High quality unintentionally doped n-type GaN layers were grown on Si (111) substrate using AlN (about 200 nm) as buffer layer by radio frequency (RF) nitrogen plasma-assisted molecular beam epitaxy (MBE). This paper presents the structural and optical studies of porous GaN sample compared to the corresponding as-grown GaN. Metal–semiconductor–metal (MSM) photodiode was fabricated on the samples. For as-grown GaN-based MSM, the detector shows a sharp cut-off wavelength at 362 nm, with a maximum responsivity of 0.254 A/W achieved at 360 nm. For porous GaN MSM detector, a sharp cut-off wavelength at 360 nm with a maximum responsivity of 0.655 A/W was achieved at 359 nm. Both the detectors show a little decrease in responsivity in the UV spectral region. The MSM photodiode based on porous GaN shows enhanced (2×) magnitude of responsivity relative to the as-grown GaN MSM photodiode. Enhancement of responsivity can be attributed to the relaxation of tensile stress and reduction of surface pit density in the porous sample.
High responsivity in molecular beam epitaxy grown β-Ga2O3 metal semiconductor metal solar blind deep-UV photodetector