In the current Research , the heat cured matrix material powder of PMMA was reinforced with peanut and walnut shells (natural powders) which are chemically treated with 5% (w/v) (NaOH) to improve the matrix bonding (PMMA) before being used as a reinforcing powder and adding to exactly similar averages particle sizes ≤ (53µm), with different weight fractions of (4, 8, and 12 wt.%). The ASTM D638 is used for composite specimens of the tensile test. The results indicated that the Elastic modulus values reached its maximum value at (8 wt.%.) when reinforced with peanut shells particles (1.053Gpa) , while ,the values of tensile strength, elongation percentage at break, decrease as the weight fraction of peanut and walnut shells powder increase and the lowest values is obtained by reinforcing with peanut shells particles to reach their minimum values at (12 wt.%.) where the lowest values of them are (29 MPa, 2.758% ) respectively. The fracture surface morphology of pure PMMA seemed to be homogenous morphology in (SEM) test, whereas the fracture surface morphology of PMMA composite reinforced by (peanut and walnut shells) powders and shows a roughness fracture surface morphology this refer to semi ductile to ductile materials.
Influence of heat treatment on mechanical properties, microstructure, and fracture surface morphology of V-5Cr-5Ti alloy