New Thermal Latent Catalyst Using Titanium and Organic Ligand for Urethane Polymerization

New thermal-latent metal catalyst such as tetrakis (lauorate) titanium (LPTi) was designed and synthesized based on a lauroyl peroxide and titanium. The synthetic method is simple with one step reaction. LPTi structure was confirmed by FT-IR analysis, also nano-sized structure of LPTi confirmed using SEM-EDX. LPTi is thermal-latent metal catalyst including titanium that not only promotes urethane synthesis reaction but also increases the dissociation rate of blocked isocyanate. As a result of quantitative analysis of NCO (%) through back titration, when LPTi was added, NCO (%) increased from 2.34% to 3.24%. LPTi can be used as an excellent catalyst for urethane reaction by reducing the polymerization time by about 30% compared to no catalyst. LPTi can be applied to the electronic polymer synthesis.

Effect of Urethane Crosslinking by Blocked Isocyanates with Pyrazole-Based Blocking Agents on Rheological and Mechanical Performance of Clearcoats

A novel blocked isocyanate crosslinker was synthesized, and its applicability was investigated for the low-temperature curing of automotive clearcoats. Various pyrazole derivatives were prepared as blocking agents in isocyanate crosslinkers, which strongly affect the deblocking and curing properties of the urethane-bonded coating systems. The thermal curing properties of clearcoat samples containing a pyrazole-based blocked isocyanate crosslinker and polyol resin were characterized under two different temperature conditions (120 and 150 °C). The decrease in the amount of hydroxyl groups in the polyol before and after curing was expressed by the change in OH stretching frequency in the Fourier transform infrared (FT-IR) spectra. The real-time rheological storage moduli of the bulk clearcoat mixtures were measured via a rotational rheometer to determine the effect of pyrazole-based blocking agents on the curing dynamics. In addition, a rigid-body pendulum tester (RPT) was employed to investigate the curing behavior in the thin film form. The nano-indentation and the nano-scratch tests were conducted to examine the surface hardness and scratch resistance characteristics of the cured clearcoat films. The results show that a low-temperature curing system of clearcoats can be realized by tuning the curing temperature and reactivity of isocyanate crosslinkers blocked with pyrazole-based substituents.

The Effect of Adhesive Additives on the Properties of Isoprene Rubber

Blocked isocyanate – 2-isocyanate-phenylcarbamidemethylbenzene was synthesized and identified using IR-spectroscopy and elemental analysis researching methods. Research showed that adding 2-isocyanate-phenylcarbamidemethylbenzene in rubber compositions based on cis-isoprene synthetic rubber provides increased thermal stability and increasing adhesion comparing them to Manobond-680c.