum of use in practice (rebuilding, reconstruction, and luting). The characterization of this type of material and comparative study of selected mechanical properties with light-cured materials were carried out for this paper. In this study, we used six materials with a dual-cure system—Bulk EZ, Fill-Up!, StarFill 2B, Rebilda DC, MultiCore Flow, Activa Bioactive-Restorative—and three light-cured materials—Filtek Bulk Fill Posterior, Charisma Classic, and G-aenial Universal Flo. The materials were conditioned for 24 h in water at 37 °C before testing. Selected material properties were determined: three-point bending flexural strength, diametral tensile strength, hardness, microhardness, and shrinkage stress. The highest three-point bending flexural strength (TPB) was 137.0 MPa (G-aenial Universal Flo), while the lowest amounted to 86.5 MPa (Activa Bioactive). The diametral tensile strength (DTS) values were in a range from 39.2 MPa (Rebilda DC) to 54.1 MPa (Charisma Classic). The lowest hardness (HV) value of 26 was obtained by the Activa Bioactive material, while the highest values were recorded for Filtek Bulk Fill Posterior and Charisma Classic-53. The shrinkage stress of the tested materials ranged from 6.3 MPa (Charisma Classic) to 13.2 MPa (G-aenial Universal Flo). Dual-curing composites were found to have similar properties to light-cured composites.

Polymerization Shrinkage of Short Fiber Reinforced Dental Composite Using a Confocal Laser Analysis

The purpose of this study was to investigate the polymerization shrinkage of short fiber reinforced composite (SFRC) using a multicolor confocal displacement laser that can measure the polymerization shrinkage with high accuracy. The three types of SFRCs used in this study were XD (Ever X Flow Dentin), XB (Ever X Flow Bulk), and XP (EverX Posterior). In addition, CF (Clearfil majesty ES Flow) with hybrid type filler was used as a control. The measured values of the final polymerization shrinkage rate and amount of polymerization shrinkage rate when the polymerization shrinkage rate became constant (less than 0.1 µm/s) were approximated for all SFRCs. XP had a large aspect ratio of glass fiber filler and showed a significant difference from XD with a small aspect ratio (p < 0.05). There was no significant difference in the measured value of time when the polymerization contraction reached a constant speed (0.1 µm/s or less) for all SFRCs (p > 0.05). There was no significant difference in the measured values of polymerization shrinkage rate after the polymerization shrinkage reached a constant rate for all SFRCs (p > 0.05). These results show that glass fiber with large aspect ratio can alleviate polymerization shrinkage stress. The polymerization behavior of SFRC was found to be dependent on the amount of glass fiber filler, aspect ratio, and orientation.