Structure–Activity Relationships between the State of Silver on Different Supports and their I2 and CH3I Adsorption Properties

In this study, the performances of silver-impregnated adsorbents prepared from different host supports (SBA-15, alumina, ceria, and faujasite Y zeolite) and calcined or not at 500 °C (1 h) were compared for the capture of I2 and CH3I. By keeping the silver content rather similar (about 15–17 wt %) among the sorbents, it was possible to assess the effect of silver dispersion and speciation on the adsorption capacities measured for both adsorbates. In a first part, several characterization techniques (XRD, DRS-UV-Vis, TEM, etc.) were used to probe the state of silver in the calcined and non-calcined materials. It was found that the characteristics of silver species are strongly influenced by the thermal treatment, the presence or absence of exchange sites, and the stability of the supports. Silver agglomeration was enhanced after calcination at 500 °C especially for supports bearing no exchange sites (SBA-15) or no ordered pores (alumina and ceria). Then, the adsorption performances of the studied silver sorbents were discussed in relation with their physicochemical characteristics. After-test characterizations were useful to assess the proportion of silver species that have reacted with CH3I and I2 to yield AgI precipitates. Depending on the adsorbate, different trends were obtained. I2 adsorption/reaction with silver sites was found to be quantitative (I/Ag ≈1), whatever the silver speciation and dispersion on the support. By contrast, a high proportion of cationic silver species was found essential to increase CH3I adsorption (I/Ag about 0.6–0.7 against 0.2–0.3 for Ag agglomerated species).

Functionalized Glutathione on Chitosan-Genipin Cross-Linked Beads Used for the Removal of Trace Metals from Water

Functionalized glutathione on chitosan-genipin cross-linked beads (CS-GG) was synthesized and tested as an adsorbent for the removal of Fe(II) and Cu(II) from aqueous solution. The beads were characterized by several techniques, including Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), CNS elementary analysis, scanning electron microscopy (SEM), and atomic force microscopy (AFM). The effect of several parameters such as the pH, the temperature, and the contact time was tested to optimize the condition for the adsorption reaction. The beads were incubated in aqueous solutions contaminated with different concentrations of Fe(II) and Cu(II) (under the range concentration from 10 to 400 mg·L−1), and the adsorption capacity was evaluated by inductively coupled plasma optical emission spectrometry (ICP-OES). The adsorption equilibrium was reached after 120 min of incubation under optimal pH 5 for Fe(II) and after 180 min under optimal pH 6 for Cu(II). According to the Langmuir isotherm, the maximum adsorption capacities (qmax) for Fe(II) and Cu(II) were 208 mg·g−1 and 217 mg·g−1, respectively. Our results showed that the adsorption efficiency of both metals on CS-GG beads was correlated with the degree of temperature. In addition, the adsorption reaction was spontaneous and endothermic, indicated by the positive values of ΔG0 and ΔH0. Therefore, the present study demonstrated that the new synthesized CS-GG beads had a strong adsorption capacity for Fe(II) and Cu(II) and were efficient to remove these trace metals from aqueous solution.

Sequential ionic layer adsorption reaction formation of LaVO4–TiO2 nanocomposites for photocatalytic water treatment

Lanthanum vanadate (LaVO4) has been deposited onto the surface of P25 TiO2 particles immobilized on glass beads for photocatalytic water treatment.