Influence of short-fiber composite base on fracture behavior of direct and indirect restorations

Objectives The aim was to examine the influence of short-fiber composite (SFC) core on the fracture-behavior of different types of indirect posterior restorations. In addition, the effect of thickness ratio of SFC-core to the thickness of the veneering conventional composite (PFC) on fracture-behavior of bi-structured composite restorations was evaluated. Materials and methods MOD cavities with removed palatal cusps were prepared on 90 intact molars. Five groups of direct overlay restorations (n = 10/group) were fabricated having a SFC-core (everX Flow) with various thicknesses (0, 1, 2, 3, 4 mm) and layer of surface PFC (G-aenial Anterior), remaining the thickness of the bi-structure restoration to be 5 mm. Four groups of CAD/CAM-made restorations (Cerasmart 270 and e-max CAD) were fabricated either with 2-mm layer of SFC-core or without fiber reinforcement. Intact teeth (n = 10) were used as control group. Restorations were statically loaded until fracture. Fracture patterns were evaluated visually. Data were analyzed using ANOVA (p = 0.05). Results With indirect overlay restorations, no statistically significant differences (p > 0.05) were observed in the load-bearing capacities between restorations reinforced by 2-mm SFC-core (bi-structured) and those fabricated from plain restorative materials. ANOVA displayed that direct overlay restorations made from 4-mm layer thickness of SFC-core had significantly higher load-bearing capacities (3050 ± 574 N) (p < 0.05) among all the groups tested. Conclusions Restorations (direct/indirect) combining SFC-core and a surface layer of conventional material demonstrated encouraging achievement in reference to fracture behavior. Clinical relevance The use of flowable short-fiber composite as reinforcing base with large direct and indirect restorations may result in more repairable failure.

Study on the flexure performance of fine concrete sheets reinforced with textile and short fiber composites

In order to study the influences of the contents of short fiber on the mechanical properties of concrete matrix, the properties of compressive, flexure and splitting of concrete matrix reinforced by alkali resistant glass fiber and calcium carbonate whisker were tested. To study the reinforced effect of different scale fibers on the flexure behavior of fine concrete sheets, the flexural tests of concrete sheet of fine concrete reinforced with basalt fiber mesh and short fiber composites were carried out. The results show that the properties of the compressive, flexure and splitting of fine concrete reinforced with appropriate amount of alkali resistant glass fiber and carbonate whisker are improved compared with that of concrete reinforced by one type of fiber. The flexure properties of the concrete sheets are improved obviously when continuous fiber textile and short fiber composite are adopted to reinforce.

Clinical Evaluation of Fiber-Reinforced Composite Restorations in Posterior Teeth - Results of 2.5 Year Follow-up

Objectives: The aim of this study was to evaluate the clinical performance of posterior composite restorations reinforced by bulk base of short-fiber composite (everX Posterior, GC Corporation). Methods: Thirty-six short fiber-reinforced composite restorations were placed in premolar and molar teeth of 33 patients. Eight of the teeth were vital and 28 were non-vital. Average follow up time of the restorations was 30.6 months (2.5 years), ranging from 16.2 to 51.3 months (1.3 - 4.3 years). Results: One restoration failed during the follow-up period due to secondary caries, at time point 39.5 months. Three fillings had minor fractures during the follow-up. The overall survival rate of the restorations was 97.2% and success rate (no maintenance needed) was 88.9%, respectively. Conclusion: Posterior composite restorations with a bulk base of short-fiber composite showed good clinical performance in the short term evaluation.