Mechanism of Grain Refinement during Equal-Channel Angular Pressing at Intermediate Temperature in an Al-Mg-Sc Alloy

Author(s):  
Sergey Malopheyev ◽  
Vladislav Kulitskiy ◽  
Marat Gazizov ◽  
Rustam Kaibyshev
2010 ◽  
Vol 667-669 ◽  
pp. 379-384 ◽  
Author(s):  
X.H. An ◽  
Shi Ding Wu ◽  
Z.F. Zhang

The microstructural evolution and grain refinement of Cu-Al alloys with different stacking fault energies (SFEs) processed by equal-channel angular pressing (ECAP) were investigated. The grain refinement mechanism was gradually transformed from dislocation subdivision to twin fragmentation with tailoring the SFE of Cu-Al alloys. Concurrent with the transition of grain refinement mechanism, the grain size can be refined into from ultrafine region (1 m~100 nm) to the nanoscale (<100 nm) and then it is found that the minimum equilibrium grain size decreases in a roughly linear way with lowering the SFE. Moreover, in combination with the previous results, it is proposed that the formation of a uniform ultrafine microstructure can be formed more readily in the materials with high SFE due to their high recovery rate of dislocations and in the materials with low SFE due to the easy formation of a homogeneously-twinned microstructure.


Crystals ◽  
2020 ◽  
Vol 10 (12) ◽  
pp. 1157
Author(s):  
Lisa-Marie Rymer ◽  
Thomas Lindner ◽  
Philipp Frint ◽  
Martin Löbel ◽  
Thomas Lampke

Single-phase, face-centered cubic (FCC) high-entropy alloys (HEA) are promising materials for future applications. In order to improve the mechanical properties, especially the tensile strength of these materials, this study focuses on the combination of spark plasma sintering (SPS) and equal-channel angular pressing (ECAP). The initial fine-grained microstructure produced by SPS is further refined by ECAP in a 90°-die. Optical microscopy and electron backscatter diffraction (EBSD) confirm this considerable grain refinement, leads to a grain size below 1 µm after 1 ECAP pass. An alternating arrangement of fine-grained areas and much coarser regions, aligned under an angle of approximately 27°, is found. Moreover, a first microstructural investigation of the twin structure is conducted. The mechanical behavior was investigated by hardness measurements and tensile testing. Both the hardness and tensile strength are remarkably increased after ECAP. In contrast, the uniform elongation and elongation at fracture are significantly reduced due to the strengthening mechanisms of strain hardening and grain refinement. It is concluded that the combination of SPS and ECAP is an attractive approach for designing (ultra)fine-grained HEAs with superior properties. The investigated techniques could be applied to understand the underlying microstructural mechanisms.


2005 ◽  
Vol 475-479 ◽  
pp. 545-548 ◽  
Author(s):  
Hyo Tae Jeong ◽  
Woo Jin Kim

Microstructure and texture evolution in the AZ31 Mg alloy subject to equal channel angular pressing (ECAP) have been investigated and correlated with the mechanical properties. When AZ31 Mg alloy was ECAPed up to 8 passes following the route Bc, grain refinement occurred effectively. Texture was also changed during ECAP. The original fiber texture of the extruded AZ31 Mg alloy changed to a new texture component of ] 1 3 2 5 )[ 1 1 01 ( , and the texture of ] 1 3 2 5 )[ 1 1 01 ( orientation was rotated to ] 0 2 5 7 )[ 6 4 13 ( orientation after 6-pass ECAP process. The variation of the strength with the pass number was explained by the texture and grain size. The strength data of AZ31 Mg alloys followed the standard Hall-Petch relationship when the similar texture was retained during the ECAP process. Otherwise the effect of texture on strength was dominant over the strengthening due to grain refinement.