Modified Red Mud Catalyst for Volatile Organic Compounds Oxidation

Red mud waste from the aluminium industry was modified by leaching using hydrochloric acid or oxalic acid with additives, followed by precipitation or evaporation. The prepared catalysts were characterized in detail and tested for toluene total oxidation. The samples prepared by precipitation of the leachate by adding a base gave a much better performance in catalytic oxidation than the ones prepared by just evaporating the leachate. These improved performances can be correlated to the enhanced textural and redox properties of the catalysts due to the better dispersion and higher enrichment of Fe oxides at their surface. The best performing catalyst had a light-off temperature of around 310 °C and complete oxidation took place at around 380 °C.

CuAlCe Oxides Issued from Layered Double Hydroxide Precursors for Ethanol and Toluene Total Oxidation

CuAlCe oxides were obtained from hydrotalcite-type precursors by coprecipitation using a M2+/M3+ ratio of 3. The collapse of the layered double hydroxide structure following the thermal treatment leads to the formation of mixed oxides (CuO and CeO2). The catalytic performance of the copper-based catalysts was evaluated in the total oxidation of two Volatile Organic Compounds (VOCs): ethanol and toluene. XRD, SEM Energy-Dispersive X-ray Spectrometry (EDX), H2-temperature programmed reduction (TPR) and XPS were used to characterize the physicochemical properties of the catalysts. A beneficial effect of combining cerium with CuAl-O oxides in terms of redox properties and the abatement of the mentioned VOCs was demonstrated. The sample with the highest content of Ce showed the best catalytic properties, which were mainly related to the improvement of the reducibility of the copper species and their good dispersion on the surface. The presence of a synergetic effect between the copper and cerium elements was also highlighted.

Synthesis of Diatomite-Based Mesoporous Wool-Ball-Like Microspheres and Their Application for Toluene Total Oxidation Reaction

Diatomite (DE) has attracted considerable attention owing to its abundance, low cost, and potential for a wide variety of applications. This work reports the development of mesoporous wool-ball-like (WBL) microspheres from natural DE through a simple hydrothermal treatment. We discovered that the presence of cetyltrimethylammonium bromide is a prerequisite for generating monodispersed WBL microspheres. The mechanism for the transformation of pristine DE into mesoporous microspheres through dissolution–recrystallization was clearly investigated. Interestingly, the microspheres exhibited a specific surface area 25–60 times larger than that of the pristine DE. The application of WBL microsphere DE as an effective support for metallic catalysts in the toluene total oxidation reaction was demonstrated.