Residual Stress Measurements in Extreme Environments for Hazardous, Layered Specimens

Background In nuclear fuel plates of low-enriched U-10Mo (LEU) clad with aluminum by hot isostatic pressing (HIP), post-irradiation stresses arising during reactor shutdown are a major concern for safe reactor operations. Measurement of those residual stresses has not previously been possible because the high radioactivity of the plates requires handling only by remote manipulation in a hot cell. Objective The incremental slitting method for measuring through-thickness stress profiles was modified, and a system for automated, remote operation was built and tested. Methods Experimental modifications consisted of replacing electric-discharge machining (EDM) with a small end mill and strain-gauge measurements with cantilever displacement measurements. The inverse method used to calculate stresses was the pulse-regularization method modified to allow discontinuities across material interfaces. The new system was validated by comparing with conventional slitting on a depleted U-10Mo (DU) fuel plate. Results The new system was applied to two measurements each on six as-fabricated (pre-irradiation) LEU miniature fuel plates. Variations between the measurements at two locations in the same plate were strongly correlated with measured geometrical heterogeneity in the plate—a tilt in the fuel foil. Compressive stresses in the U-10Mo were shown to increase from 20 to 250 MPa as the ratio of aluminum thickness to U-10Mo thickness increased causing increased constraint during cooling. Faster cooling rates during processing also increased stress magnitudes. Conclusions The measurements trends agreed with data in the literature from similar plates made with DU, which further validates the method. Because other methods are impractical in a hot cell, the modified slitting method is now poised for the first measurements of post-irradiation stresses.

Effect of Hot Isostatic Pressing on Microstructures and Stress-Rupture Properties of CM 939 Weldable Alloy

Effect of hot isostatic pressing (HIP) treatment on the microstructure and the stress rupture properties of CM 939 Weldable alloy have been investigated. The results shown that the HIP has the function of densification and homogenization, all of the microporosity have been almost removed, the segregation of the alloy have been reduced, the microstructure became better, the stress rupture life of CM 939 Weldable alloy have been obviously improved, Meanwhile, the data dispersion of stress rupture properties have been reduced for the alloy after HIP.

Evolution of Microstructure and Elements Distribution of Powder Metallurgy Borated Stainless Steel during Hot Isostatic Pressing

prepared by powder metallurgy process incorporating atomization and hot isostatic pressing (HIP) sintering at six different temperatures from 600 to 1160 °C, borated stainless steel (BSS) containing boron content of 1.86 wt% was studied. The phase of BSS, relative density of different temperature, microstructure, elemental distribution, and mechanical properties were tested and analyzed. The phases of the alloy were calculated by the Thermo-Calc (2021a, Thermo-Calc Software, Solna, Sweden) and studied by quantitative X-ray diffraction phase analysis. The distributions of boron, chromium, and iron in grains of the alloy were analyzed by scanning electron microscopy and transmission electron microscope. The grain size distributions and average grain sizes were calculated for the boron-containing phases at 900, 1000, 1100, and 1160 °C, as well as the average grain size of the austenite phase at 700 and 1160 °C. After undergoing HIP sintering at 900, 1000, 1100, and 1160 °C, respectively, the tensile strength and ductility of the alloy were tested, and the fracture surfaces were analyzed. It was found that the alloy consisted of two phases (austenite and boron-containing phase) when HIP sintering temperature was higher than 900 °C, and the relative density of the prepared alloys was higher than 99% when HIP temperature was higher than 1000 °C. According to the boron-containing phase grain size distribution and microstructure analysis, the boron-containing phase precipitated both inside the austenite matrix and at the grain boundaries and its growth mechanism was divided into four steps. The tensile strength and elongation of alloy were up to 776 MPa and 19% respectively when the HIP sintering was at 1000 °C.