scholarly journals Residual stresses determination by neutron diffraction in a 100Cr6 chromium steel bearing ring

2021 ◽  
Vol 51 (05) ◽  
pp. 275-281
Author(s):  
M. ROGANTE ◽  
G. MARTINAT ◽  
P. MIKULA ◽  
M. VRÁNA
2010 ◽  
Vol 652 ◽  
pp. 111-115 ◽  
Author(s):  
D.G. Hattingh ◽  
Axel Steuwer ◽  
M. Neil James ◽  
I.N. Wedderburn

This paper presents microstructural, hardness and residual strain information for solid-state welds in creep-resistant Cr-Mo steel, made using the new local damage repair technique offered by friction taper stud welding (FTSW). The technique is suitable for making single welds to repair, for example, localised creep damage but can also be extended to deal with planar defects through the use of overlapping welds. Neutron diffraction was used to measure residual strains at a number of positions along a series of 5 overlapping FTS welds.


2014 ◽  
Vol 777 ◽  
pp. 213-218 ◽  
Author(s):  
Chandrahas Rathod ◽  
David Wexler ◽  
Vladimir Luzin ◽  
Paul Boyd ◽  
Manicka Dhanasekar

Insulated rail joints (IRJs) are a primary component of the rail track safety and signalling systems. Rails are supported by two fishplates which are fastened by bolts and nuts and, with the support of sleepers and track ballast, form an integrated assembly. IRJ failure can result from progressive defects, the propagation of which is influenced by residual stresses in the rail. Residual stresses change significantly during service due to the complex deformation and damage effects associated with wheel rolling, sliding and impact. IRJ failures can occur when metal flows over the insulated rail gap (typically 6-8 mm width), breaks the electrically isolated section of track and results in malfunction of the track signalling system. In this investigation, residual stress measurements were obtained from rail-ends which had undergone controlled amounts of surface plastic deformation using a full scale wheel-on-track simulation test rig. Results were compared with those obtained from similar investigations performed on rail ends associated with ex-service IRJs. Residual stresses were measured by neutron diffraction at the Australian Nuclear Science and Technology Organisation (ANSTO). Measurements with constant gauge volume 3x3x3 mm3 were carried in the central vertical plane on 5mm thick sliced rail samples cut by an electric discharge machine (EDM). Stress evolution at the rail ends was found to exhibit characteristics similar to those of the ex-service rails, with a compressive zone of 5mm deep that is counterbalanced by a tension zone beneath, extending to a depth of around 15mm. However, in contrast to the ex-service rails, the type of stress distribution in the test-rig deformed samples was apparently different due to the localization of load under the particular test conditions. In the latter, in contrast with clear stress evolution, there was no obvious evolution of d0. Since d0 reflects rather long-term accumulation of crystal lattice damage and microstructural changes due to service load, the loading history of the test rig samples has not reached the same level as the ex-service rails. It is concluded that the wheel-on-rail simulation rig provides the potential capability for testing the wheel-rail rolling contact conditions in rails, rail ends and insulated rail joints.


2008 ◽  
Vol 59 ◽  
pp. 299-303
Author(s):  
K. Mergia ◽  
Marco Grattarola ◽  
S. Messoloras ◽  
Carlo Gualco ◽  
Michael Hofmann

In plasma facing components (PFC) for nuclear fusion reactors tungsten or carbon based tiles need to be cooled through a heat sink. The joint between the PFC and the heat sink can be realized using a brazing process through the employment of compliant layer of either a low yield material, like copper, or a high yield material, like molybdenum. Experimental verification of the induced stresses during the brazing process is of vital importance. Strains and residual stresses have been measured in Mo/CuCrZr brazed tiles using neutron diffraction. The strains and stresses were measured in Mo tile along the weld direction and at different distances from it. The experimental results are compared with Finite Element Simulations.


2000 ◽  
Vol 276-278 ◽  
pp. 923-924 ◽  
Author(s):  
F Fiori ◽  
E Girardin ◽  
A Giuliani ◽  
T Lorentzen ◽  
A Pyzalla ◽  
...  

2008 ◽  
Vol 571-572 ◽  
pp. 21-26 ◽  
Author(s):  
Adele Carradò ◽  
D. Duriez ◽  
Laurent Barrallier ◽  
Sebastian Brück ◽  
Agnès Fabre ◽  
...  

Seamless tubes are used for many applications, e.g. in heating, transport gases and fluids, evaporators as well as medical use and as intermediate products for hydroforming and various mechanical applications, where the final dimensions normally are given by some cold drawing steps. The first process step – piercing of the billet, for example by extrusion or 3-roll-milling - typically results in ovality and eccentricity in the tube causing non-symmetric material flow during the cold drawing process, i.e. inhomogeneous deformation. Because of this non-axisymmetric deformation and of deviations over tube length caused by moving tools, this process step generates residual stresses. To understand the interconnections between the geometrical changes in the tubes and the residual stresses, the residual strains in a copper tube had been measured by neutron diffraction.


2013 ◽  
Vol 772 ◽  
pp. 193-199 ◽  
Author(s):  
Carsten Ohms ◽  
Rene V. Martins

Bi-metallic piping welds are frequently used in light water nuclear reactors to connect ferritic steel pressure vessel nozzles to austenitic stainless steel primary cooling piping systems. An important aspect for the integrity of such welds is the presence of residual stresses. Measurement of these residual stresses presents a considerable challenge because of the component size and because of the material heterogeneity in the weld regions. The specimen investigated here was a thin slice cut from a full-scale bi-metallic piping weld mock-up. A similar mock-up had previously been investigated by neutron diffraction within a European research project called ADIMEW. However, at that time, due to the wall thickness of the pipe, stress and spatial resolution of the measurements were severely restricted. One aim of the present investigations by high energy synchrotron radiation and neutrons used on this thin slice was to determine whether such measurements would render a valid representation of the axial strains and stresses in the uncut large-scale structure. The advantage of the small specimen was, apart from the easier manipulation, the fact that measurement times facilitated a high density of measurements across large parts of the test piece in a reasonable time. Furthermore, the recording of complete diffraction patterns within the accessible diffraction angle range by synchrotron X-ray diffraction permitted mapping the texture variations. The strain and stress results obtained are presented and compared for the neutron and synchrotron X-ray diffraction measurements. A strong variation of the texture pole orientations is observed in the weld regions which could be attributed to individual weld torch passes. The effect of specimen rocking on the scatter of the diffraction data in the butt weld region is assessed during the neutron diffraction measurements.


2001 ◽  
Vol 61 (3-6) ◽  
pp. 575-577 ◽  
Author(s):  
A. Carradò ◽  
F. Fiori ◽  
E. Girardin ◽  
T. Pirling ◽  
P. Powell ◽  
...  

2008 ◽  
Vol 571-572 ◽  
pp. 327-332 ◽  
Author(s):  
Jesus Ruiz-Hervias ◽  
Giovanni Bruno ◽  
Jonas Gurauskis ◽  
A.J. Sanchez-Herencia ◽  
C. Baudin

Residual stress profiles were measured by neutron diffraction in Al2O3/Y-TZP ceramic composites containing 5 and 40 vol.% Y-TZP fabricated by conventional slip casting and by a novel tape casting route. Residual stresses in the zirconia are tensile and increase as its volume fraction decreases. For the alumina matrix, residual stress is compressive and increases with the zirconia volume fraction. In the composite with 5 vol.% zirconia, the processing route does not have an influence on residual stresses. However, in the composite with 40 vol.% zirconia, residual stresses are different in the samples obtained by both processing routes.