The relationship between minimum creep rate and rupture time in Cr-Mo steels

1992 ◽  
Vol 1 (1) ◽  
pp. 123-128 ◽  
Author(s):  
V. M. Radhakrishnan
Keyword(s):  
Creep Rate ◽  
Minimum Creep Rate ◽  
Rupture Time ◽  
The Relationship

On Time-Temperature Parameters for Correlation of Creep-Rupture Data in Stainless Steel Weldments

1978 ◽  
Vol 100 (3) ◽  
pp. 319-332 ◽  
Author(s):  
W. E. White ◽  
Iain Le May
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Creep Rate ◽  
Creep Rupture ◽  
Rupture Time ◽  
Function Approach ◽  
Secondary Creep ◽  
Rupture Data ◽  
The Relationship ◽  
Secondary Creep Rate

The Manson-Haferd, Larson-Miller, and Orr-Sherby-Dorn time-temperature parameters were applied to creep-rupture data obtained from testing two batches of austenitic stainless steel weldments. It was found that none of these correlated the data satisfactorily. A new parameter, based on a modification of one proposed originally by Manson and by Goldhoff and Sherby, was found to adequately correlate the data. The Minimum-Commitment, Station-Function Approach of Manson and Ensign was also applied, the results of which supported those obtained from the analysis made using the parameters listed above. Finally, from the relationship between rupture-time and secondary creep-rate, it is suggested that the form of the rupture data may be useful in predicting the physical basis for creep.

scholarly journals On the physical basis for the creep of ice: the high temperature regime

2020 ◽  
Vol 66 (257) ◽  
pp. 401-414 ◽  
Author(s):  
D.M. Cole
Keyword(s):  
Activation Energy ◽  
High Temperature ◽  
Melting Point ◽  
Creep Rate ◽  
Minimum Creep Rate ◽  
Constitutive Behavior ◽  
Thermally Induced ◽  
Dislocation Glide ◽  
Dislocation Mechanics ◽  
The Relationship

AbstractThis work quantifies the increased temperature sensitivity of the constitutive behavior of ice with proximity to the melting point in terms of dislocation mechanics. An analysis of quasistatic and dynamic cyclic loading data for several ice types leads to the conclusion that high temperature (e.g. T ≥ −8°C) behavior is the result of a thermally induced increase in the number of mobile dislocations rather than an increase in the activation energy of dislocation glide or the introduction of a new deformation mechanism. The relationship between dislocation density and temperature is quantified and the model is shown to adequately represent the published minimum creep rate vs stress data for isotropic granular freshwater ice for −48 ≤ T ≤ −0.01°C.

scholarly journals Effect of Low-Temperature Annealing on Creep Properties of AlSi10Mg Alloy Produced by Additive Manufacturing: Experiments and Modeling

Metals ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 179
Author(s):  
Chiara Paoletti ◽  
Emanuela Cerri ◽  
Emanuele Ghio ◽  
Eleonora Santecchia ◽  
Marcello Cabibbo ◽  
...  
Keyword(s):  
Creep Rate ◽  
Applied Stress ◽  
Minimum Creep Rate ◽  
Annealing Treatment ◽  
Constant Load ◽  
Experimental Conditions ◽  
Creep Properties ◽  
Low Temperature Annealing ◽  
Physically Based ◽  
Excellent Description

The effects of postprocessing annealing at 225 °C for 2 h on the creep properties of AlSi10Mg alloy were investigated through constant load experiments carried out at 150 °C, 175 °C and 225 °C. In the range of the experimental conditions here considered, the annealing treatment resulted in an increase in minimum creep rate for a given stress. The reduction in creep strength was higher at the lowest temperature, while the effect progressively vanished as temperature increased and/or applied stress decreased. The minimum creep rate dependence on applied stress was modeled using a physically-based model which took into account the ripening of Si particles at high temperature and which had been previously applied to the as-deposited alloy. The model was successfully validated, since it gave an excellent description of the experimental data.

