Mixed-Phase Ion-Exchangers from Waste Amber Container Glass

This study investigated the one-pot hydrothermal synthesis of mixed-phase ion-exchangers from waste amber container glass and three different aluminium sources (Si/Al = 2) in 4.5 M NaOH(aq) at 100 °C. Reaction products were characterised by X-ray diffraction analysis, Fourier transform infrared spectroscopy, 27Al and 29Si magic angle spinning nuclear magnetic resonance spectroscopy and scanning electron microscopy at 24, 48 and 150 h. Nitrated forms of cancrinite and sodalite were the predominant products obtained with reagent grade aluminium nitrate (Al(NO3)3∙9H2O). Waste aluminium foil gave rise to sodalite, tobermorite and zeolite Na-P1 as major phases; and the principal products arising from amorphous aluminium hydroxide waste were sodalite, tobermorite and zeolite A. Minor proportions of the hydrogarnet, katoite, and calcite were also present in each sample. In each case, crystallisation was incomplete and products of 52, 65 and 49% crystallinity were obtained at 150 h for the samples prepared with aluminium nitrate (AN-150), aluminium foil (AF-150) and amorphous aluminium hydroxide waste (AH-150), respectively. Batch Pb2+-uptake (~100 mg g−1) was similar for all 150-h samples irrespective of the nature of the aluminium reagent and composition of the product. Batch Cd2+-uptakes of AF-150 (54 mg g−1) and AH-150 (48 mg g−1) were greater than that of AN-150 (36 mg g−1) indicating that the sodalite- and tobermorite-rich products exhibited a superior affinity for Cd2+ ions. The observed Pb2+- and Cd2+-uptake capacities of the mixed-product ion-exchangers compared favourably with those of other inorganic waste-derived sorbents reported in the literature.

Production of Soda Lime Glass Having Antibacterial Property for Industrial Applications

This study was aimed to produce and characterize the first commercial glass materials with enhanced antibacterial property using conventional melting method. For this purpose, typical container glass composition that contains some specific metal ions, such as silver, strontium, and copper, was used to obtain antibacterial glass samples using classical melting method. After the melting process, antibacterial tests and migration tests were applied to the glasses, and it was found that the glass doped with 2% Ag2O was the best composition. X-rays diffractometer (XRD), thermal expansion coefficient, density, refractive index, hardness, and elastic module results showed that the glass doped with 2% Ag2O was a suitable material as a container glass. High Temperature Melting Observation System studies were performed on the produced antibacterial glass composition, and it was found that the antibacterial glass can be produced in soda lime glass furnaces without changing any furnace design and production parameters. As a result of the characterization studies, it was concluded that the produced container glass doped with silver can be a good candidate for food and pharmaceutical products where bacterial growth is absolutely undesirable.