Differential Thermal Analysis for the Characterization of the Stability of Sludge

Author(s):  
P. Balmér ◽  
B. Kaffehr
2003 ◽  
Vol 28 (1) ◽  
pp. 33-38 ◽  
Author(s):  
A. T. Adorno ◽  
A. V. Benedetti ◽  
R. A. G. da Silva ◽  
M. Blanco

The influence of the Al content on the phase transformations in Cu-Al-Ag alloys was studied by classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The results indicated that the increase in the Al content and the presence of Ag decrease the rate of the <FONT FACE=Symbol>b</font>1 phase decomposition reaction and contribute for the raise of this transition temperature, thus decreasing the stability range of the perlitic phase resulted from the b1 decomposition reaction.


2006 ◽  
pp. 89-95 ◽  
Author(s):  
Catalina Mocioiu ◽  
Georgeta Jitianu ◽  
Maria Zaharescu

Lead-containing glasses have been used from the ancient time. Recently, due to the possible application in optics, electronics, nuclear techniques, wastes inactivation. the interest in these types of glasses has been renewed. For lead waste inactivation, glasses with high amount of PbO in the composition are required, those exhibiting at the same time a high chemical and thermal stability. Thermal behavior of lead-silicate glasses was examined by differential thermal analysis (DTA). Infrared spectroscopy was used to investigate the structure of the glasses. The spectra were interpreted in terms of the structures of silicate group by comparison with the spectra of other silicate crystals. The DTA and infrared data were correlated with the chemical stability tests.


2014 ◽  
Vol 805 ◽  
pp. 486-491
Author(s):  
J.M.R. Figueirêdo ◽  
Juliana Melo Cartaxo ◽  
I.A. Silva ◽  
C.D. Silva ◽  
Gelmires Araújo Neves ◽  
...  

The State of Paraíba, Brazil, retains about 88.5% of all Brazilian bentonite, and much of this production comes from deposits in the District of Boa Vista, PB. Nevertheless, the deposits are almost depleted. Recently, new deposits were found, which will increases the reserves of the State, in the regions of Cubati and Pedra Lavrada, PB. The objective of this work is to characterize and develop purified clays, through sieving and hydrocycloning techniques, from those recently discovered bentonites for several applications. The characterization of the sample was done through granulometric analysis by laser diffraction, X-ray diffraction, chemical analysis by X-ray fluorescence, and thermogravimetric and differential thermal analysis. The results show that the samples are typical of bentonite clays, and that the purification solely by hydrocyclone presents the best results.


2011 ◽  
Vol 217-218 ◽  
pp. 163-168 ◽  
Author(s):  
Lin Xin Tong ◽  
Jin Hong Li ◽  
Jian Cao

A series of gels with 3Al2O3•2SiO2 were prepared by Sol-gel method and heated at several temperatures for 2 h to synthesize Ti, Fe-doped mullite. The powers were characterized by differential thermal analysis (DSC-TG) and X-ray powder diffraction (XRD). Phase separation was promoted by doping both TiO2 and Fe2O3; with increasing the amount of dopant ions the formation temperature of Si-Al spinel decreased and the formation temperature of mullite increased by TiO2 doping but decreased by Fe2O3 doping. The formation temperature of pure mullite was about 1250-1350 °C.


1996 ◽  
Vol 11 (11) ◽  
pp. 2869-2875 ◽  
Author(s):  
K. Byrappa ◽  
Amita Jain

The growth of NaLa(WO4)2 crystals has been carried out by the hydrothermal method at fairly low P-T conditions. The crystal morphology has been studied with respect to the growth parameters. The crystals obtained were characterized by various techniques such as x-ray diffraction (XRD), differential thermal analysis (DTA), and infrared (IR) spectroscopy.


Science ◽  
2017 ◽  
Vol 355 (6323) ◽  
pp. 374-376 ◽  
Author(s):  
Chong Zhang ◽  
Chengguo Sun ◽  
Bingcheng Hu ◽  
Chuanming Yu ◽  
Ming Lu

Pentazole (HN5), an unstable molecular ring comprising five nitrogen atoms, has been of great interest to researchers for the better part of a century. We report the synthesis and characterization of the pentazolate anion stabilized in a (N5)6(H3O)3(NH4)4Cl salt. The anion was generated by direct cleavage of the C–N bond in a multisubstituted arylpentazole using m-chloroperbenzoic acid and ferrous bisglycinate. The structure was confirmed by single-crystal x-ray diffraction analysis, which highlighted stabilization of the cyclo-N5ˉ ring by chloride, ammonium, and hydronium. Thermal analysis indicated the stability of the salt below 117°C on the basis of thermogravimetry-measured onset decomposition temperature.


2013 ◽  
Vol 770 ◽  
pp. 22-25 ◽  
Author(s):  
Thitipong Kruaehong

The new Y257 superconductor in YBaCuO family was synthesized by standard solid state reaction. The Y257 samples were measured the critical temperature (Tc) by the four-probes method that found at 90 K. The XRD technique and FULLPROF program were used to determine the lattice parameters, space group and phase compositions. It was found that the Y257 exhibited in both of superconducting and non-superconducting phase. The Pmmm space group was fit well on superconducting phase with the lattice parameters as a=3.8108 Å, b=3.8544 Å and c=26.4967 Å. The non-superconducting phase exhibited in two space groups of Pccm (a=12.9770 Å, b=20.54780 Å and c=11.3530 Å) and Im-3m (a= 18.2104 Å, b=18.2104 Å and c=18.2104 Å). The peritectic temperature at 976.73°C was measured by differential thermal analysis.