The Influence of Processing Parameters on Mechanical Properties of Spark Plasma Sintered Chromium Carbide Based Cermets

2017 ◽  
Vol 267 ◽  
pp. 162-166
Author(s):  
Kristjan Juhani ◽  
Jüri Pirso ◽  
Marek Tarraste ◽  
Mart Viljus ◽  
Sergei Letunovitš
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Liquid Phase ◽  
Chromium Carbide ◽  
Processing Parameters ◽  
Liquid Phase Sintering ◽  
Fine Grained ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Sintered Chromium

Present paper discusses the influence of spark plasma sintering (SPS) on the microstructure and perfomances of chromium carbide based cermets. The effect of SPS parameters (temperature, pressure) is discussed. It is shown that SPS enables to produce more fine grained chromium carbide based cermets compared to conventional liquid phase sintering. Hardness and fracture toughness are exhibited.

scholarly journals Mechanical Properties of WC-Si3N4 Composites With Ultrafine Porous Boron Nitride Nanofiber Additive

2021 ◽  
Vol 8 ◽  
Author(s):  
Ting Cao ◽  
Xiaoqiang Li ◽  
Jingmao Li ◽  
Yang Huang ◽  
Shengguan Qu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Liquid Phase ◽  
Boron Nitride ◽  
Probable Mechanism ◽  
Sintering Process ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Catastrophic Fracture ◽  
First Time

WC-10 wt.% Si3N4 composites toughened with ultrafine porous boron nitride nanofiber (0, 0.01, 0.05, 0.1, and 0.15 wt.%) were prepared for the first time by spark plasma sintering. Compared with the WC-Si3N4 composite sintered in the same condition, the obtained WC-10 wt.% Si3N4 composites with ultrafine porous boron nitride were found to possess better hardness and fracture toughness. In addition, the Si3N4 phase in the UPBNNF toughened composites did not exhibit traditional catastrophic fracture as indicated in most investigations. In this study, the phenomena are discussed, and a probable mechanism is elucidated. It is deduced that the approach could be extended to materials with a feature of internal liquid phase during the sintering process and could improve hardness and fracture toughness.

Effects of Powder Microscopic Defects on Densification and Mechanical Properties of WC via Spark Plasma Sintering

2021 ◽  
Vol 1016 ◽  
pp. 1770-1777
Author(s):  
Liu Zhu ◽  
Jin Fang Wang ◽  
Zhi Biao Tu ◽  
Na Xue ◽  
Wei Wei Li
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Free Energy ◽  
Composite Powder ◽  
Sintering Temperature ◽  
Chemical Activation ◽  
Activation Technique ◽  
Specific Chemical ◽  
Plasma Sintering ◽  
Spark Plasma

The WC composite powder was synthesized by a new specific chemical activation technique. A large number of lattice defects such as surface humps, dislocations and stacking fault exist in the surface of the WC powder after chemical activation technique. By using such activated WC powder, the binderless WC cemented carbide with high density (15.54 g/cm3), super hardness (average 26.29 GPa) and excellent fracture toughness (8.9 MPa.m1/2) can be fabricated by SPS at 1700 °C and 50 MPa pressure. The improvement in density, hardness and fracture toughness are respectively 4.5%, 15.3% and 17.1% compared to when using the original WC powder. This improvement is because microscopic defects on the surface of the WC powder can greatly improve surface free energy of the powder, which improves the sintering activity and reduces the sintering temperature of the WC powder.

Preparation and Characterization of Alumina based TiNn and SiCn Composites

2002 ◽  
Vol 740 ◽  
Author(s):  
Mats Carlsson ◽  
Mats Johnsson ◽  
Annika Pohl
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Grain Growth ◽  
Ceramic Composites ◽  
Processing Route ◽  
Nano Structure ◽  
Plasma Sintering ◽  
Water Based ◽  
Spark Plasma

ABSTRACTCeramic composites containing 2 and 5vol. % of nanosized commercially available TiN and SiC particles in alumina were prepared via a water based slurry processing route followed by spark plasma sintering (SPS) at 75 MPa in the temperature range 1200–1600°C. Some of the samples could be fully densified by use of SPS already after five minutes at 1200°C and 75 MPa. The aim was to control the alumina grain growth and thus obtain different nano-structure types. The microstructures have been correlated to some mechanical properties; e.g. hardness and fracture toughness.

Microstructure and Mechanical Properties of Spark-Plasma-Sintered SiC-TiC Composites

2005 ◽  
Vol 287 ◽  
pp. 335-339 ◽  
Author(s):  
Kyeong Sik Cho ◽  
Kwang Soon Lee
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Heating Rate ◽  
Spark Plasma Sintering ◽  
Sintering Temperature ◽  
Applied Pressure ◽  
Argon Atmosphere ◽  
Full Density ◽  
Plasma Sintering ◽  
Spark Plasma

Rapid densification of the SiC-10, 20, 30, 40wt% TiC powder with Al, B and C additives was carried out by spark plasma sintering (SPS). In the present SPS process, the heating rate and applied pressure were kept at 100°C/min and at 40 MPa, while the sintering temperature varied from 1600-1800°C in an argon atmosphere. The full density of SiC-TiC composites was achieved at a temperature above 1800°C by spark plasma sintering. The 3C phase of SiC in the composites was transformed to 6H and 4H by increasing the process temperature and the TiC content. By tailoring the microstructure of the spark-plasma-sintered SiC-TiC composites, their toughness could be maintained without a notable reduction in strength. The strength of 720 MPa and the fracture toughness of 6.3 MPa·m1/2 were obtained in the SiC-40wt% TiC composite prepared at 1800°C for 20 min.

scholarly journals Effect of Doped CeO with Si3N4 Powders on the Densification Mechanism During

2021 ◽  
Author(s):  
Yao Liu
Keyword(s):  
Liquid Phase ◽  
Relative Density ◽  
Stress Exponent ◽  
Spark Plasma Sintering ◽  
Liquid Phase Sintering ◽  
Creep Model ◽  
Stress Regime ◽  
Densification Mechanism ◽  
Plasma Sintering ◽  
Spark Plasma

Abstract The densification mechanism of doped CeO with Si3N4 powder during Spark Plasma Sintering (SPS) was investigated under temperatures ranging from 1500 to 1750 °C at soaking pressures of 30, 40, 50 MPa. Results showed that the relative density of Si3N4 ceramics sintered at 1650 °C and 30 MPa was 97.9%. A creep model was employed to determine the mechanism, which can be interpreted on the basis of the stress exponent (n). The results showed that the mechanism was controlled by liquid phase sintering at low effective stress regime (n=1).