scholarly journals Effect of Austempering below and above Ms on the Microstructure and Wear Performance of a Low-Carbon Bainitic Steel

Metals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 104
Author(s):  
Zhirui Wei ◽  
Haijiang Hu ◽  
Man Liu ◽  
Junyu Tian ◽  
Guang Xu
Keyword(s):  
Impact Toughness ◽  
Low Carbon Steel ◽  
Total Elongation ◽  
Bainitic Steel ◽  
Low Carbon ◽  
Bainite Transformation ◽  
Wear Performance ◽  
Isothermal Temperature ◽  
Considerable Impact ◽  
Fresh Martensite

The microstructure and wear performance of a low-carbon steel treated by austempering below and above martensite start temperature (Ms) were investigated. The results show that the bainite, fresh martensite (FM) and retained austenite (RA) were observed in samples austempered above Ms. Except for the three above phases, the athermal martensite (AM) was also observed in samples austempered below Ms. The bainite transformation was accelerated and finer bainite was obtained due to the AM formation in samples austempered below Ms. In addition, the strength and hardness were improved with the decrease of the isothermal temperature and time, whereas the total elongation decreased with the increasing isothermal time and the decreasing isothermal temperature. Moreover, the materials austempered below Ms exhibited better wear performance than the ones treated above Ms, which is attributed to the improved impact toughness by the finer bainite and the enhanced hardness by AM. The best wear resistance was obtained in the samples austempered at 300 °C below Ms for 200 s, due to the highest hardness and considerable impact toughness.

Microstructure and Mechanical Properties of a Low-Carbon Steel Treated by One-Step Quenching and Partitioning Process

2014 ◽  
Vol 1082 ◽  
pp. 202-207 ◽  
Author(s):  
Shu Yan ◽  
Xiang Hua Liu
Keyword(s):  
Mechanical Properties ◽  
Carbon Steel ◽  
Microstructural Evolution ◽  
Retained Austenite ◽  
Uniform Elongation ◽  
Low Carbon Steel ◽  
Total Elongation ◽  
Low Carbon ◽  
Quenching And Partitioning ◽  
Partitioning Time

A low carbon steel was treated by quenching and partitioning (Q&P) process, and a detailed characterization of the microstructural evolution and testing of mechanical properties were carried out. The resulted mechanical properties indicate that with the partitioning time increasing, the tensile strength decreases rapidly first and then remains stable, and the total elongation increases first then decreases. The investigated steel subjected to Q&P process exhibits excellent products of strength and elongation (17.8-20.6 GPa•%). The microstructural evolution of martensite matrix during the partitioning step was observed, and the morphology and content of retained austenite were characterized. The working hardening behavior of the samples was analyzed, and the retained austenite with higher carbon content contributes to the uniform elongation more effectively.

Effects of Al, Si and N Content on the Formation of M-A Constituent and HAZ Toughness of Ti-Containing Low-Carbon Steel

2021 ◽  
Vol 1016 ◽  
pp. 42-49
Author(s):  
Kook Soo Bang ◽  
Joo Hyeon Cha ◽  
Kyu Tae Han ◽  
Hong Chul Jeong
Keyword(s):  
Carbon Steel ◽  
Impact Toughness ◽  
Low Carbon Steel ◽  
Charpy Impact ◽  
Coarse Grained ◽  
Low Carbon ◽  
N Content ◽  
Si Content ◽  
The Impact ◽  
Haz Toughness

The present work investigated the effects of Al, Si, and N content on the impact toughness of the coarse-grained heat-affected zone (CGHAZ) of Ti-containing low-carbon steel. Simulated CGHAZ of differing Al, Si, and N contents were prepared, and Charpy impact toughness was determined. The results were interpreted in terms of microstructure, especially martensite-austenite (M-A) constituent. All elements accelerated ferrite transformation in CGHAZ but at the same time increased the amount of M-A constituent, thereby deteriorating CGHAZ toughness. It is believed that Al, Si, and free N that is uncombined with Ti retard the decomposition of austenite into pearlite and increase the carbon content in the last transforming austenite, thus increasing the amount of M-A constituent. Regardless of the amount of ferrite in CGHAZ, its toughness decreased linearly with an increase of M-A constituent in this experiment, indicating that HAZ toughness is predominantly affected by the presence of M-A constituent. When a comparison of the effectiveness is made between Al and Si, it showed that a decrease in Si content is more effective in reducing M-A constituents.

