Wooden elements may be subjected to mechanical, environmental or biological alterations during their service life. The most susceptible parts of wood structural members are the exposed surfaces since they are subjected to ageing, weathering and/or decay. Knowledge of the influence of weathering factors and polymer degradation mechanisms is essential for understanding the weathering process of wood. The goal of this study was to investigate the degradation of thin wooden samples exposed to short-term weathering. Tests were performed through the European summer (July), which according to previous research is considered as the most severe period for weathering of wood micro-sections. Fourier transform near infrared spectroscopy was used for evaluation of chemical changes of wood samples. Three approaches for data evaluation are presented in this paper: (1) direct spectral interpretation, (2) a concept for calculation of a weathering index Wind and (3) kinetics of lignin changes in relation to the exposure direction for selected wavelengths. Observation of the effects of weathering will allow better understanding of the degradation process. The southern exposure site was slightly more affected by weathering than other sites. Results of this research will be used for future determination of the weather-dose response model and could be essential for predicting the future performance of timber facade elements.
Weathering Kinetics of Thin Wood Veneers Assessed with near Infrared Spectroscopy