Si, Zn-Modified Tricalcium Phosphates: A Phase Composition and Crystal Structure Study

2005 ◽  
Vol 284-286 ◽  
pp. 83-88 ◽  
Author(s):  
Xiang Wei ◽  
Mufit Akinc
Keyword(s):  
Crystal Structure ◽  
Bone Formation ◽  
Tricalcium Phosphate ◽  
Unit Volume ◽  
Structure Study ◽  
Phase Changes ◽  
Second Phase ◽  
Bone Implant ◽  
Essential Trace Elements ◽  
Tricalcium Phosphates

Tricalcium phosphate modified by silicon and zinc was synthesized as a candidate for resorbable temporal bone implant having a controlled solubility and improved biocompatibility. Since Si and Zn are essential trace elements with stimulatory effects on bone formation, Si,Znmodified tricalcium phosphate can also promote bone formation. From XRD and ICP analyses, it was shown that up to 10 mol% Si and Zn can be incorporated in the tricalcium phosphate lattice without formation of a second phase. Changes in lattice parameters and unit volume of TCP as calculated by Rietveld refinement analysis indicate that Si and Zn substitute for P and Ca respectively.

In Vivo and In Vitro Evaluation of Coated HAp Films with Different Surface Morphology

2007 ◽  
Vol 539-543 ◽  
pp. 710-715
Author(s):  
Kotaro Kuroda ◽  
Ryoichi Ichino ◽  
Masazumi Okido
Keyword(s):  
Bone Formation ◽  
Surface Morphology ◽  
New Bone Formation ◽  
Contact Ratio ◽  
Bone Implant ◽  
Ft Ir ◽  
Mouse Osteoblast ◽  
Surface Morphologies

Hydroxyapatite (HAp) coatings were formed on cp titanium plates and rods by the thermal substrate method in an aqueous solution that included 0.3 mM Ca(H2PO4)2 and 0.7 mM CaCl2. The coating experiments were conducted at 40-140 oC and pH = 8 for 15 or 30 min. The properties for the coated samples were studied using XRD, EDX, FT-IR, and SEM. All the specimens were covered with HAp, which had different surface morphologies such as net-like, plate-like and needle-like. After cleaning and sterilization, all the coated specimens were subjected to in vivo and vitro testing. In the in vitro testing, the mouse osteoblast-like cells (MC3T3-E1) were cultured on the coated and non-coated specimens for up to 30 days. Moreover, the specimens (φ2 x 5 mm) were implanted in rats femoral for up to 8 weeks, the osseoinductivity on them were evaluated. In in vitro evaluations, there were not significant differences between the different surface morphologies. In in vivo evaluations, however, two weeks postimplantation, new bone formed on both the HAp coated and non-coated titanium rods in the cancellous and cortical bone. The bone-implant contact ratio, which was used for the evaluation of new bone formation, was significantly dependent on the surface morphology of the HAp, and the results demonstrated that the needle-like coating appears to promote rapid bone formation.

Biological Response to Wollastonite Doped α-Tricalcium Phosphate Implants in Hard and Soft Tissues in Rats

2008 ◽  
Vol 396-398 ◽  
pp. 7-10 ◽  
Author(s):  
Ana Maria Minarelli Gaspar ◽  
Sybele Saska ◽  
R. García Carrodeguas ◽  
A.H. De Aza ◽  
P. Pena ◽  
...  
Keyword(s):  
Connective Tissue ◽  
Bone Formation ◽  
Bone Tissue ◽  
Tricalcium Phosphate ◽  
Rattus Norvegicus ◽  
Soft Tissues ◽  
Subcutaneous Tissue ◽  
Biological Response ◽  
New Bone Formation ◽  
Rat Bone

The biological response following subcutaneous and bone implantation of β-wollastonite(β-W)-doped α-tricalcium phosphate bioceramics in rats was evaluated. Tested materials were: tricalcium phosphate (TCP), consisting of a mixture of α- and β-polymorphs; TCP doped with 5 wt. % of β-W (TCP5W), composed of α-TCP as only crystalline phase; and TCP doped with 15 wt. % of β-W (TCP15), containing crystalline α-TCP and β-W. Cylinders of 2x1 mm were implanted in tibiae and backs of adult male Rattus norvegicus, Holtzman rats. After 7, 30 and 120 days, animals were sacrificed and the tissue blocks containing the implants were excised, fixed and processed for histological examination. TCP, TCP5W and TCP15W implants were biocompatible but neither bioactive nor biodegradable in rat subcutaneous tissue. They were not osteoinductive in connective tissue either. However, in rat bone tissue β-W-doped α-TCP implants (TCP5W and TCP15W) were bioactive, biodegradable and osteoconductive. The rates of biodegradation and new bone formation observed for TCP5W and TCP15W implants in rat bone tissue were greater than for non-doped TCP.

