Effect of niobium and austenitizing temperature on the microstructures and properties of spray-deposited AISI M3:2 high speed steel

The microstructure and properties of niobium-containing AISI M3:2 high speed steels (HSSs) fabricated by spray forming and traditional casting have been investigated. The results show that fine and uniformly-distributed grains without macrosegregation appeared in the as-deposited HSSs that differ from those of as-cast HSSs. Nb mostly appears in primary MC carbides, whereas it contributes less to the formation of M6C carbides. The high stabilization of Nb-rich MC carbides can pin the grain boundaries during high-temperature austenitizing process, thus conferring a fine grains and raising the content of dissolved alloying elements. Enhanced precipitation strengthening and fine dispersion of NbC carbides throughout the matrix contribute to the high hardness and red hardness of Nb-containing HSS.

Effect of Temperature on Microstructure and Mechanical Properties of Fe-9Ni-2Cu Steel during the Tempering Process

In this paper, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray stress meter (XRSA), atom probe tomography (APT), hardness, and tensile tests were used to study the effect of tempering temperature on the microstructure and properties of Fe-9Ni-2Cu steel. The results show that after the quenched samples were tempered at 460 °C for 2 h, the hardness values increased from 373 to 397 HV, and elongation also increased from 13% to 16%. With the tempering temperature increasing from 460 to 660 °C, the hardness firstly decreases from 397 to 353 HV and then increases to 377 HV, while the elongation increases to 17% and then decreases to 11%. The variation of the mechanical properties greatly depends on the evolution of the Cu-rich phase and carbides. The precipitation strengthening of the Cu-rich phase and carbides leads to the increase of hardness, but when the precipitate is coarsened, the precipitation strengthening weakens, and then, the hardness increases. When the tempering temperature is 560 °C, a large amount of stable reverse transformation austenite was formed with a content of 7.1%, while the tensile strength reached the lowest value of 1022 MPa and the elongation reached the maximum value of 17%.

Microstructure Characteristics and Strengthening Behavior of Cu-Bearing Non-Oriented Silicon Steel: Conventional Process versus Strip Casting

Based on conventional hot rolling processes and strip casting processes, Cu precipitation strengthening is used to improve the strength of non-oriented silicon steel in order to meet the requirements of high-speed driving motors of electric vehicles. Microstructure evolution was studied, and the effects of Cu precipitates on magnetic and mechanical properties are discussed. Compared with conventional processes, non-oriented silicon steel prepared by strip casting exhibited advantages with regard to microstructure optimization with coarse grain and {100} texture. Two-stage rolling processes were more beneficial for uniform microstructure, coarse grains and improved texture. The high magnetic induction B50 of 1.762 T and low core losses with P1.5/50, P1.0/400 and P1.0/1000 of 1.93, 11.63 and 44.87 W/kg, respectively, were obtained in 0.20 mm sheets in strip casting. Cu precipitates significantly improved yield strength over ~120 MPa without deteriorating magnetic properties both in conventional process and strip casting. In the peak stage aged at 550 °C for 120 min, Cu precipitates retained bcc structure and were coherent with the matrix, and the yield strength of the 0.20 mm sheet was as high as 501 MPa in strip casting. The main mechanism of precipitation strengthening was attributed to coherency strengthening and modulus strengthening. The results indicated that balanced magnetic and mechanical properties can be achieved in thin-gauge non-oriented silicon steel with Cu addition in strip casting.

Probability-Dependent Precipitation Strengthening Effect of Anisotropic Precipitate in Al-Mg-Si Alloy Produced by T6 Heat Treatment

This study proposed a constitutive equation to predict the change in yield strength according to the behavior of β″ metastable precipitates, which have a profound effect on strength among materials precipitated during the T6 heat treatment of Al-Mg-Si alloy. The β″ precipitate is a metastable phase before it becomes a β (Mg2Si) precipitate, and is distributed in the form of nano-scale rods in the aluminum alloy matrix. Existing precipitation strengthening models assume the shape of the precipitate to be spherical, and in that case the equation that depends on the Orowan mechanism with the average precipitate size and distribution should dominate. However, precipitates are formed in various shapes and sizes by anisotropic growth. In particular, rod-shaped precipitates are not suitable for the existing precipitation strengthening model. In this study, an Al-Mg-Si alloy was fabricated by gravity casting followed by T6 heat treatment. The new precipitation strengthening effect equation proposes that the β″ precipitate affects yield strength during plastic deformation of the Al-Mg-Si alloy. The proposed precipitation strengthening effect equation probabilistically considers the Critical Resolved Shear Stress (CRSS), which varies depending on the angle between the dislocation and the precipitate, when the dislocation passes through a rod-shaped precipitate.