Detectable Depth of Copper, Steel, and Aluminum Alloy Plates with Pulse-Echo Laser Ultrasonic Propagation Imaging System

Pulse-echo laser ultrasonic propagation imaging is a nondestructive testing technique developed for composite materials and aluminum alloys used in aerospace. Although this method has been in usage for a considerable time, information of the detectable depth and the relationship between ultrasonic frequencies and the acoustic properties of metals is not readily available. Therefore, we investigate the A-scan and C-scan ultrasonic testing data of aluminum alloy, hot rolled steel, stainless steel, and copper alloy, which are used in aircraft bodies, frameworks, and gas pipelines. Experiments are performed with the pulse-width and excitation laser power fixed at 32 ns and approximately 4 W, respectively. The metal specimens include 24 artificial cylindrical defects with a diameter of 5 mm, located at depths of 1–12 mm on the front surface. The A-scan and C-scan data obtained at room temperature indicate the detectable depth for metals via the pulse-echo laser ultrasonic propagation imaging technique.

Effect of the Grain Sizes on the Ultrasonic Propagation and Attenuation on Different Types of Steels Microstructure During Non-Destructive Testing

In this paper we have proposed an experimental study of the steel grains sizes effect on the shift frequency of the ultrasonic waves being propagated in steels. Ultrasonic testing has been used in most inspection services for different materials as non-destructive testing. The novelty of our research work has been focused on the investigation of the new method for determining microstructure evolution of metals by using ultrasonic signals in conjunction with changes in grain size and hardness of steels. Furthermore, we have studied the microstructure of steel types S355, S275, Corten B and S275N. The microstructure results of steels have shown the changes that have been undergone from thermal and mechanical processes by using the attenuation of ultrasound waves during non-destructive testing.

Ultrasonic Propagation in Liquid and Ice Water Drops. Effect of Porosity

This work studies ultrasonic propagation in liquid and ice water drops. The effect of porosity on attenuation of ultrasonic waves in the drops is also explored. The motivation of this research was the possible application of ultrasonic techniques to the study of interstellar and cometary ice analogs. These ice analogs, made by vapor deposition onto a cold substrate at 10 K, can display high porosity values up to 40%. We found that the ultrasonic pulse was fully attenuated in such ice, and decided to grow ice samples by freezing a liquid drop. Several experiments were performed using liquid or frozen water drops with and without pores. An ultrasonic pulse was transmitted through each drop and measured. This method served to estimate the ultrasonic velocity of each drop by measuring drop size and time-of-flight of ultrasonic transmission. Propagation of ultrasonic waves in these drops was also simulated numerically using the SimNDT program developed by the authors. After that, the ultrasonic velocity was related with the porosity using a micromechanical model. It was found that a low value of porosity in the ice is sufficient to attenuate the ultrasonic propagation. This explains the observed lack of transmission in porous astrophysical ice analogs.

Characterization and Analysis of the Carbonation Process of a Lime Mortar Obtained from Phosphogypsum Waste

This work addresses the reuse of waste products as a raw material for lime putties, which are one of the components of mortar. 1:3 Lime/sand mortars very similar to conventional construction mortars were prepared using a lime putty obtained from the treatment of phosphogypsum with sodium hydroxide. The physical, rheological and mechanical properties of this phosphogypsum-derived mortar have been studied, as well as the mineralogical composition, microstructure by scanning electron microscope (SEM) and curing process by monitoring carbonation and ultrasonic propagation velocity. Considering the negative influence of sulphates on the hardened material, the behaviour of the material after sulphates precipitation by adding barium sulphate was additionally tested. Carbonation progressed from the outside to the inside of the specimen through the porous system by Liesegang rings patterns for mortars with soluble sulphates, while the carbonation with precipitated sulphates was controlled by diffusion-precipitation. Overall, the negative influence of low-sulphate contents on the mechanical properties of mortars was verified. It must be highlighted the importance of their precipitation to obtain adequate performance.