Influence of Temperature of Accumulative Roll Bonding on the Microstructure and Mechanical Properties of AA5251 Aluminum Alloy

2014 ◽  
Vol 59 (1) ◽  
pp. 127-131 ◽  
Author(s):  
J. Bogucka
Keyword(s):  
Mechanical Properties ◽  
Ambient Temperature ◽  
Accumulative Roll Bonding ◽  
Bonding Temperature ◽  
Tensile Tests ◽  
Structure Evolution ◽  
X Ray Diffraction ◽  
Roll Bonding ◽  
X Ray ◽  
Microstructure And Mechanical Properties

Abstract The influence of bonding temperature on microstructure and mechanical properties of AA5251 alloy sheets have been analyzed in the paper. The alloy was deformed with the method of accumulative roll bonding (ARB) in various temperature conditions i.e. at ambient temperature up to 5th cycle (ε = 4.0) and using pre-heating of sheet packs at 200°C and 300°C up to 10 cycles (ε = 8.0). The deformed material was subjected to structural observations using TEM, measurements of crystallographic texture with the technique of X-ray diffraction and tensile tests. It was established that the temperature of roll-bonding had a significant effect on the structure evolution and the observed changes of mechanical properties. High refinement of microstructure and optimum mechanical properties were obtained for the material processed at lower temperatures, i.e. at ambient temperature and pre-heating at 200°C. Recovery structure processes occurring during deformation were observed in the alloy bonded with pre-heating at 300°C and therefore mechanical properties were lower than for the alloy bonded at lower temperatures.

Research on the Microstructure and Mechanical Properties of Spray-Deposited 8009 Heat Resistant Aluminum Alloy

2014 ◽  
Vol 543-547 ◽  
pp. 3733-3736
Author(s):  
Rong Hua Zhang ◽  
Biao Wu ◽  
Xiao Ping Zheng
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Tensile Tests ◽  
Test Results ◽  
Secondary Phases ◽  
X Ray Diffraction ◽  
X Ray ◽  
Heat Resistant ◽  
Microstructure And Mechanical Properties ◽  
Transmission Electron

In this study, 8009 heat resistant aluminum alloy was synthesized by the spray atomization and deposition technique. The microstructure and mechanical properties of the alloy were studied using transmission electron microscopy, X-ray diffraction, and tensile tests. The secondary phases in the microstructure of the spray-deposited alloy were examined. The tensile test results indicate that the spray-deposited 8009 alloy both at room and elevated temperature displays superior tensile strength due to the presence of the thermally stable Al12(Fe,V)3Si particles.

Microstructure and Mechanical Properties of an Al-Cu-Mg-Fe-Ni Alloy

2014 ◽  
Vol 988 ◽  
pp. 156-160
Author(s):  
Hong Wei Liu ◽  
Feng Wang ◽  
Bai Qing Xiong ◽  
Yong An Zhang ◽  
Zhi Hui Li ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Cast Alloy ◽  
Tensile Tests ◽  
Eutectic Structure ◽  
Test Results ◽  
X Ray Diffraction ◽  
X Ray ◽  
Microstructure And Mechanical Properties ◽  
Ni Alloy ◽  
Scanning Electron

The microstructure and mechanical properties of the Al-2.24Cu-1.42Mg-0.9Fe-0.9Ni alloy were studied using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and tensile tests. The results indicate that the microstructures of the as cast alloy involve α-Al matrix, Al/Al2CuMg eutectic structure, Al7Cu2Fe, Al7Cu4Ni and Al9FeNi compounds. The tensile test results indicate that the alloy at elevated temperature (200°C) displays superior tensile strength due to the presence of the thermally stable Al7Cu2Fe, Al7Cu4Ni and Al9FeNi compounds.

Microstructure and Mechanical Properties of Spray-Deposited Zn-30Al-1Cu Alloy

2012 ◽  
Vol 706-709 ◽  
pp. 264-267
Author(s):  
Feng Wang ◽  
Bai Qing Xiong ◽  
Yon Gan Zhang ◽  
Hong Wei Liu ◽  
Zhi Hui Li ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Tensile Tests ◽  
Chinese Script ◽  
Spray Atomization ◽  
Test Results ◽  
X Ray Diffraction ◽  
X Ray ◽  
Microstructure And Mechanical Properties ◽  
Transmission Electron

In this study, Zn-30Al-1Cu alloy was synthesized by the spray atomization and deposition technique. The microstructure and mechanical properties of the alloy were studied using optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and tensile tests. It can be seen that the microstructure of spray-deposited Zn-30Al-1Cu alloy is composed of the Zn/Al eutectoids and few compounds. The Zn/Al eutectoids were shown lamellar, particle and Chinese script morphologies. The compound phases in the microstructure of the spray-deposited alloy were examined. The property test results indicate that the spray-deposited Zn-30Al-1Cu alloy displays superior tensile strength.

Microstructure and Mechanical Properties of VTaTiMoAlx Refractory High Entropy Alloys

2017 ◽  
Vol 898 ◽  
pp. 638-642 ◽  
Author(s):  
Dong Xu Qiao ◽  
Hui Jiang ◽  
Xiao Xue Chang ◽  
Yi Ping Lu ◽  
Ting Ju Li
Keyword(s):  
Mechanical Properties ◽  
Vacuum Arc ◽  
High Entropy Alloys ◽  
X Ray Diffraction ◽  
Dendrite Structure ◽  
X Ray ◽  
High Entropy ◽  
Arc Melting ◽  
Vacuum Arc Melting ◽  
Microstructure And Mechanical Properties

A series of refractory high-entropy alloys VTaTiMoAlx with x=0,0.2,0.6,1.0 were designed and produced by vacuum arc melting. The effect of added Al elements on the microstructure and mechanical properties of refractory high-entropy alloys were investigated. The X-ray diffraction results showed that all the high-entropy alloys consist of simple BCC solid solution. SEM indicated that the microstructure of VTaTiMoAlx changes from equiaxial dendritic-like structure to typical dendrite structure with the addition of Al element. The composition of different regions in the alloys are obtained by energy dispersive spectroscopy and shows that Ta, Mo elements are enriched in the dendrite areas, and Al, Ti, V are enriched in inter-dendrite areas. The yield strength and compress strain reach maximum (σ0.2=1221MPa, ε=9.91%) at x=0, and decrease with the addition of Al element at room temperature. Vickers hardness of the alloys improves as the Al addition.

Sign in / Sign up

Export Citation Format

Share Document