Effect of Ti, Al and Mg Addition on the Impact Toughness of Heat Affected Zone in Low Carbon Steel

2009 ◽  
Vol 79-82 ◽  
pp. 143-146
Author(s):  
Jiang Hua Ma ◽  
Dong Ping Zhan ◽  
Zhou Hua Jiang ◽  
Ji Cheng He
Keyword(s):  
Carbon Steel ◽  
Impact Toughness ◽  
Heat Affected Zone ◽  
Low Carbon Steel ◽  
Optical Microscope ◽  
Carbon Steels ◽  
Low Carbon ◽  
Welding Simulation ◽  
Mg Addition ◽  
The Impact

In order to understand the effects of deoxidizer such as aluminium, titanium and magnesium on the impact toughness of heat affected zone (HAZ), three low carbon steels deoxidized by Ti-Al, Mg and Ti-Mg were obtained. After smelting, forging, rolling and welding simulation, the effects of Al, Ti and Mg addition on the impact toughness of HAZ in low carbon steel were studied. The inclusion characteristics (size, morphology and chemistry) of samples before welding and the fracture pattern of the specimens after the Charpy-type test were respectively analyzed using optical microscope and scanning electron microscopy (SEM). The following results were found. The density of inclusion in Ti-Mg deoxidized steel is bigger than Ti-Al deoxidized steel. The average diameter is decreased for the former than the latter. The addition of Ti-Mg can enhance the impact toughness of the HAZ after welding simulation. The maximal value of the impact toughness is 66.5J/cm2. The complex particles of MgO-TiOx-SiO2-MnS are most benefit to enhance impact toughness. The improvement of HAZ is attributable to the role of particle pinning and the formation of intergranular ferrite.

scholarly journals Exploring the Difference in Bainite Transformation with Varying the Prior Austenite Grain Size in Low Carbon Steel

Metals ◽  
2018 ◽  
Vol 8 (12) ◽  
pp. 988 ◽  
Author(s):  
Liangyun Lan ◽  
Zhiyuan Chang ◽  
Penghui Fan
Keyword(s):  
Grain Size ◽  
Prior Austenite ◽  
Low Carbon Steel ◽  
Low Carbon ◽  
Bainite Transformation ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Austenite Grains ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

The simulation welding thermal cycle technique was employed to generate different sizes of prior austenite grains. Dilatometry tests, in situ laser scanning confocal microscopy, and transmission electron microscopy were used to investigate the role of prior austenite grain size on bainite transformation in low carbon steel. The bainite start transformation (Bs) temperature was reduced by fine austenite grains (lowered by about 30 °C under the experimental conditions). Through careful microstructural observation, it can be found that, besides the Hall–Petch strengthening effect, the carbon segregation at the fine austenite grain boundaries is probably another factor that decreases the Bs temperature as a result of the increase in interfacial energy of nucleation. At the early stage of the transformation, the bainite laths nucleate near to the grain boundaries and grow in a “side-by-side” mode in fine austenite grains, whereas in coarse austenite grains, the sympathetic nucleation at the broad side of the pre-existing laths causes the distribution of bainitic ferrite packets to be interlocked.

Microstructure and Mechanical Properties of Nb Alloyed Steel Processed by Hot Equal Channel Angular Extrusion

2016 ◽  
Vol 879 ◽  
pp. 2528-2531
Author(s):  
Akira Yanagida ◽  
Ryo Aoki ◽  
Masataka Kobayashi
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Carbon Steel ◽  
Equal Channel Angular Extrusion ◽  
Low Carbon Steel ◽  
Total Elongation ◽  
Low Carbon ◽  
Angular Extrusion ◽  
Ferrite Grain Size

A Nb alloyed low carbon steel was processed by hot equal channel angular extrusion (ECAE) and following transformation. The workpieces were heated up to the 960°C in the furnace for 10 min within the container block. Before extrusion, the die was preheated to 400oC. The workpiece was cooled in the die after ECAE process. 1 pass and 2 pass via route C were conducted at a speed of 32mm/s, the inter-pass time is about 2 sec. The sample of average ferrite grain size of about 2μm, a tensile strength of 800MPa, a total elongation about 20% is produced after 2 pass ECAE processed and subsequent cooling.

Microstructural engineering and strength-impact toughness prediction in ultra-low carbon bainitic steel

2018 ◽  
Vol 34 (15) ◽  
pp. 1910-1918 ◽  
Author(s):  
Md. Basiruddin Sk ◽  
Debalay Chakrabarti ◽  
S. Chatterjee
Keyword(s):  
Impact Toughness ◽  
Bainitic Steel ◽  
Low Carbon

Impact toughness of friction stir processed low carbon steel used in shipbuilding

2016 ◽  
Vol 672 ◽  
pp. 40-48 ◽  
Author(s):  
D.M. Sekban ◽  
S.M. Aktarer ◽  
P. Xue ◽  
Z.Y. Ma ◽  
G. Purcek
Keyword(s):  
Carbon Steel ◽  
Impact Toughness ◽  
Low Carbon Steel ◽  
Low Carbon ◽  
Friction Stir
Sign in / Sign up

Export Citation Format

Share Document