Robust ferromagnetic insulating and large exchange bias in LaMnO3:CoO composite thin films

Ferromagnetic insulators have received widespread attention for applications in novel low power consumption spintronic devices. Further optimizing the robust ferromagnetic insulating and developing multifunctional ferromagnetic insulator by integrating other magnetic property can not only ease or pave the way for actual application, but also provide an additional freedom degree for device designing. In this work, by introducing antiferromagnetic CoO into ferromagnetic insulator LaMnO3, we have constructed (1-x)LaMnO3:xCoO composite thin films. The films simultaneously show robust ferromagnetic insulator characteristics and large exchange bias. For x = 0.5 sample, the resistivity is 120 Ω·cm at 250 K while the magnetization is 100 emu/cm3 and the exchange bias field is -2200 Oe at 10 K. Especially, the blocking temperature is up to 140 K. Synchrotron radiation x-ray absorption spectroscopy reveals the coexistence of Mn3+, Mn2+, Co2+ and Co3+, arising from interfacial charge transfer and space charge/defect trapping, should be responsible for the enhanced and integrated multifunctional magnetic properties.

Composite thin films based on multilayer carbon nanotubes and calcium phosphate with electrical conductive properties for bone tissue engineering

This work is aimed at developing of electrically conductive composite thin films based on calcium phosphates (CP) and multi-walled carbon nanotubes (MWCNT) for bone tissue engineering. A method based on the sputtering of an dispersion of CPs and MWCNTs on a substrate with subsequent exposure to a laser with different power values to form connected networks of nanotubes has been proposed. It is shown that the electrical conductivity of CP/MWCNT films reaches high values for dispersions with a MWCNT concentration of 1 mg/ml when exposed to laser radiation with a power of 2.1–3.0 W. It was found that ablation areas of CPs and MWCNTs as a result of exposure to a high-power laser are found in areas of the film with increased resistance.