Phase Transformations from Nanocrystalline to Amorphous (Zr70Ni25Al5)100-xWx (x; 0, 2, 10, 20, 35 at. %) and Subsequent Consolidation

Glasses, which date back to about 2500 BC, originated in Mesopotamia and were later brought to Egypt in approximately 1450 BC. In contrast to the long-range order materials (crystalline materials), the atoms and molecules of glasses, which are noncrystalline materials (short-range order) are not organized in a definite lattice pattern. Metallic glassy materials with amorphous structure, which are rather new members of the advanced materials family, were discovered in 1960. Due to their amorphous structure, metallic glassy alloys, particularly in the supercooled liquid region, behave differently when compared with crystalline alloys. They reveal unique and unusual mechanical, physical, and chemical characteristics that make them desirable materials for many advanced applications. Although metallic glasses can be produced using different techniques, many of these methods cannot be utilized to produce amorphous alloys when the system has high-melting temperature alloys (above 1500 °C) and/or is immiscible. As a result, such constraints may limit the ability to fabricate high-thermal stable metallic glassy families. The purpose of this research is to fabricate metallic glassy (Zr70Ni25Al5)100-xWx (x; 0, 2, 10, 20, and 35 at. %) by cold rolling the constituent powders and then mechanically alloying them in a high-energy ball mill. The as-prepared metallic glassy powders demonstrated high-thermal stability and glass forming ability, as evidenced by a broad supercooled liquid region and a high crystallization temperature. The glassy powders were then consolidated into full-dense bulk metallic glasses using a spark plasma sintering technique. This consolidation method did not result in the crystallization of the materials, as the consolidated buttons retained their short-range order fashion. Additionally, the current work demonstrated the capability of fabricating very large bulk metallic glassy buttons with diameters ranging from 20 to 50 mm. The results indicated that the microhardness of the synthesized metallic glassy alloys increased as the W concentration increased. As far as the authors are aware, this is the first time this metallic glassy system has been reported.

Improve the Forming Ability of Al-Based Metallic Glass Under Ultrasonic Vibration at Room Temperature

In this work, a rapid and controllable ultrasonic vibration method for forming Al-based metallic glass at room temperature is proposed. This method can dramatically improve the forming ability of Al-based metallic glasses, which are virtually brittle at room temperature and have almost no supercooled liquid region at high temperatures. Under ultrasonic vibration, Al-based metallic glasses exhibited obvious plastic flow, with a maximum deformation degree up to 58% and an average deformation degree up to 43%. It is worth mentioning that no crystalline peaks were found on the X-ray diffraction patterns after deformation under ultrasonic vibration, and the mechanical properties remained the same as the primary sample. The present results provide a new approach for the deformation and forming of Al-based metallic glasses, which can significantly broaden their applications.

Effects of Annealing on Enthalpy Recovery and Nanomechanical Behaviors of a La-Based Bulk Metallic Glass

Structural relaxation and nanomechanical behaviors of La65Al14Ni5Co5Cu9.2Ag1.8 bulk metallic glass (BMG) with a low glass transition temperature during annealing have been investigated by calorimetry and nanoindentation measurement. The enthalpy release of this metallic glass is deduced by annealing near glass transition. When annealed below glass transition temperature for 5 min, the recovered enthalpy increases with annealing temperature and reaches the maximum value at 403 K. After annealed in supercooled liquid region, the recovered enthalpy obviously decreases. For a given annealing at 393 K, the relaxation behaviors of La-based BMG can be well described by the Kohlrausch-Williams-Watts (KWW) function. The hardness, Young’s modulus, and serrated flow are sensitive to structural relaxation of this metallic glass, which can be well explained by the theory of solid-like region and liquid-like region. The decrease of ductility and the enhancement of homogeneity can be ascribed to the transformation from liquid-like region into solid-like region and the reduction of the shear transition zone (STZ).

Investigation of the Structural Heterogeneity and Corrosion Performance of the Annealed Fe-Based Metallic Glasses

This study investigated the structural heterogeneity, mechanical property, electrochemical behavior, and passive film characteristics of Fe–Cr–Mo–W–C–B–Y metallic glasses (MGs), which were modified through annealing at different temperatures. Results showed that annealing MGs below the glass transition temperature enhanced corrosion resistance in HCl solution owing to a highly protective passive film formed, originating from the decreased free volume and the shrinkage of the first coordination shell, which was found by pair distribution function analysis. In contrast, the enlarged first coordination shell and nanoscale crystal-like clusters were identified for MGs annealed in the supercooled liquid region, which led to a destabilized passive film and thereby deteriorated corrosion resistance. This finding reveals the crucial role of structural heterogeneity in tuning the corrosion performance of MGs.