Thermal barrier coatings (TBC-s) have been utilized in gas turbine engines for over two decades, primarily to protect the existing materials under the demands for higher temperatures and greater engine efficiency. Atmospheric Plasma Sprayed TBC, commonly used for hot combustion chamber components of advanced gas turbines, are exposed to thermo-mechanical loads, which may lead to failure in form of macroscopic spallations from the metallic component. The durability of TBC is limited by the interaction of different processes and parameters, such as bond coat oxidation, cyclic strains, visco-plastic and relaxation properties, interface roughness and others. In this work, the spallation failure mechanisms and damage evolution of APS-TBC system are investigated on samples aged by isothermal and thermal cycle tests using different time and temperatures exposures. Several parameters have been analyzed by SEM and a life prediction model approach for APS-TBC is being developed focusing on oxidation kinetics, identifying the parameters such as rumpling, bond coat oxidation, TGO thickness and interdiffusion of base metal elements which drive the oxide formation and TBC spallation mechanisms.
Damage evolution and failure mechanisms in additively manufactured stainless steel