Evaluation of Creep Deformation Property of Grade 91 Steels

2015 ◽  
Author(s):  
Kazuhiro Kimura ◽  
Kota Sawada ◽  
Hideaki Kushima
Keyword(s):  
Creep Rate ◽  
Creep Deformation ◽  
Minimum Creep Rate ◽  
Deformation Property ◽  
Time Dependent ◽  
Tertiary Creep ◽  
Total Strain ◽  
Dominant Factor ◽  
Creep Equation ◽  
Time To Rupture

Creep deformation property of Grade T91 steels over a range of temperatures from 550 to 625°C was analyzed by means of the empirical creep equation reported in the previous study [1]. The creep equation consists of four time dependent terms and one constant and time to rupture is estimated as a time to total strain of 10%. Accuracy of the creep equation to represent creep curve and to predict time to rupture and minimum creep rate was indicated. Times to minimum creep rate, total strain of 1%, initiation of tertiary creep and rupture were evaluated by the creep equation. Stress dependence of strains at minimum creep rate and the initiation of tertiary creep were analyzed. Contribution of four time dependent terms to the strains at minimum creep rate, total strain of 1% and initiation of tertiary creep was investigated. Three parameters to determine a temperature and time-dependent stress intensity limit, St, were compared and a dominant factor of St was examined. Heat-to-heat variation of the creep deformation property was investigated on two heats of T91 steels contain low and high nickel concentrations.

Investigation on Creep Behavior of Grade 91 Heat-Resistant Steel at 923K

2016 ◽  
Vol 853 ◽  
pp. 163-167
Author(s):  
Fa Cai Ren ◽  
Xiao Ying Tang
Keyword(s):  
Creep Rate ◽  
Creep Behavior ◽  
Creep Deformation ◽  
Deformation Behavior ◽  
Minimum Creep Rate ◽  
Resistant Steel ◽  
Creep Tests ◽  
Heat Resistant Steel ◽  
Heat Resistant ◽  
Grade 91

Creep deformation behavior of SA387Gr91Cl2 heat-resistant steel used for steam cooler has been investigated. Creep tests were carried out using flat creep specimens machined from the normalized and tempered plate at 973K with stresses of 100, 125 and 150MPa. The minimum creep rate and rupture time dependence on applied stress was analyzed. The analysis showed that the heat-resistant steel obey Monkman-Grant and modified Monkman-Grant relationships.

Creep Deformation Behavior and Microstructural Degradation During Creep of Pre-Strained 25Cr-20Ni-Nb-N Steel

2007 ◽  
Author(s):  
Nobuhiko Saito ◽  
Nobuyoshi Komai
Keyword(s):  
Creep Rate ◽  
Creep Deformation ◽  
Deformation Behavior ◽  
Minimum Creep Rate ◽  
Strengthening Mechanism ◽  
Creep Rupture ◽  
Microstructural Degradation ◽  
Solution Treated ◽  
Long Time ◽  
Strained Materials

The purpose of this study is to clarify the creep deformation behavior and microstructural degradation during creep of pre-strained 25Cr-20Ni-Nb-N steel (TP310HCbN), which has the highest creep strength among austenite stainless steels used for boiler tubes. The creep rupture strengths of the 20% pre-strained materials tested at 650°C under 210 MPa and 180 MPa were higher than those of solution-treated materials. However, the long time creep rupture strengths of the 20% pre-strained materials tested at 700°C and 750°C were lower than those of solution-treated materials. Thus, the creep strengths of the prestrained materials depend on test temperature and stress. Furthermore, the minimum creep rate of the 20% pre-strained materials and re-solution-treated materials tested at 650°C under 300MPa were 1.2 × 10−9 and 1.6 × 10−8 s−1, respectively. Thus, the minimum creep rate of the 20% pre-strained materials was lower than for re-solution-treated materials. The creep strengthening mechanism of the pre-strained materials at 650°C was considered to be that high-density dislocations were maintained until the late stage of creep. On the other hand, the creep rupture strengths of the 20% pre-strained materials were lower than those of solution-treated materials tested at over 700°C because of agglomeration and coarsening of precipitates and the recovery of dislocations.

The Creep Deformation and Elevated Temperature Microstructural Stability of a Two-Phase TiAl/Ti3Al Lamellar Alloy.

1994 ◽  
Vol 364 ◽  
Author(s):  
M. F. Bartholomeusz ◽  
J. A. Wert
Keyword(s):  
Elevated Temperature ◽  
Creep Rate ◽  
Microstructural Evolution ◽  
Creep Deformation ◽  
Minimum Creep Rate ◽  
Single Phase ◽  
Lamellar Microstructure ◽  
Microstructural Stability ◽  
Two Phase ◽  
The Individual

AbstractEnhanced work hardening of the phases in the lamellar microstructure has been cited as an explanation for the lower minimum creep rates of a two-phase TiAl/Ti3Al lamellar alloy compared with the minimum creep rates of the individual TiAl and Ti3Al single-phase alloys tested between 980 K and 1130 K. This proposition is confirmed by TEM observations. Thermal and thermomechanical exposure result in the microstructural evolution, which increases the minimum creep rate (εmin) of the lamellar alloy. The effect of microstructural evolution on εmin will be discussed in the present paper.