Abstract
Sheet moulding compound (SMC) is a combination of glass fibers and filled polyester resin. It is processed by a compression moulding process and finds extensive applications in structural, automotive, electrical and electronic industries. The compression moulding process is characterized by the flow behavior of SMC under heat and pressure in the press mould. This paper is focused on the prediction of ideal processibility conditions of SMC. The qualitative aspect of a properly thickened (matured) moulding compound could be seen from its tack-free nature, which was quantitatively calibrated in terms of penetration depth, measured by a specially constructed softness indicator. The weight (wt)% of calcium carbonate (CaCO3) as filler, magnesium oxide (MgO) as thickener, graphite (C) and zinc stearate [Zn (C18H35O2)2] (ZnSt) as lubricants along with the maturation time (Tm) were selected as process variables. Taguchi’s scheme of experimental design was adapted to perform the experiments. It was found that the higher levels of MgO and CaCO3 were favorable for a good penetration depth as well as a reduced maturation time. We have also found that a penetration depth of at least 5 mm was required for achieving good processability conditions of SMC. An optimization study was under taken to find the right blend of additives and fillers, at their minimal weights and in the least possible maturation time, to achieve the desired processability. This study is particularly useful in a production run to make moulded parts from SMC.