Solid solution strengthening in Ti-Al alloys

1973 ◽  
Vol 4 (5) ◽  
pp. 1333-1338 ◽  
Author(s):  
H. W. Rosenberg ◽  
W. D. Nix
Alloy Digest ◽  
2004 ◽  
Vol 53 (6) ◽  

Abstract Olin Alloy C5218 is a phosphor bronze alloy given both dispersion- and solid-solution strengthening for applications in the automotive connector market. This datasheet provides information on composition, physical properties, elasticity, tensile properties, and bend strength. Filing Code: CU-715. Producer or source: Olin Brass.


2021 ◽  
pp. 110877
Author(s):  
Ankit Roy ◽  
Praveen Sreeramagiri ◽  
Tomas Babuska ◽  
Brandon Krick ◽  
Pratik K. Ray ◽  
...  

Hydrogen ◽  
2021 ◽  
Vol 2 (3) ◽  
pp. 262-272
Author(s):  
Sebastian DiMauro ◽  
Gabrielle Legall ◽  
Coleman Lubinsky ◽  
Monica Nadeau ◽  
Renee Tait ◽  
...  

Strength, hardness, and ductility characteristics were determined for a series of palladium-copper alloys that compositionally vary from 5 to 25 weight percent copper. Alloy specimens subjected to vacuum annealing showed clear evidence of solid solution strengthening. These specimens showed, as a function of increasing copper content, increased yield strength, ultimate strength, and Vickers microhardness, while their ductility was little affected by compositional differences. Annealed alloy specimens subsequently subjected to exposure to hydrogen at 323 K and PH2 = 1 atm showed evidence of hydrogen embrittlement up to a composition of ~15 wt. % Cu. The magnitude of the hydrogen embrittlement decreased with increasing copper content in the alloy.


Materials ◽  
2021 ◽  
Vol 14 (7) ◽  
pp. 1677
Author(s):  
Hooi Peng Lim ◽  
Willey Yun Hsien Liew ◽  
Gan Jet Hong Melvin ◽  
Zhong-Tao Jiang

This paper reviews the phase structures and oxidation kinetics of complex Ti-Al alloys at oxidation temperatures in the range of 600–1000 °C. The mass gain and parabolic rate constants of the alloys under isothermal exposure at 100 h (or equivalent to cyclic exposure for 300 cycles) is compared. Of the alloying elements investigated, Si appeared to be the most effective in improving the oxidation resistance of Ti-Al alloys at high temperatures. The effect of alloying elements on the mechanical properties of Ti-Al alloys is also discussed. Significant improvement of the mechanical properties of Ti-Al alloys by element additions has been observed through the formation of new phases, grain refinement, and solid solution strengthening.


2016 ◽  
Vol 838-839 ◽  
pp. 344-349 ◽  
Author(s):  
Galina P. Grabovetskaya ◽  
Ekaterina N. Stepanova ◽  
Ilya V. Ratochka ◽  
I.P. Mishin ◽  
Olga V. Zabudchenko

Hydrogenation effect on the development of superplastic deformation in the submicrocrystalline Ti–6Al–4V alloy at temperatures (0.4–0.5)Тmelt is investigated. Hydrogenation of the submicrocrystalline Ti–6Al–4V alloy to 0.26 mass% during superplastic deformation is found to result in solid solution strengthening, plastic deformation localization, and as a consequence, decrease of the deformation to failure. Possible reasons for the decrease of the flow stress and increase of the deformation to failure in the submicrocrystalline Ti–6Al–4V–0.26H alloy during deformation under conditions of superplasticity and simultaneous hydrogen degassing from the alloy are discussed.


2015 ◽  
Vol 817 ◽  
pp. 307-311 ◽  
Author(s):  
Peng Chao Zhang ◽  
Jin Chuan Jie ◽  
Yuan Gao ◽  
Tong Min Wang ◽  
Ting Ju Li

The Cu-Cr and Cu-Cr-Ti alloy plates were prepared by vacuum melting and plastic deformation. The effect of slight Ti element on microstructure and mechanical properties of Cu-Cr alloy was discussed. The result shows that Cr particles with spherical shape precipitated from Cu matrix after aging. Plenty Ti atoms dissolved in the vicinity of Cr particles and there were still parts of solid solution Ti atoms in other regions. Improvements in peak hardness and softening resistance were achieved with the addition of Ti element in Cu-Cr alloy. The addition of 0.1 wt.% Ti element makes Cu-Cr alloy possess tensile strength of 565 MPa and hardness of 185.9 HV after aging at 450 °C for 120 min, which can be attributed to multiple strengthening mechanisms, i.e. work hardening, solid solution strengthening and precipitation strengthening.