Effects of dietary alteration of bicarbonate and magnesium on rat bone

1986 ◽  
Vol 250 (2) ◽  
pp. F302-F307 ◽  
Author(s):  
J. M. Burnell ◽  
C. Liu ◽  
A. G. Miller ◽  
E. Teubner
Keyword(s):  
Crystal Structure ◽  
Bone Formation ◽  
X Ray Diffraction ◽  
X Ray ◽  
Growing Rats ◽  
Final Composition ◽  
Rat Bone

To study the effects of bicarbonate and magnesium on bone, mild acidosis and/or hypermagnesemia were produced in growing rats by feeding ammonium chloride and/or magnesium sulfate. Bone composition, quantitative histomorphometry, and mineral x-ray diffraction (XRD) characteristics were measured after 6 wk of treatment. The results demonstrated that both acidosis (decreased HCO3) and hypermagnesemia inhibited periosteal bone formation, and, when combined, results were summative; and the previously observed in vitro role of HCO3- and Mg2+ as inhibitors of crystal growth were confirmed in vivo. XRD measurements demonstrated that decreased plasma HCO3 resulted in larger crystals and increased Mg resulted in smaller crystals. However, the combined XRD effects of acidosis and hypermagnesemia resembled acidosis alone. It is postulated that the final composition and crystal structure of bone are strongly influenced by HCO3- and Mg2+, and the effects are mediated by the combined influence on both osteoblastic bone formation and the growth of hydroxyapatite.

scholarly journals Physical and Histological Comparison of Hydroxyapatite, Carbonate Apatite, and β-Tricalcium Phosphate Bone Substitutes

Materials ◽  
2018 ◽  
Vol 11 (10) ◽  
pp. 1993 ◽  
Author(s):  
Kunio Ishikawa ◽  
Youji Miyamoto ◽  
Akira Tsuchiya ◽  
Koichiro Hayashi ◽  
Kanji Tsuru ◽  
...  
Keyword(s):  
Bone Formation ◽  
Bone Defect ◽  
Tricalcium Phosphate ◽  
Bone Substitutes ◽  
Physiological Solution ◽  
Tissue Response ◽  
Histological Evaluation ◽  
Carbonate Apatite ◽  
Artificial Bone ◽  
New Bone Formation

Three commercially available artificial bone substitutes with different compositions, hydroxyapatite (HAp; Neobone®), carbonate apatite (CO3Ap; Cytrans®), and β-tricalcium phosphate (β-TCP; Cerasorb®), were compared with respect to their physical properties and tissue response to bone, using hybrid dogs. Both Neobone® (HAp) and Cerasorb® (β-TCP) were porous, whereas Cytrans® (CO3Ap) was dense. Crystallite size and specific surface area (SSA) of Neobone® (HAp), Cytrans® (CO3Ap), and Cerasorb® (β-TCP) were 75.4 ± 0.9 nm, 30.8 ± 0.8 nm, and 78.5 ± 7.5 nm, and 0.06 m2/g, 18.2 m2/g, and 1.0 m2/g, respectively. These values are consistent with the fact that both Neobone® (HAp) and Cerasorb® (β-TCP) are sintered ceramics, whereas Cytrans® (CO3Ap) is fabricated in aqueous solution. Dissolution in pH 5.3 solution mimicking Howship’s lacunae was fastest in CO3Ap (Cytrans®), whereas dissolution in pH 7.3 physiological solution was fastest in β-TCP (Cerasorb®). These results indicated that CO3Ap is stable under physiological conditions and is resorbed at Howship’s lacunae. Histological evaluation using hybrid dog mandible bone defect model revealed that new bone was formed from existing bone to the center of the bone defect when reconstructed with CO3Ap (Cytrans®) at week 4. The amount of bone increased at week 12, and resorption of the CO3Ap (Cytrans®) was confirmed. β-TCP (Cerasorb®) showed limited bone formation at week 4. However, a larger amount of bone was observed at week 12. Among these three bone substitutes, CO3Ap (Cytrans®) demonstrated the highest level of new bone formation. These results indicate the possibility that bone substitutes with compositions similar to that of bone may have properties similar to those of bone.

Sign in / Sign up

Export Citation Format

Share Document