MECHANICAL CHARACTERIZATION OF POLYMERIC FILMS BASED ON COPOLYMERS OF STYRENE AND BUTYL ACRYLATE OBTAINED BY HETEROGENEOUS POLYMERIZATION IN SEMICONTINUOUS

The aim of this work was to synthesize copolymers of styrene (St) and butyl acrylate (AB) cross-linked with allyl methacrylate by semicontinuous heterogeneous polymerization in order to study the mechanical properties of the polymeric films prepared from the latexes obtained. Copolymer latexes were stable and nanoparticles with spherical morphology were observed by Transmission Electron Microscopy (TEM). The latexes had final conversions between 92,5 and 97,0%, which were determined by the gravimetric method, and a solids content close to 20%. The nanoparticles of latex had an average diameter of 59,1; 55,1 and 49,0 nm for monomer dosing rates of 0,75; 0,45 and 0,15 g/min, respectively. By means of mechanical characterization of the polymeric films and according to the statistical analysis, it was found that when the monomer dosage rate decreased in the synthesis, the mean particle diameter and molecular weight also decreased, and with it a decrease in its Young's Modulus (MPa).

Novel tetraphenylethylene (TPE)-functionalized nitroxide/alkoxyamine for nitroxide-mediated homogeneous and heterogeneous polymerizations

Tetraphenylethylene (TPE)-functionalized nitroxide/alkoxyamine realized the “in situ observation” of the NMP process for both homogeneous and heterogeneous polymerization systems.

Recent advances in colloidal nanocomposite designviaheterogeneous polymerization techniques

Recent advances in colloidal nanocomposite design by heterogeneous polymerization are reviewed, with a specific focus on encapsulation and particle-based stabilization for specific materials applications.

Self-Stabilized Precipitation Polymerization and Its Application

An effective, value-added use of the large amounts of olefinic compounds produced in the processing of petroleum, aside from ethylene and propylene, has been a long outstanding challenge. Here, we developed a novel heterogeneous polymerization method, beyond emulsion/dispersion/suspension, termed self-stabilized precipitation (2SP) polymerization, which involves the nucleation and growth of nanoparticles (NPs) of a well-defined size without the use of any stabilizers and multifunctional monomers (crosslinker). This technique leads to two revolutionary advances: (1) the generation of functional copolymer particles from single olefinic monomer or complex olefinic mixtures (including C4/C5/C9 fractions) in large quantities, which open a new way to transform huge amount of unused olefinic compounds in C4/C5/C9 fractions into valuable copolymers, and (2) the resultant polymeric NPs possess a self-limiting size and narrow size distribution, therefore being one of the most simple, efficient, and green strategies to produce uniform, size-tunable, and functional polymeric nanoparticles. More importantly, the separation of the NPs from the reaction medium is simple and the supernatant liquid can be reused; hence this new synthetic strategy has great potential for industrial production.